High-property water-based metal die-casting releasing agent, preparation method and application of high-property water-based metal die-casting releasing agent

A release agent and metal mold technology, applied in metal processing equipment, casting molding equipment, casting molds, etc., can solve problems such as difficult to ensure the residual amount of lubricating components, burrs, pores, etc., to facilitate automated production, solve porous problems, The effect of strong heat resistance at high temperature

Active Publication Date: 2018-04-06
上海力太化学有限公司
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the components of the existing release agent are easy to evaporate or become decomposed gas due to heat, and it is difficult to ensure the residual amount of lubricating components in the high-temperature mold, which often results in the formation of porous, burr and other structures on the surface of the die-casting metal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-property water-based metal die-casting releasing agent, preparation method and application of high-property water-based metal die-casting releasing agent
  • High-property water-based metal die-casting releasing agent, preparation method and application of high-property water-based metal die-casting releasing agent
  • High-property water-based metal die-casting releasing agent, preparation method and application of high-property water-based metal die-casting releasing agent

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The preparation method of metal die-casting release agent of the present invention comprises the steps:

[0038]Mixing of the oil phase system: adding the functional organic composition and the nonionic surfactant to the multifunctional reactor, and stirring to form an oil phase system;

[0039] W / O water-in-oil: Stir at 1000r / min, and drop water into the oil phase system to form a water-in-oil system. The amount of water added accounts for 1 / 10 of the mass of the oil phase system. The water-in-water system undergoes phase transformation to form an O / W oil-in-water system. After the phase transformation, stop adding water to the oil phase system and continue stirring for 5-10 minutes;

[0040] O / W oil-in-water: continue to inject water into the oil-in-water system for 3-5 minutes, the amount of water injected is 1 / 3-1 / 2 of the oil phase system, and the speed is increased to 1500r / min to make oil-in-water O / W W pre-emulsion, the speed is increased to 600r / min, and the p...

Embodiment 1

[0044] Example 1 is a specific example of preparing a mold release agent suitable for aluminum alloy die-casting. As shown in the following table 1, 1.5phr high carbonized phenolic resin contained in this embodiment, 20.6phr high temperature resistant silicone oil, 10.0phr refined rapeseed oil, 10.0phr high viscosity mineral oil, 3.0phr Span-80, 2.0phr 1310 , 1.0phr AEO-3, 1.0phr triethanolamine, 0.03phr isothiazolinone, 0.01phr benzisothiazolone and 50.86phr solvent.

[0045] Concrete preparation process is as follows:

[0046] Add high-carbonized phenolic resin, high-temperature-resistant silicone oil, high-viscosity mineral oil, refined rapeseed oil, Span-80, AEO-3 and 1310 into the multifunctional reaction kettle, and heat and stir to form an oil phase system at the same time. Then stir at a speed of 1000r / min, and add water dropwise to the oil phase system, and the dropwise addition is completed in 20 minutes to form an oil-in-water system. Continue to inject water into...

Embodiment 2

[0049] Example 2 is a specific example of preparing a release agent suitable for aluminum alloy die-casting. As shown in the following table 1, 1.0phr high carbonized phenolic resin contained in this embodiment, 24.0phr high temperature resistant silicone oil, 10.0phr refined rapeseed oil, 7.5phr high viscosity mineral oil, 2.6phr Span-80, 2.0phr 1310 , 1.0phr AEO-3, 1.0phr triethanolamine, 0.03phr isothiazolinone, 0.01phr benzisothiazolone and 50.86phr solvent.

[0050] Concrete preparation process is as follows:

[0051] Add high-carbonized phenolic resin, high-temperature-resistant silicone oil, high-viscosity mineral oil, refined rapeseed oil, Span-80, AEO-3 and 1310 into the multifunctional reaction kettle, and heat and stir to form an oil phase system at the same time. Then stir at a speed of 1000r / min, and add water dropwise to the oil phase system, and the dropwise addition is completed in 20 minutes to form an oil-in-water system. Continue to inject water into the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a high-property water-based metal die-casting releasing agent and further discloses a preparation method and application of the metal die-casting releasing agent. The high-property water-based metal die-casting releasing agent comprises the components of a functional organic composition, an assistant and a solvent. The functional organic composition comprises high-temperature-resisting resin, high-temperature-resisting silicone oil, mineral oil, animal and vegetable grease and the like, the assistant comprises a non-ionic surface active agent, a defoaming agent, a preservative, a sterilizing agent and the like, and the solvent is specifically deionized water. The high-property water-based aluminum alloy die-casting releasing agent is light yellow grey emulsion, the kinematic viscosity is 5-38 mm2 / s, the particle size is 200-500 nm, and the emulsion is stable; and in the aluminum die-casting technological process, the good lubricating and die releasing propertiesare achieved, the good cooling and heat-insulating properties are achieved, the good high-temperature wetting and lubricating properties are achieved, die sticking and destruction under pulling are prevented, carbon deposit and coking are avoided, thus a casting is purely white and bright, smoke and pollution are avoided, the clean environment is kept, and use is convenient and fast.

Description

technical field [0001] The invention relates to the technical field of release agents, in particular to a high-performance water-based metal die-casting release agent, a preparation method and an application thereof. Background technique [0002] As a metal forming method using a die, there are a casting method and a die forging method. Examples of casting methods include low-pressure casting methods, pressurized casting methods, and the like. In such a casting method, before filling the mold with molten metal, a release agent is used for the purpose of suppressing the reaction (welding) between the mold and the molten metal and also assisting the release of the shaped product. In the low pressure casting method, the squeeze casting method etc. which is one of the pressurized casting methods, due to the low speed of filling the mold cavity with molten metal such as aluminum alloy, the mold temperature and molten metal temperature are kept higher than typical A high-speed p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00B22D17/22
CPCB22C3/00B22D17/2209
Inventor 罗健军曾祥云
Owner 上海力太化学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com