Nylon 11/polylactic acid biological base high molecular alloy and preparation method and application thereof

A technology of bio-based polymer and polylactic acid, which is applied in the field of high-performance bio-based nylon 11/polylactic acid alloy and its preparation, can solve the problems of poor compatibility and stability of nylon 11/polylactic acid alloy, and achieve unique Biodegradability and biocompatibility, high strength and modulus, effect of increasing intrinsic viscosity

Inactive Publication Date: 2018-03-27
ZHONGBEI UNIV
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the problem of poor compatibility and stability of nylon 11 / polylactic acid alloy during processing, and to prepare a reinforced and toughened nylon 11 / polylactic acid bio-based polymer alloy material. The material has high tensile strength, high modulus, improved impact resistance, good thermal stability during processing, low price, low equipment requirements, and is suitable for industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nylon 11/polylactic acid biological base high molecular alloy and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-8

[0028] After drying 30-70 parts of nylon 11, 30-70 parts of polylactic acid, and 1-8 parts of reactive compatibilizer SAG008 at 60-80°C for 12-24 hours in vacuum, they are mixed with 0.1-0.6 parts of stabilizer, 0- Add 80 parts of additives into a high-speed mixer and mix at high speed for 3-5 minutes, then extrude through the discharge port of the twin-screw extruder to uniformly granulate, and finally dry in a vacuum oven at 60-80°C for 12-24 hours to remove moisture, and obtain the described Nylon 11 / polylactic acid bio-based polymer alloy sample. In the preparation process, the heating temperature control conditions in the twin-screw extruder are as follows: eight zones are set in sequence from the feed port to the discharge port, wherein the first zone is 170-180°C, the second zone is 170-180°C, and the third zone is 180°C. ~190°C, 180~190°C for the fourth zone, 190~200°C for the fifth zone, 190~200°C for the sixth zone, 200~210°C for the seventh zone, 200~210°C for the e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nylon 11 / polylactic acid biological base high molecular alloy, which comprises the following substances in parts by weight: 30-70 parts of nylon 11, 30-70 parts of polylacticacid, 1-8 parts of a compatilizer and 0.1-0.6 part of a stabilizer. A preparation method of the nylon 11 / polylactic acid biological base high molecular alloy comprises the following steps: vacuum-drying a PA11 matrix resin, a PLA resin, the compatilizer and the heat stabilizer; uniformly mixing the materials through a high speed mixer; then extruding the mixture through a twin-screw extruder, anduniformly granulating the mixture; and finally, drying the mixture in a vacuum oven to remove water. The primary raw material of the nylon 11 / polylactic acid biological base high molecular alloy is the biological base material, so that the demand on a petroleum-based high molecular material is lowered. The nylon 11 / polylactic acid biological base high molecular alloy material has great tensile strength, high modulus, high impact performance, good heat stability and low price, and the production process technology thereof has low demand on equipment, and the alloy is suitable for industrial production on a large scale.

Description

technical field [0001] The invention relates to the fields of polymer material technology and ecological environment materials, in particular to a high-performance bio-based nylon 11 / polylactic acid alloy and its preparation method and application. Background technique [0002] Polymer materials are one of the pillar industries of the national economy, and most of them come from petroleum products. However, my country's petroleum resources are very short. With the rising dependence of China's petroleum on foreign countries, the issue of petroleum strategic security has become very serious in front of us. , the lack of oil resources has become a "bottleneck" restricting the sustainable development of economy and society. At the same time, polymer materials are difficult to degrade, and the white pollution produced seriously affects the living environment of human beings. The development of new polymer materials using renewable biological resources is an important way to replac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L77/02C08L67/04C08L25/14C08K5/134C08K5/526
CPCC08L77/02C08L67/04C08L2201/08C08L2205/03C08L2205/08C08L25/14C08K5/134C08K5/526
Inventor 付一政杨潞霞廉紫超徐晓彤张建斌刘治宇
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products