Butyl rubber modified asphalt waterproof material as well as preparation method and application thereof

A technology of butyl rubber and modified asphalt, used in building thermal insulation materials, building components, buildings, etc., can solve the problem that the properties of asphalt cannot be effectively improved, easy to delaminate, coagulate or phase separate, and leakage of asphalt waterproof materials, etc. problems, to achieve safe and controllable operating conditions, easy mass production, and the effect of solving cracking

Inactive Publication Date: 2018-03-20
北京市住房和城乡建设科学技术研究所
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, asphalt cannot fully meet these requirements, resulting in serious leakage of asphalt waterproof materials and short service life.
Moreover, the existing modified asphalt only by adding materials has poor compatibility between the modifier and the asphalt, and is easy to delaminate, coagulate or phase separate, and the properties of the asphalt cannot be effectively improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Butyl rubber modified asphalt waterproof material as well as preparation method and application thereof
  • Butyl rubber modified asphalt waterproof material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] In the butyl rubber modified asphalt waterproof material provided in this embodiment, the amount of each raw material is as follows:

[0045] 90# Asphalt 45kg, butyl rubber 11kg, 4303 styrene butadiene rubber 5kg, minus third-line oil 11kg, talc 28kg. Wherein, the talc powder is 300 mesh, the butyl rubber is butyl rubber after desulfurization treatment, and the butyl rubber after desulfurization treatment does not contain sulfur.

[0046] The preparation method of the butyl rubber modified asphalt waterproof material in this embodiment includes the following steps:

[0047] A) Add all 45kg of 90# asphalt into the heating pot. After adding, heat to 140°C under stirring conditions, then add all 5kg of 4303 styrene butadiene rubber, and add 5.5kg of reduced third-line oil.

[0048] B) The mixture obtained in step A) is heated to 160° C. and stirred at low speed. After the 4303 styrene butadiene rubber is completely melted, the remaining 5.5 kg minus tertiary oil is added.

[0049] ...

Embodiment 2

[0052] In the butyl rubber modified bitumen waterproof material provided in this embodiment, the amount of each raw material is respectively: 90# asphalt 41kg, butyl rubber 13kg, 4303 styrene butadiene rubber 4kg, minus three-line oil 20kg, and talc 22kg. Wherein, the talc powder is 300 mesh, the butyl rubber is butyl rubber after desulfurization treatment, and the butyl rubber after desulfurization treatment does not contain sulfur.

[0053] The preparation method of the butyl rubber modified asphalt waterproof material in this embodiment includes the following steps:

[0054] A) Add all 41kg of 90# asphalt in the heating pot. After adding, heat to 140°C under stirring, then add all 4kg of 4303 styrene butadiene rubber, and add 10kg of reduced third-line oil.

[0055] B) The mixture obtained in step A) is heated to 160° C. and stirred at low speed. After the 4303 styrene butadiene rubber is completely melted, the remaining 10 kg minus third-line oil is added.

[0056] C) Control the ...

Embodiment 3

[0059] In the butyl rubber modified asphalt waterproof material provided in this embodiment, the amount of each raw material is as follows:

[0060] 90# Asphalt 42kg, butyl rubber 12kg, 4303 styrene butadiene rubber 3kg, minus three-line oil 18kg, talc 25kg. Wherein, the talc powder is 300 mesh, the butyl rubber is butyl rubber after desulfurization treatment, and the butyl rubber after desulfurization treatment does not contain sulfur.

[0061] The preparation method of the butyl rubber modified asphalt waterproof material in this embodiment includes the following steps:

[0062] A) Add all 42kg of 90# asphalt in the heating pot. After adding, heat to 140°C under stirring conditions, then add all 3kg of 4303 styrene butadiene rubber, and add 9kg of reduced third-line oil.

[0063] B) Raise the temperature of the mixture obtained in step A) to 160° C. and perform low-speed stirring. After the 4303 styrene butadiene rubber is completely melted, add the remaining 9 kg minus tertiary oil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of waterproof materials, in particular to a butyl rubber modified asphalt waterproof material as well as a preparation method and application thereof. Thebutyl rubber modified asphalt waterproof material is mainly prepared from the following components in percentage by weight: 40-60% of asphalt, 8-20% of butyl rubber, 2-4% of butadiene styrene rubber,6-25% of softening oil and 10-36% of talcum powder. According to the butyl rubber modified asphalt waterproof material disclosed by the invention, butyl rubber is added for modifying, so that ageing resistance and stable performance of asphalt are effectively improved, and embrittlement of the asphalt is improved; a little butadiene styrene rubber is added, so that strength of the waterproof material is improved; and butyl rubber and butadiene styrene rubber are good in compatibility, can form a homogenized mixed system with asphalt, and effectively improves performances of the asphalt, so that the waterproof material has the advantages of being resistant to a high temperature, a low temperature, ageing, corrosion and water; and meanwhile, low-temperature elasticity and plasticity as wellas high-temperature strength and stability are met.

Description

Technical field [0001] The present invention relates to the technical field of waterproof materials, in particular to a butyl rubber modified asphalt waterproof material and a preparation method and application thereof. Background technique [0002] Waterproof materials are a very important item in building products, which are related to the use value, use conditions and sanitary conditions of the building, and affect people's production activities and the quality of work and life. The quality of waterproof materials directly affects the function and service life of the building. With the continuous improvement of social living conditions, people pay more and more attention to their quality of life, and the requirements for waterproof conditions are constantly increasing. In recent years, with the development of social science and technology, new waterproof products and their engineering application technologies have developed rapidly. [0003] Waterproof materials are mostly use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L95/00C08L23/22C08L9/06C08L91/00C08K3/34
CPCC08L95/00C08L2201/08C08L2205/035C08L2205/08C08L23/22C08L9/06C08L91/00C08K3/34
Inventor 冷涛李树利郝根培
Owner 北京市住房和城乡建设科学技术研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap