A kind of high-temperature crystalline glaze with white dot pattern on yellow background and preparation method thereof

A high-temperature crystallization and white point technology, applied in the field of ceramics, can solve the problem of single color and fineness, and achieve the effect of high artistic aesthetic value

Active Publication Date: 2020-12-08
北京智匠文化咨询有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-temperature crystallization glaze with white dot pattern on yellow background and its preparation method, which effectively overcomes the lack of single color and fineness of ceramic glaze, and produces a special crystallization mechanism by firing mineral raw materials at high temperature The effect is combined with ceramic materials to achieve a very natural artistic texture effect and has a very high artistic aesthetic value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A high-temperature crystalline glaze with white dotted patterns on a yellow background, which is prepared by first preparing a high-temperature crystallized glaze with white dotted patterns on a yellow background, and then glazing and sintering at a high temperature. The raw materials contained in the dot pattern high-temperature crystallization glaze and the mass percentage of each raw material are:

[0038] Frit 38.7%, Calcined Zinc Oxide 29.3%, Silica 18.5%, Kaolin 3.5%, Titanium Dioxide 4.7%, Bentonite 1%, and Tin Oxide 4.3%.

[0039] Described frit, the raw material that comprises and the mass percent of each raw material thereof are:

[0040] Potassium oxide 1.8%, sodium oxide 15.9%, calcium oxide 7%, diboron trioxide 2% and silicon dioxide 73.3%.

[0041] A method for preparing high-temperature crystalline glaze with white dotted patterns on yellow background, comprising the following steps: firstly preparing high-temperature crystallized glaze with white dotted...

Embodiment 2

[0048] A high-temperature crystalline glaze with white dotted patterns on a yellow background, which is prepared by first preparing a high-temperature crystallized glaze with white dotted patterns on a yellow background, and then glazing and sintering at a high temperature. The raw materials contained in the dot pattern high-temperature crystallization glaze and the mass percentage of each raw material are:

[0049] Frit 33%, calcined zinc oxide 29%, silicon dioxide 13%, kaolin 5%, titanium dioxide 8%, bentonite 4% and tin oxide 8%;

[0050] Described frit, the raw material that comprises and the mass percent of each raw material thereof are:

[0051] Potassium oxide 1%, sodium oxide 19%, calcium oxide 4%, diboron trioxide 1%, and silicon dioxide 75%.

[0052] A method for preparing high-temperature crystalline glaze with white dotted patterns on yellow background, comprising the following steps: firstly preparing high-temperature crystallized glaze with white dotted patterns...

Embodiment 3

[0060] A high-temperature crystalline glaze with white dotted patterns on a yellow background, which is prepared by first preparing a high-temperature crystallized glaze with white dotted patterns on a yellow background, and then glazing and sintering at a high temperature. The raw materials contained in the dot pattern high-temperature crystallization glaze and the mass percentage of each raw material are:

[0061] Frit 43%, calcined zinc oxide 23%, silicon dioxide 23%, kaolin 4%, titanium dioxide 2%, bentonite 1% and tin oxide 4%;

[0062] Described frit, the raw material that comprises and the mass percent of each raw material thereof are:

[0063] Potassium oxide 3%, sodium oxide 10%, calcium oxide 10%, diboron trioxide 5% and silicon dioxide 72%.

[0064] A method for preparing high-temperature crystalline glaze with white dotted patterns on yellow background, comprising the following steps: firstly preparing high-temperature crystallized glaze with white dotted patterns...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

Yellow-base white-spotty-line high-temperature crystallizing glaze and a preparation method thereof belong to the field of ceramics. The yellow-base white-spotty-line high-temperature crystallizing glaze is prepared by: preparing yellow-base white-spotty-line high-temperature crystallizing glaze material, applying the glaze material, and sintering at high temperature, wherein the yellow-base white-spotty-line high-temperature crystallizing glaze material comprises, by weight, 33-43% of frit, 23-33% of calcined zinc oxide, 13-23% of silicon dioxide, 1-5% of kaolin, 2-8% of titanium dioxide, 1-4% of bentonite, and 4-8% of tin oxide; the frit comprises, by weight, 1-3% of potassium oxide, 10-20% of sodium oxide, 4-10% of calcium oxide, 1-5% of calcium oxide, 1-5% of boron trioxide, and 65-75%of silicon dioxide. The yellow-base white-spotty-line high-temperature crystallizing glaze and the preparation method thereof have the advantages that white spotty crystal is grown on the yellow ceramic glaze and is distributed evenly and special artistic effect is created.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a high-temperature crystalline glaze with white dotted pattern on a yellow background and a preparation method thereof. Background technique [0002] Ceramic glaze is an important raw material that must be used in the production of ceramics. It has a strong protective effect on the ceramic body. At the same time, the physical properties of silicate make the glass enamel on the ceramic surface effectively resistant to acid and alkali corrosion. Very good antibacterial properties. Ordinary ceramic color glazes are achieved by adding metal colorants to the glass enamel to achieve color development during the firing process. Such glaze colors are often single in color and cannot highlight the artistic beauty of the ceramic color glaze itself and the high-temperature firing process. special artistic effects produced in The high-temperature crystalline glaze with white dot pattern o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/20C03C8/02C03C1/06C04B41/86
CPCC03C1/06C03C8/02C03C8/20C04B41/5022C04B41/86
Inventor 沈海泳冼宁
Owner 北京智匠文化咨询有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com