Tear-resistant hard plastic film and preparation method thereof

A hard plastic and tear-resistant technology, applied in the field of plastic film, can solve problems such as uneven thickness, many fish eyes in the film, and poor transparency, so as to improve surface activity, tear resistance, and compatibility Effect

Inactive Publication Date: 2018-02-09
苏州工业园区汇统科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Plastic film is a common daily necessities for people nowadays. Plastic film has the advantages of good transparency, good moisture resistance, excellent heat resistance, convenient use, and low price. It is widely used in all walks of life. At present, plastic films on the market are mainly polymer Ethylene plastic film is the main product, but some products have problems such as wrinkles, poor transparency, uneven thickness, and many fish eyes in the film. The higher the higher, therefore, the higher the requirements for its tear strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of anti-tear hard plastic film, it is made up of the raw material of following weight part:

[0020] Vinyl carboxylate 3, azodicarbonamide 0.2, divinylbenzene 0.3, pyrithione zinc 1, polytetrafluoroethylene 140, aluminum dihydrogen phosphate 5, isopropanol 8, ferrous ammonium sulfate 2, tris Chloroisocyanuric acid 4, silicon micropowder 20, magnesium stearate 2, tetrakis hydroxymethyl phosphorus sulfate 1, fiber dispersion 20.

[0021] The preparation method of described fiber dispersion comprises the following steps:

[0022] Take ethyl cellulose, add it to 15 times its weight in deionized water, insulate and stir at 70°C for 10 minutes, add triethylamine, stir to normal temperature, and obtain the fiber dispersion.

[0023] A preparation method for a tear-resistant hard plastic film, comprising the following steps:

[0024] (1) Take silicon micropowder, add it to isopropanol, put it into a water bath at 60°C, add zinc pyrithione, keep it warm and stir for 20 ...

Embodiment 2

[0031] A kind of anti-tear hard plastic film, it is made up of the raw material of following weight part:

[0032] Vinyl carboxylate 1, azodicarbonamide 0.1, divinylbenzene 0.1, zinc pyrithione 0.5, polytetrafluoroethylene 120, aluminum dihydrogen phosphate 3, isopropanol 6, ferrous ammonium sulfate 1, tris Chloroisocyanuric acid 2, silicon micropowder 15, magnesium stearate 1, tetrakis hydroxymethyl phosphorus sulfate 0.6, fiber dispersion 15.

[0033] The preparation method of described fiber dispersion comprises the following steps:

[0034] Take ethyl cellulose, add it to 10 times its weight in deionized water, heat and stir at 60°C for 3 minutes, add triethylamine, stir to normal temperature, and obtain the fiber dispersion.

[0035] A preparation method for a tear-resistant hard plastic film, comprising the following steps:

[0036] (1) Take silicon micropowder, add it to isopropanol, put it into a water bath at 50°C, add zinc pyrithione, keep warm and stir for 10 minu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a tear-resistant hard plastic film, which comprises the following raw materials in parts by weight: 1-3 parts of vinyl carboxylate, 0.1-0.2 part of azodicarbonamide, 0.1-0.3 part of divinyl benzene, 0.5-1 part of zinc pyrithione, 120-140 parts of polytetrafluoroethylene, 3-5 parts of aluminum dihydrogen phosphate, 6-8 parts of isopropanol, 1-2 parts of ammonium ferrous sulfate, 2-4 parts of trichloroisocyanuric acid, 15-20 parts of silicon micropowder, 1-2 parts of magnesium stearate, 0.6-1 parts of Tetrakis hydroxymethyl phosphonium sulfate and 15-20 parts of a fiber dispersion. Esterified crosslinked fiber obtained can effectively improve the compatibility in the polytetrafluoroethylene, and the tear strength of the finished product can be further improved.

Description

technical field [0001] The invention belongs to the field of plastic films, and in particular relates to a tear-resistant rigid plastic film and a preparation method thereof. Background technique [0002] Plastic film is a common daily necessities for people nowadays. Plastic film has the advantages of good transparency, good moisture resistance, excellent heat resistance, convenient use, and low price. It is widely used in all walks of life. At present, plastic films on the market are mainly polymer Ethylene plastic film is the main product, but some products have problems such as wrinkles, poor transparency, uneven thickness, and many fish eyes in the film. The higher the higher, therefore, the higher the requirements for its tear strength. Contents of the invention [0003] The object of the present invention is to provide a tear-resistant rigid plastic film and a preparation method thereof for the defects and deficiencies of the prior art. [0004] To achieve the abo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/18C08L1/32C08K13/02C08K3/32C08K3/30C08K3/36C08K5/098C08J5/18
CPCC08L27/18C08J5/18C08J2327/18C08J2401/28C08K2003/3045C08K2003/327C08L2203/16C08L1/32C08K13/06C08K9/04C08K3/32C08K3/30C08K3/36C08K5/098
Inventor 俞育新韦建国
Owner 苏州工业园区汇统科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap