White cast iron with anti-fracture property and heat treatment technology

A technology of white cast iron and nickel-hard white cast iron, which is applied in the field of iron-carbon alloys, can solve problems such as low impact resistance, low toughness, and poor fracture resistance, so as to improve toughness and wear resistance, increase service life, and save energy. The effect of processing time

Inactive Publication Date: 2018-01-05
鲍凡凡
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the disadvantages of ordinary white cast iron such as low toughness, low impact resistance, and poor fracture resistance during use, the present invention proposes a white cast iron with fracture resistance and a heat treatment process. The composition of the white cast iron is more reasonable, Longer working life, easier manufacture, can greatly improve the mechanical properties of white cast iron, and can meet the needs of strong impact and other uses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The chemical composition of white cast iron in terms of mass percentage is as follows: C 2.0%, Si 0.6%, Cr 6.0%, Mn 0.2%, Ni 3.6%, Mo ≤0.98%, P ≤ 0.045%, S ≤ 0.06%, Fe margin.

Embodiment 2

[0022] The chemical composition of white cast iron in terms of mass percentage is as follows: C 2.8%, Si 0.9%, Cr 7.0%, Mn 0.38%, Ni 4.2%, Mo ≤0.98%, P ≤ 0.045%, S ≤ 0.06%, Fe margin.

Embodiment 3

[0024] The chemical composition of white cast iron in terms of mass percentage is as follows: C 2.5%, Si 0.8%, Cr 6.5%, Mn 0.3%, Ni 3.9%, Mo ≤0.98%, P ≤ 0.045%, S ≤ 0.06%, Fe margin.

[0025] The white cast iron with anti-fracture performance and the heat treatment process proposed by the present invention have novel components and a reasonable and clear production process. After two times of quenching and tempering, and through experiments to determine the quenching and tempering temperature, the treatment is carried out at this temperature. Greatly improve the toughness and wear resistance of nickel-hard white cast iron, make the cast iron less prone to cracks during use, and improve the service life. Productivity.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

White cast iron with anti-fracture performance and heat treatment process, belonging to the technical field of iron-carbon alloys, the chemical composition in terms of mass percentage is as follows: C 2.0-2.8%, Si 0.6-0.9%, Cr 6.0-7.0%, Mn 0.2 ~0.38%, Ni 3.6~4.2%, Mo ≤0.98%, P ≤0.045%, S ≤0.06%, Fe balance. The composition of the invention is novel, the production process is reasonable and clear, through two times of quenching and tempering, and the quenching and tempering temperature is determined through experiments, and the treatment is carried out at this temperature, which can greatly improve the toughness and wear resistance of nickel hard white cast iron , so that the cast iron is not easy to produce cracks during use, which improves the service life. The hardness after heat treatment in the as-cast state reaches 53HRC, and greatly saves the processing time of heat treatment and improves production efficiency.

Description

technical field [0001] The invention belongs to the technical field of iron-carbon alloys, and relates to a white cast iron, in particular to a white cast iron with fracture resistance and a heat treatment process. Background technique [0002] Cast iron in which carbon exists in the form of cementite, its cross-section is off-white. It is a good anti-wear material and works under abrasive wear conditions. White cast iron includes ordinary white cast iron, low alloy white cast iron, medium alloy white cast iron and high alloy white cast iron. [0003] Ordinary white cast iron White cast iron with good wear resistance was made in China as early as the Spring and Autumn Period, and was used as some wear-resistant parts. This kind of cast iron has the characteristics of high carbon and low silicon, and has high hardness, but is very brittle. It is suitable for making parts with small impact load, and is generally used in plowshares, grinding discs, guide plates, etc. Heat tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C37/10C21D5/04C21D1/18
Inventor 鲍凡凡
Owner 鲍凡凡
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products