High-hardness Jun porcelain sapphire glaze and preparation method thereof

A high-hardness, Jun porcelain technology, applied in the field of Jun porcelain manufacturing, can solve the problems of high production cost and difficulty, few formulas and preparation methods, low mechanical strength, etc., and achieve enhanced structural stability, mechanical strength and reproducibility Strong, mechanical strength improvement effect

Inactive Publication Date: 2018-01-05
禹州市锦丰源瓷业有限公司
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides a high-hardness jun porcelain sapphire blue glaze with novel raw materials and proportioning and a preparation method thereof to solve the problem tha

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hardness Jun porcelain sapphire glaze and preparation method thereof
  • High-hardness Jun porcelain sapphire glaze and preparation method thereof
  • High-hardness Jun porcelain sapphire glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A high-hardness Jun porcelain sapphire blue glaze, prepared from the following raw materials in parts by weight: 30-36 parts of feldspar, 20-28 parts of quartz, 12-18 parts of calcite, 12-18 parts of wollastonite, and 4 parts by weight of calcined talc -6 parts, zinc oxide 3-5 parts, tin oxide 0.5-1.5 parts, copper oxide 0.5-1.5 parts, cobalt oxide 0.3-0.7 parts, kaolin 3-5 parts.

[0024] The preparation method of above-mentioned Jun porcelain sapphire blue glaze of high hardness comprises the following steps:

[0025] (1) After pulverizing the above raw materials, mix them into a ball mill for ball milling, add water to make the mass concentration of the glaze reach 53-54%, wet mill for 7-8 hours, and pass the wet milled slurry through a 250-320 mesh sieve to obtain the glaze slurry ;

[0026] (2) The green body is dipped in glaze for 1-2 times;

[0027] (3) Firing, the firing temperature is 1200-1240°C.

[0028] Firing process specifically comprises the following ...

Embodiment 2

[0034] A high-hardness Jun porcelain sapphire blue glaze, prepared from the following raw materials in parts by weight: 33 parts of feldspar, 24 parts of quartz, 15 parts of calcite, 15 parts of wollastonite, 5 parts of burnt talc, 4 parts of zinc oxide, 1 part of tin, 1 part of copper oxide, 0.5 part of cobalt oxide, 4 parts of kaolin.

[0035] The preparation method of the Jun porcelain sapphire blue glaze of above-mentioned high hardness comprises the following steps:

[0036] (1) After pulverizing the above-mentioned raw materials, put them into a ball mill for ball milling, add water to make the mass concentration of the glaze reach 53%, wet mill for 7 hours, and pass the wet milled slurry through a 280-mesh sieve to obtain the glaze slurry;

[0037] (2) The green body is dipped in glaze twice;

[0038] (3) Firing, the firing process is as follows:

[0039] ①The body after glazing is put into the kiln and fired in an oxidizing atmosphere, so that the temperature rises t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-hardness Jun porcelain sapphire glaze, which is characterized by being prepared from the following materials in parts by weight: 30 to 36 parts of melilite, 20 to 28 parts of quartz, 12 to 18 parts of calcite, 12 to 18 parts of wollastonite, 4 to 6 parts of calcined talc, 3 to 5 parts of zinc oxide, 0.5 to 1.5 parts of tin oxide, 0.5 to 1.5 parts of copper oxide, 0.3to 0.7 part of cobalt oxide and 3 to 5 parts of kaolin. A preparation method of the high-hardness Jun porcelain sapphire glaze includes the following steps: (1) after being crushed, the materials aremixed, put into a ball mill and milled, water is added, so that the mass concentration of the glaze material reaches 53 to 54 percent, wet milling is conducted for 7 to 8 hours, and wet-milled slurrypasses through a 250- to 320-mesh sieve, so that glaze slurry is obtained; (2) a green body is dipped in the glaze once or twice; (3) firing is carried out, wherein firing temperature is 1200 DEG C to 1240 DEG C.

Description

technical field [0001] The invention relates to the technical field of Jun porcelain manufacturing, in particular to a high-hardness Jun porcelain sapphire blue glaze and a preparation method thereof. Background technique [0002] Jun porcelain originated in the Eastern Han Dynasty. It is one of the five famous kiln porcelains in the Song Dynasty. Famous for its unique kiln transformation art, it has the reputation of "gold is priceless and Jun porcelain is priceless" and "a family with a lot of money is not as good as a piece of Jun porcelain". [0003] Jun Porcelain is a unique national treasure porcelain in Shenhou Town, Yuzhou City, Xuchang City, Henan Province. With its simple shape, exquisite craftsmanship, complex glaze matching, and the magical kiln transformation of "one color in the kiln, thousands of colors in the kiln", the scenery of lakes and mountains, clouds and clouds Fog, human, animal, flower, bird, insect, fish, etc. are known as the first of the "Five F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/14C04B41/86
Inventor 崔松伟温红超崔世豪崔鹏豪
Owner 禹州市锦丰源瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap