A kind of composite nanofiber filter material with photocatalytic/antibacterial function and preparation method thereof

A technology of composite nanofibers and filter materials, which is applied in the field of composite nanofiber filter materials with both photocatalytic/antibacterial functions and its preparation, can solve the problems of easy blockage of the liquid outlet, achieve improved liquid output, small pore size, Effect of low resistance pressure drop

Active Publication Date: 2020-05-26
DONGHUA UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to effectively solve the problem of easy blockage of the liquid outlet of the existing needles / nozzles for electrospinning, have good photocatalytic efficiency for formaldehyde, amines and toluene, and have inhibitory effects on bacteria, viruses and microorganisms , with excellent filtration performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite nanofiber filter material with photocatalytic/antibacterial function and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A composite nanofiber filter material with both photocatalytic / antibacterial functions and a preparation method thereof, the preparation method comprising the following steps:

[0050]1) Spinning solution preparation: uniformly disperse titanium dioxide photocatalyst (addition amount 0.5wt%, particle size 10nm) and silver ion antibacterial agent (addition amount 0.5wt%) in formic acid to form dispersion liquid, utilize ultrasonic disperser ( Ultrasonic frequency 40kHz, ultrasonic temperature 80°C) after ultrasonic stirring for 20 minutes, nylon 6 (weight average molecular weight: 50,000) was added to the dispersion, and after sealing, it was continuously stirred for 15 hours with a magnetic stirring device, and finally a stable and uniform quality A polymer spinning solution with a concentration of 10%;

[0051] 2) Electrospinning: the prepared polymer spinning solution is sucked into the spinning module through the liquid supply device, and the combined needle for elec...

Embodiment 2

[0056] A composite nanofiber filter material with both photocatalytic / antibacterial functions and a preparation method thereof, the preparation method comprising the following steps:

[0057] 1) Spinning solution preparation: uniformly disperse titanium dioxide photocatalyst (addition amount 1wt%, particle size 15nm) and zinc oxide antibacterial agent (addition amount 0.1wt%) in N, N-dimethylacetamide to form a dispersion , using an ultrasonic disperser (ultrasonic frequency 40kHz, ultrasonic temperature 70°C) to ultrasonically stir for 30 minutes, polyurethane (weight average molecular weight: 80,000) was added to the dispersion, and after sealing, it was continuously stirred for 8 hours with a magnetic stirring device, and finally prepared into Stable and uniform polymer spinning solution with a mass concentration of 15%;

[0058] 2) Electrospinning: the prepared polymer spinning solution is sucked into the spinning module through the liquid supply device, and the combined n...

Embodiment 3

[0063] A composite nanofiber filter material with both photocatalytic / antibacterial functions and a preparation method thereof, the preparation method comprising the following steps:

[0064] 1) Spinning solution preparation: uniformly disperse titanium dioxide photocatalyst (addition amount 1.5wt%, particle size 18nm) and copper oxide antibacterial agent (addition amount 0.8wt%) in N, N-dimethylformamide to form a dispersed After ultrasonically stirring for 40 minutes with an ultrasonic disperser (ultrasonic frequency 35 kHz, ultrasonic temperature 50°C), polyvinylidene fluoride (weight-average molecular weight: 320,000) was added to the dispersion, and after sealing, it was continuously stirred for 9 hours with a magnetic stirring device. , finally prepared into a stable and uniform polymer spinning solution with a mass concentration of 18%;

[0065] 2) Electrospinning: the prepared polymer spinning solution is sucked into the spinning module through the liquid supply device...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Basis weightaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite nano fiber filtration material with photocatalysis / anti-bacterial functions and a preparation method of the filtration material. The filtration material comprises a supporting layer and a nano fiber filtration layer which adheres to the surface of the supporting layer, the nano fiber layer is uniformly filled with an photocatalyst and an antibacterial agent, and the preparation method comprises the following steps: 1, preparing a spinning liquid: dispersing a certain amount of the photocatalyst and the antibacterial agent into a solution uniformly to form a dispersion liquid, performing ultrasonic treatment, and adding a high polymer to form a stable and uniform electrostatic spinning solution; 2, performing electrostatic spinning: setting up electrostatic spinning parameters, and performing stretching on the spinning polymer solution at solid metal wire tips for wire production by utilizing an assembled needle head; and 3, performing slight dissolving treatment on the surface of the composite nano fiber filtration material by adopting solvent vapour recovery at a certain releasing speed to obtain the final composite nano fiber filtration material with the photocatalysis / the anti-bacterial functions. The composite nano fiber filtration material effectively solves a problem that the liquid outlet end of a current needle head / spray nozzle used for the electrostatic spinning is easy to block, can be directly used for decomposition of organic pollutants, inactivation of microorganism pathogenes and the like under visible light, and has excellent filtration performance at the same time.

Description

technical field [0001] The invention relates to a composite nanofiber filter material with both photocatalytic / antibacterial functions, in particular to a preparation method, that is, using a combined needle for electrospinning to realize the stretching of the spinning polymer solution at the tip of a solid metal wire The method is used to process the surface of the composite nanofiber filter material with microsolution at a certain release rate by recovering solvent vapor, which belongs to the field of functional filter materials. Background technique [0002] Smog and PM2.5 have attracted more and more attention and attention, and the source and harm of smog have become more and more known to people. In addition to air pollution sources such as PM2.5, there are also volatile organic compounds such as formaldehyde and benzene, as well as pollutants such as bacteria, viruses, and fungi, which bring great harm to human health. Therefore, in addition to intercepting fine part...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D39/16B01D53/86B01D53/72B01D53/58D01F6/90D01F6/94D01F6/48D01F6/92D01F6/52D01F6/50D01F6/44D01F6/54D01F1/10D01F11/08D01F11/06D01D5/00
CPCB01D39/1623B01D53/8634B01D53/8668B01D2239/0216B01D2239/025B01D2239/10D01D5/003D01F1/10D01F1/103D01F6/44D01F6/48D01F6/50D01F6/52D01F6/54D01F6/90D01F6/92D01F6/94D01F11/06D01F11/08
Inventor 丁彬廖亚龙李玉瑶赵兴雷印霞俞建勇
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com