Ultraviolet-light self-cleaning ceramic and preparation method thereof

A self-cleaning, ultraviolet light technology, applied in the field of sanitary ware

Inactive Publication Date: 2017-12-15
广东澳丽泰陶瓷实业有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The toilet has to be in contact with different users on the skin, and the function of the toilet is for excretion, so the hygienic condition must meet the requirements; the existing toilets on the market need to be cleaned regularly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Calculated in parts by mass: 32 parts of kaolin, 23 parts of quartz, 17 parts of dolomite, 23 parts of clay, 19 parts of perovskite, 11 parts of smithsonite, and 11 parts of sandstone. 10kg in total.

[0029] (1) According to the proportion, after mixing kaolin, quartz, dolomite, clay, perovskite, smithsonite and sandstone, ball milling is carried out according to the mass ratio of raw materials and grinding balls at 1:3 to obtain porcelain clay;

[0030] (2) Grout the porcelain clay, after repairing the embryo, fire at 400°C for 2 hours, then continue to heat up, stay at 900°C for 3 hours, then raise the temperature to 1350°C, and fire for 1 hour to obtain UV self-cleaning ceramics.

Embodiment 2

[0032] Calculated in parts by mass: 30 parts of kaolin, 20 parts of quartz, 15 parts of dolomite, 25 parts of clay, 20 parts of perovskite, 12 parts of smithsonite, and 12 parts of sandstone. 10kg in total.

[0033] (1) According to the proportion, after mixing kaolin, quartz, dolomite, clay, perovskite, smithsonite and sandstone, ball milling is carried out according to the mass ratio of raw materials and grinding balls at 1: 4 to obtain porcelain clay;

[0034] (2) Grout the porcelain clay, after trimming, fire at 500°C for 1 hour, then continue to heat up, stay at 700°C for 3 hours, then raise the temperature to 1250°C, and fire for 2 hours to obtain UV self-cleaning ceramics.

Embodiment 3

[0036] Calculated in parts by mass: 35 parts of kaolin, 25 parts of quartz, 18 parts of dolomite, 20 parts of clay, 18 parts of perovskite, 10 parts of smithsonite, and 10 parts of sandstone. 10kg in total.

[0037] (1) According to the proportion, after mixing kaolin, quartz, dolomite, clay, perovskite, smithsonite and sandstone, ball milling is carried out according to the mass ratio of raw materials and grinding balls at 1: 4 to obtain porcelain clay;

[0038] (2) Grout the porcelain clay, after repairing the embryo, fire at 500°C for 1 hour, then continue to heat up, stay at 700°C for 3 hours, then raise the temperature to 1300°C, and fire for 2 hours to obtain UV self-cleaning ceramics.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ultraviolet-light self-cleaning ceramic and a preparation method thereof. The method comprises the following steps: according to proportion, mixing kaolin, quartz, dolomite, clay, perovskite, smithsonite and sandstone rock, performing ball-grinding according to the mass ratio of raw materials to grinding balls of 1:(3-4) to obtain petuntse; grouting the petuntse, finishing blanks, sintering for 1 to 2 at 400-500DEG C, continuing heating, retaining for 2-3h at 700-900DEG C, heating to 1250-1350DEG C, and sintering to obtain the ultraviolet-light self-cleanness ceramic. The product has ultraviolet-light self-cleanness, and the high-efficient cleanness effect can be achieved by matching the ceramic with an ultraviolet light on the toilet product.

Description

technical field [0001] The invention belongs to the field of sanitary ware and sanitary ware, and in particular relates to an ultraviolet light self-cleaning ceramic and a preparation method thereof. Background technique [0002] The toilet is also called a toilet, which is a covered bucket for defecation. The invention of the toilet is called a great invention, which solves the problem of people's own eating and drinking. Later, it evolved into a toilet using the principles of siphon, spiral siphon, and now the latest jet siphon and super-rotary siphon. The toilet has to be in contact with different users on the skin, and the function of the toilet is for excretion, so the hygienic condition must meet the requirements; the existing toilets on the market all need to be cleaned regularly. Contents of the invention [0003] The invention discloses an ultraviolet light self-cleaning ceramic and a preparation method thereof. The ceramic is matched with an ultraviolet lam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/13E03D11/02
CPCC04B33/13C04B33/16C04B2235/321C04B2235/3236C04B2235/3284C04B2235/3418C04B2235/6022C04B2235/612C04B2235/656C04B2235/6567C04B2235/94E03D11/02
Inventor 谢培东吴洁新
Owner 广东澳丽泰陶瓷实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com