A kind of preparation method of micron titanium foil

A micron-scale, titanium foil technology, applied in contour control, manufacturing tools, metal rolling, etc., can solve the problems of narrow use range, long production cycle, complex process, etc., to achieve short production cycle, small work roll diameter, internal The effect of uniform structure

Active Publication Date: 2019-01-29
NORTHWEST INSTITUTE FOR NON-FERROUS METAL RESEARCH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the process is more complicated, the production cycle is longer, the finished product is thicker, and the scope of use is relatively narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of micron titanium foil
  • A kind of preparation method of micron titanium foil
  • A kind of preparation method of micron titanium foil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The preparation method of the micron titanium foil of this embodiment comprises the following steps:

[0041] Step 1. Send a titanium strip with a thickness of 0.198mm and a width of 120mm into a rolling mill for one-time rolling to obtain a semi-finished product of primary rolling titanium foil with a thickness of 0.058mm; Between 26.5kN and rolling tension between 110kg and 180kg; the titanium content in the titanium strip is not less than 99.95wt%, the hydrogen content is not more than 0.005wt%, the iron content is not more than 0.02wt%, and the oxygen content is not more than 0.05wt% %;

[0042] One rolling is 10-pass reversible rolling, the total reduction ratio is 70.7%, and the reduction ratios of 10 passes are 8.1%, 8.2%, 8.4%, 9.2%, 11.5%, 11.4%, 14.7%, 13.9%, 15.0%, 14.7%;

[0043] Step 2: Clean the primary rolled titanium foil semi-finished product obtained in step 1 and put it into a vacuum furnace, keep it warm for 100 minutes at 620°C, and the vacuum deg...

Embodiment 2

[0055] The preparation method of the micron titanium foil of this embodiment comprises the following steps:

[0056] Step 1. Send a titanium strip with a thickness of 0.196 mm and a width of 100 mm into a rolling mill for one-time rolling to obtain a semi-finished product of primary rolling titanium foil with a thickness of 0.056 mm; control the pressure of the pressure cylinder in the rolling mill to 25.5 kN to between 26.5kN and rolling tension between 105kg and 180kg; the titanium content in the titanium strip is not less than 99.95wt%, the hydrogen content is not more than 0.005wt%, the iron content is not more than 0.02wt%, and the oxygen content is not more than 0.05wt% %;

[0057] One rolling is 10-pass reversible rolling, the total reduction ratio is 71.4%, and the reduction ratios of 10 passes are 8.2%, 11.1%, 9.4%, 10.3%, 11.5%, 13.0%, 15.0%, 11.8%, 13.3%, 13.8%;

[0058] Step 2. Clean the primary rolled titanium foil semi-finished product obtained in step 1 and pu...

Embodiment 3

[0070] The preparation method of the micron titanium foil of this embodiment comprises the following steps:

[0071] Step 1. Send a titanium strip with a thickness of 0.2mm and a width of 80mm into the rolling mill for one-time rolling to obtain a semi-finished product of primary rolling titanium foil with a thickness of 0.054mm; control the pressure of the pressing oil cylinder in the rolling mill to 25.5kN~ Between 26.5kN and rolling tension between 100kg and 170kg; the titanium content in the titanium strip is not less than 99.95wt%, the hydrogen content is not more than 0.005wt%, the iron content is not more than 0.02wt%, and the oxygen content is not more than 0.05wt% %;

[0072] One rolling is 10-pass reversible rolling, the total reduction ratio is 73%, and the reduction ratios of 10 passes are 9.0%, 10.4%, 11.0%, 12.4%, 13.4%, 13.6%, 13.7%, 14.6%, 12.9%, 11.5%;

[0073] Step 2. Clean the primary rolled titanium foil semi-finished product obtained in step 1 and put it...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for micron-grade titanium foil. The preparation method comprises the steps that firstly, a titanium belt is fed into a rolling mill to be subjected to primary rolling, and a primary rolled titanium foil semi-finished product is obtained; second, after being washed, the primary rolled titanium foil semi-finished product is fed into a vacuum furnace to be subjected to heat preservation treatment; thirdly, the primary rolled titanium foil semi-finished product is fed into the rolling mill to be subjected to secondary rolling, and a secondary rolled titanium foil semi-finished product is obtained; fourthly, after being washed, the secondary rolled titanium foil semi-finished product is fed into the vacuum furnace to be subjected to heat preservation treatment; fifthly, the secondary rolled titanium foil semi-finished product is fed into the rolling mill to be subjected to tertiary rolling, and a tertiary rolled titanium foil semi-finished product is obtained; and sixthly, after being washed, the tertiary rolled titanium foil semi-finished product is fed into the vacuum furnace to be subjected to heat preservation treatment, and the finished titanium foil product is obtained. According to the preparation method, the technological process is simple, energy sources are saved, the energy consumption is low, the production efficiency is effectively improved, the titanium foil with the thickness only being 0.007 mm-0.009 mm can be prepared, the titanium foil is smooth in surface, the defects of cracking, peeling, folding, obvious oxidation and impurity pressing-in are not caused, the titanium foil can replace an existing titanium foil product, and the titanium foil has wide market space and development prospects.

Description

technical field [0001] The invention belongs to the technical field of titanium foil preparation, and in particular relates to a preparation method of micron titanium foil. Background technique [0002] Titanium foil is widely used in military sensors, aviation remote sensors, aerospace and electronic terminal vibration plates, civil medical treatment, loudspeakers and other industries. Another application market is as a catalyst carrier to promote oil cracking reactions. In recent years, it is also being developed for marine applications. Titanium foil for anti-corrosion of buildings and regular filling body for catalysts and titanium foil for the development of nuclear instruments for protection and detection, especially in the loudspeaker industry, because of its low hydrogen and iron content, high hardness, good ductility, especially ultra-thin The titanium sound film made of titanium foil has become the first choice for high-quality speakers. The published production p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/40B21B27/02B21B37/30C22F1/02C22F1/18
CPCB21B1/40B21B27/021B21B37/30B21B2027/022B21B2263/04B21B2267/18B21B2267/19C22F1/02C22F1/183
Inventor 张国霞舒滢展宏勋薛少博张洁杨森闫西安薛小田郭金明王国栋
Owner NORTHWEST INSTITUTE FOR NON-FERROUS METAL RESEARCH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap