Porous ceramics adopting biomass powder material as pore former

A technology of biomass powder and porous ceramics, applied in the field of porous ceramics, can solve problems such as environmental pollution, and achieve the effects of easy demoulding and less polluting gas emission.

Inactive Publication Date: 2017-11-28
九江汇泰科技有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, in the traditional ceramic production process, paraffin wax is often used as lubricant, which is easy to cause pollution to the environment when fired at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The invention discloses a porous ceramic using biomass powder as a pore-forming agent. In this embodiment, expressed in parts by weight, its raw material composition is:

[0027] 50 parts of cordierite powder, 5 parts of black mud powder, 10 parts of coal powder; 10 parts of biomass powder. 8 parts of medicine, 0.8 parts of stearic acid; 20 parts of water. The lubricant of the present embodiment contains 2 parts of kerosene, 4 parts of tallow, and 2 parts of tung oil.

[0028] Pass the powder in the above raw materials through a 30-mesh sieve to ensure that the particle size of each powder is uniform; melt kerosene, stearic acid, tallow, and tung oil for later use.

[0029] Knead all the materials in the kneader for half an hour, send the kneaded mud into the vacuum mud mixer for mixing, stale, and then pour it into the mold to form, cool, demould, and become porous after firing. ceramics.

[0030] Biomass powder is used as a pore-forming agent. Due to the good tough...

Embodiment 2

[0033] In the present embodiment, its raw material composition is:

[0034] 60 parts of cordierite powder, 8 parts of black mud powder, 16 parts of coal powder; 20 parts of biomass powder, in this embodiment, corn stalks are used as raw materials to make biomass powder, 1 part of hydroxypropyl methylcellulose 13 parts of lubricant, 2 parts of stearic acid; 25 parts of water. The lubricant of the present embodiment contains 4 parts of kerosene, 5 parts of tallow, and 4 parts of tung oil.

[0035] The particle size of various powders in this embodiment is 50 mesh.

[0036] The porous ceramic of this embodiment has a porosity of 62%.

Embodiment 3

[0038] In the present embodiment, its raw material composition is:

[0039] 75 parts of cordierite powder, 10 parts of black mud powder, 20 parts of pulverized coal; 30 parts of biomass powder, in the present embodiment, adopt dry grass milling as raw material to make biomass powder, 3 parts of hydroxypropyl methylcellulose , 20 parts of lubricant, 2.5 parts of stearic acid; 25 parts of water. The lubricant of the present embodiment contains 6 parts of kerosene, 8 parts of tallow, and 6 parts of tung oil.

[0040] The particle size of various powders in this embodiment is 100 mesh.

[0041] The porous ceramic of this embodiment has a porosity of 65%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of ceramics and particularly relates to porous ceramics adopting a biomass powder material as a pore former. The porous ceramics are prepared from the raw materials in parts by weight: 50-75 parts of cordierite powder, 5-10 parts of black mud powder, 10-20 parts of powder coal, 10-30 parts of biomass powder material, 0.5-5 parts of hydroxypropyl methylcellulose, 8-20 parts of lubricant, 0.8-2.5 parts of stearic acid and 20-30 parts of water. According to the porous ceramics, the biomass powder material is adopted as the pore former, and meanwhile, the powder coal is used for assisting pore forming, so that the porosity of the ceramic product is increased by 10% to 15% compared with that of the traditional technologies.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a porous ceramic using biomass powder as a pore-forming agent. Background technique [0002] In ceramic products, especially ceramic plates, the porosity has a great influence on the product performance. Products with high porosity have high air permeability, high thermal stability, and low density, which are suitable for the production of ceramic heaters. heating parts. At the same time, in the traditional ceramic production process, paraffin wax is often used as lubricant, which is easy to pollute the environment when fired at high temperature. Contents of the invention [0003] The purpose of the present invention is to overcome the deficiencies of the prior art, meet the actual needs, and provide a porous ceramic using biomass powder as a pore-forming agent. [0004] In order to realize the purpose of the present invention, the technical scheme adopted in the present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/06C04B35/195C04B35/636C04B35/632
CPCC04B35/195C04B35/632C04B35/6365C04B38/0675C04B38/068C04B38/0074
Inventor 李洁峰成贵华
Owner 九江汇泰科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap