Aromatic polyamide compound diaphragm, preparation method thereof and secondary battery

A technology of aromatic polyamide and composite diaphragm, which is applied in the direction of lithium batteries, battery pack components, non-aqueous electrolyte batteries, etc., and can solve the problems of lithium secondary batteries such as reduced safety, combustion or explosion, and limited temperature resistance. Achieve good thermal stability and chemical stability, increase safety, and have strong solvency

Active Publication Date: 2017-10-31
微宏先进膜公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The melting point of the polyolefin material is 160°C or lower, and the separator melts before the shutdown effect is obtained, which may cause a large-area short circuit between the electrodes, and the heat generated will cause the electrolyte to vaporize, causing combustion or explosion
The limitation of polyolefin diaphragm material is: limited temperature resistance, usually lower than 160°C, which reduces the safety of lithium secondary batteries, and is not suitable as a lithium ion power battery diaphragm for electric vehicles
Some domestic research institutes have applied aramid fibers to lithium-ion battery separators. For example, in the Chinese patent with the publication number CN103242556A and the Chinese patent with the announcement number CN202384420U, aromatic polyamide polymer fibers are coated on the surface of the polyolefin separator. These Applicability of the method is greatly compromised due to its limitation to polyolefin substrates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aromatic polyamide compound diaphragm, preparation method thereof and secondary battery
  • Aromatic polyamide compound diaphragm, preparation method thereof and secondary battery
  • Aromatic polyamide compound diaphragm, preparation method thereof and secondary battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060]Polymerize in a reaction kettle to obtain 4500 g of polym-phenylene isophthalamide solution, the solvent is DMAC, and the mass percent concentration of the polymer is 9%. 2300 g of N-methyl-N-propylpyrrolium tetrafluoroborate and 700 g of absolute ethanol were mixed in a stirred tank to obtain an ionic liquid solution. The ionic liquid solution and the polym-phenylene isophthalamide solution prepared in the previous stage were respectively injected into the stirring tank and mixed evenly, and then injected into the coating tank. Immerse the glass fiber cloth with a thickness of 12 μm and a single filament diameter of 4.5 μm into the mixed solution in the coating tank, take it out from the mixed solution and then squeeze it through a pressure roller to ensure a uniform thickness of the membrane. The coated film enters the gel bath, the gel bath is a mixed solvent of water and DMAC, wherein the mass percentage of water is 50%, the temperature of the gel bath is 60° C., and...

Embodiment 2

[0064] Same as Example 1, the difference is that 2300 g of N-methyl-N-propylpyrrolium tetrafluoroborate and 230 g of deionized water were mixed in a stirred tank to obtain an ionic liquid solution.

Embodiment 3

[0066] Same as Example 2, the difference is that the gel bath is water, the gel bath temperature is 80°C, the gel time is 10 seconds, and the drying temperature is 150°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an aromatic polyamide compound diaphragm, a preparation method thereof and a secondary battery. The aromatic polyamide compound diaphragm provided by the invention comprises a glass fiber and aromatic polyamide. The hot-shrinkage rate of the compound diaphragm at 300 DEG C is below 30%. The invention also provides the preparation method for the aromatic polyamide compound diaphragm. The compound diaphragm provided by the invention has excellent mechanical property and heat resistance and is especially suitable for the secondary battery.

Description

technical field [0001] The invention relates to an aromatic polyamide composite diaphragm, its preparation method and a secondary battery. Background technique [0002] As an outstanding representative of the new energy industry, lithium secondary batteries have shown a blowout growth in recent years. Especially in the field of electric vehicles, the supply of power batteries with high-rate charge-discharge performance is in short supply. With the extensive application of lithium secondary batteries in electric vehicles, battery safety has become one of the important criteria for power battery inspection. Among them, the lithium battery separator is the first "line of defense" to ensure the safety of single cells. At present, the separators that are widely used in lithium batteries are mainly polyolefin-based melt-stretched separators. The shutdown effect of these materials helps to improve safety when the battery heats up. [0003] However, when an internal short circuit ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M2/16H01M2/14H01M10/052H01M50/403H01M50/423H01M50/431H01M50/437H01M50/44H01M50/454H01M50/489H01M50/491H01M50/494
CPCH01M10/052H01M50/44H01M50/403H01M50/491H01M50/423H01M50/489H01M50/437H01M50/494Y02E60/10Y02T10/70C08L77/10C08L81/10C08L2203/20
Inventor 孙庆津李翔
Owner 微宏先进膜公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com