Method for absorbing wind turbine blade wastes in cement kiln

A technology for wind power blades and waste is applied in the field of absorbing wind power blade waste in cement kilns. The effect of less toxic gas

Inactive Publication Date: 2017-10-31
SINOMATECH WIND POWER BLADE
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above-mentioned problems, the present invention combines mechanical cutting and crushing technology, utilizes the wide accommodative capacity of cement kiln, and completely and thoroughly processes wind power blade waste, so as to solve the difficult problem of wind power blade waste disposal, and at the same time solve the problem of fuel and raw materials in the cement industry. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for absorbing wind turbine blade wastes in cement kiln
  • Method for absorbing wind turbine blade wastes in cement kiln

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] To transfer the scrapped wind power blades to the designated location, first use mechanical cutting to separate the metal parts and parts with high chlorine content from the main body of the blade. The metal parts are collected and sold in a centralized manner, and the parts with high chlorine content are temporarily stored. After the alternative fuel is blended, it enters the cement kiln under the premise that the chlorine content of the alternative fuel is less than 0.025%.

[0058] After removing the metal parts and parts with high chlorine content, cut the wind power blades into blocks with a length×width of 300×100mm, store the pure glass fiber reinforced plastic parts and the sandwich structural parts with core material, and put the glass fiber reinforced plastic parts and core materials to be pulverized The sandwich structure part is transported to the pulverizer device manually or by conveyor belt, and the pure FRP parts are pulverized by the pulverizer for secon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for absorbing wind turbine blade wastes in a cement kiln. The method comprises the following steps: separating metal parts and high-chlorine content parts in the wind turbine blade wastes, and segmenting the remaining wind turbine blade wastes as massive wastes; grinding the massive wastes into particles so as to obtain ground materials; and taking the ground materials as alternative fuel of the cement kiln, and combusting the fuel in a cement kiln decomposing furnace. The method disclosed by the invention is simple, practical, less in initial investment and subsequent maintenance cost, environment-friendly and harmless, belongs to a circular economy manner, accords with the treatment policy of 'reduction, recycling and harmlessness' of municipal wastes, can thoroughly implement and carry out the national policy of cooperatively treating non-medical wastes and industrial wastes in the cement kiln, solves the thermosetting material waste disposal difficulty problem troubling the society for a long time, provides alternative fuel and raw materials for the high-energy-consumption cement industry and has wide application prospects.

Description

technical field [0001] The invention relates to the field of wind power blade waste treatment, in particular to a method for accommodating wind power blade waste in a cement kiln. Background technique [0002] Thermosetting materials can be divided into thermosetting resin composite materials and thermosetting plastics. Thermosetting composite materials are generally composed of thermosetting resin as a matrix, glass fiber, carbon fiber and synthetic fiber as reinforcing materials, and wind turbine blades are thermosetting resin composite materials. Due to the excellent properties of light weight, high strength and corrosion resistance, thermosetting composite materials have been widely used in various industries in society. However, during the curing process of thermosetting resins, chemical bonds are formed between molecular chains, and a three-dimensional network structure is formed after curing, resulting in thermosetting materials. Infusible and insoluble, making this t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F23G5/033F23G5/44
CPCY02E20/12F23G5/033F23G5/44
Inventor 李永国赵小龙
Owner SINOMATECH WIND POWER BLADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com