Fireproof silicon rubber wallpaper

A technology of silicone rubber and silicone rubber layer, applied in the field of decorative materials, can solve the problems of easy to produce mildew, not easy to scrub, not resistant to stains, etc., and achieve the effects of not easily adhering to stains, improving smoothness, and improving tensile properties.

Pending Publication Date: 2017-10-24
东莞市火矽硅橡胶科技有限公司
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the problems in the prior art that the wallpaper is more or less not fireproof, prone to mildew, not moistureproof, not resistant to stains, not easy to scrub, etc., on the one hand, the present invention provides a fireproof silicone rubber wallpaper comprising a glue The adhesive is attached to the base layer on the wall and the silicone rubber layer outside the base layer, the base layer is a fireproof cloth with a thickness of 0.1 mm to 0.5 mm, and the silicone rubber layer is a silicone rubber layer with a thickness of 0.2 mm to 2.0 mm;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof silicon rubber wallpaper
  • Fireproof silicon rubber wallpaper
  • Fireproof silicon rubber wallpaper

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1: Preparation of fireproof silicone rubber wallpaper

[0048] In order to solve the problems that the wallpaper in the prior art is more or less not fireproof, prone to mildew, not moisture-proof, not resistant to stains, not easy to scrub, etc., this embodiment provides figure 1 The fireproof silicone rubber wallpaper shown includes a base layer 1 attached to the wall by an adhesive and a silicone rubber layer 3 located outside the base layer. The base layer 1 is a fireproof cloth with a thickness of 0.1 mm to 0.5 mm, and the silicone rubber layer 3 is A silicone rubber layer with a thickness of 0.2mm to 2.0mm. Fireproof cloth is also called flame-retardant cloth, specifically glass fiber cloth, basalt fiber fireproof cloth or acrylic cotton fiber fireproof cloth.

[0049] The main structural layer of fire-resistant silicone rubber wallpaper is the silicone rubber layer. Silicone rubber not only has a soft texture, but also makes the wallpaper feel better...

Embodiment 2

[0076] Embodiment 2: Preparation of fireproof silicone rubber wallpaper

[0077] The difference from the above-mentioned Example 1 is that the ratio of parts by weight of raw materials for the preparation of silicone rubber is:

[0078] Polymethylvinylsiloxane raw rubber (molecular weight 650,000-700,000, vinyl content 0.25%-0.35%): 60 parts;

[0079] Fumed silica: 10 parts;

[0080] High temperature resistant agent (silicon carbide): 1 part;

[0081] Flame retardant (magnesium hydroxide): 50 parts;

[0082] Structure control agent (alkoxy terminated small molecule silicone oil): 4 parts;

[0083] Platinum catalyst (chloroplatinic acid tetrahydrofuran solution): 1 part;

[0084] Delayed catalyst (3,7,11-trimethyldodeyn-3-ol): 2 parts;

[0085] Color masterbatch (raw rubber carrier): 15 parts.

[0086] Another difference between this embodiment and embodiment 1 is that when preparing fireproof silicone rubber wallpaper:

[0087] The base material is 0.5mm basalt fiber fi...

Embodiment 3

[0088] Embodiment 3: Preparation of fireproof silicone rubber wallpaper

[0089] The difference from the above-mentioned Example 1 is that the ratio of parts by weight of raw materials for the preparation of silicone rubber is:

[0090] Polymethyl vinyl siloxane raw rubber (molecular weight 600,000-700,000, vinyl content 0.25%-0.35%): 55 parts;

[0091] Fumed silica: 8 parts;

[0092] High temperature resistant agent (silicon carbide): 0.8 parts;

[0093] Flame retardant (aluminum oxide): 45 parts;

[0094] Structure control agent (diphenyldihydroxysilane): 2 parts;

[0095] Platinum catalyst (chloroplatinic acid-divinyltetramethyldisiloxane complex): 0.8 parts;

[0096] Delay catalyst (methyl butynol): 1.6 parts;

[0097] Color masterbatch (raw rubber carrier): 10 parts.

[0098] Another difference between this embodiment and embodiment 1 is that when preparing fireproof silicone rubber wallpaper:

[0099] The thickness of the bridging agent coating is controlled at 0.05...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of decorative materials, and particularly relates to fireproof silicon rubber wallpaper. The fireproof silicon rubber wallpaper comprises a base layer and a silicon rubber layer, wherein the base layer is attached to a wall face, and the silicon rubber layer is attached to the outer part of the base layer. The base layer is fireproof cloth with the thickness of 0.1 mm-0.5 mm, and the thickness of the silicon rubber layer is 0.2 mm-2.0 mm; a bridging agent layer with the thickness of 0.01 mm-0.1 mm is evenly sprayed between the base layer and the silicon rubber layer, and the top face of the base layer and the bottom face of the silicon rubber layer are fully bonded by the bridging agent layer; and an ink layer is sprayed on the top face of the silicon rubber layer, and ink used in the ink layer is oil with the silicone hand feeling or silicone PU ink. The fireproof silicon rubber wallpaper has flame resistant and high-temperature resistant performance, corrosion resistance, damp prevention and stain resistance and is easy to scrub; and the fireproof cloth of the base layer and the main silicon rubber layer are made of environmental-friendly materials, gas harmful to human health is not generated, and the fireproof silicon rubber wallpaper is well suitable for indoor decoration using.

Description

technical field [0001] The invention belongs to the technical field of decorative materials, and in particular relates to a fireproof silicone rubber wallpaper. Background technique [0002] Wallpaper, also known as wallpaper, is an interior decoration material used to paste walls, and is widely used in interior decoration of houses, offices, hotels, hotels, etc. Wallpapers are divided into many categories, such as laminated wallpapers, coated wallpapers, embossed wallpapers, etc. Usually produced from bleached chemical wood pulp base paper , and then processed by different processes, such as coating, printing, Embossed Or the surface is covered with plastic, and finally it is cut and packaged before leaving the factory. [0003] Wallpaper is widely used in some wall or wall decoration, because of its low price and strong decoration, it is loved by consumers. When people decorate houses, the wood, stone, paint, paint and other materials used in the decoration contain ch...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/00B32B25/20B32B25/10B32B7/12B32B5/02
CPCE04F13/002B32B5/02B32B7/12B32B25/10B32B25/20E04F2290/047B32B2255/02B32B2250/02B32B2255/10B32B2255/26B32B2262/0223B32B2262/10B32B2262/103
Inventor 蓝火连
Owner 东莞市火矽硅橡胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com