Preparation method of methylated polythiophene electromagnetic material

A technology of methylated polythiophene and electromagnetic materials, applied in the field of materials, can solve the problems of difficulty in dispersion, affecting the research and application of graphene, etc., and achieves the effects of good safety and environmental protection, time saving and production cost reduction.

Inactive Publication Date: 2017-10-24
赵阳
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Graphene with a complete structure is composed of stable benzene six-membered rings, its surface is inert, and the interaction force between it and the polymer is small, while there is a strong van der Waals force between the graphene sheets, which is easy to aggregate and difficult to Uniform dispersion in the polymer matrix, which seriously affects the research and application of graphene in polymer modification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing a methylated polythiophene electromagnetic material, comprising the following steps:

[0026] (1) Take 60 parts by weight of thiophene, add it to chloroform which is 6 times its weight, stir evenly, add 3 parts by weight of 3-aminopropyltriethoxysilane, raise the temperature to 45°C, and ultrasonically for 1 hour, Chloroform was removed by distillation to obtain an aminated monomer;

[0027] (2) Take the above-mentioned aminated monomer, add it into a hydrogen peroxide solution 10 times its weight, and stir evenly;

[0028] (3) Take 90 parts by weight of graphene, add it to 96% sulfuric acid solution that is 30 times its weight, stir evenly, add 50 parts by weight of potassium permanganate, stir at 25°C for 16 hours, filter, and remove the precipitate Washing with water, drying at room temperature, adding to the hydrogen peroxide solution of the aminated monomer, stirring for 1 hour, raising the temperature to 70°C, adding 6 parts by weight of ol...

Embodiment 2

[0035] A method for preparing a methylated polythiophene electromagnetic material, comprising the following steps:

[0036] (1) Take 70 parts by weight of thiophene, add it to 9 times its weight in chloroform, stir evenly, add 4 parts by weight of 3-aminopropyltriethoxysilane, raise the temperature to 50°C, and ultrasonically for 2 hours, Chloroform was removed by distillation to obtain an aminated monomer;

[0037] (2) Take the above-mentioned aminated monomer, add it into a hydrogen peroxide solution 14 times its weight, and stir evenly;

[0038] (3) Take 100 parts by weight of graphene, add it to 98% sulfuric acid solution that is 40 times its weight, stir evenly, add 60 parts by weight of potassium permanganate, stir at 30°C for 20 hours, filter, and remove the precipitate Washing with water, drying at room temperature, adding to the hydrogen peroxide solution of the above-mentioned aminated monomer, stirring for 2 hours, increasing the temperature to 75°C, adding 9 parts...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a methylated polythiophene electromagnetic material, wherein water is used as a solvent instead of chloroform as the solvent in a polymerization reaction of thiophene in prior art, so that complex processes for treating the organic solvent is avoided, and time is saved and production cost is reduced; meanwhile, with deionized water as the reaction solvent, the method has good safety, is environment-friendly, and is beneficial to industrial production.

Description

technical field [0001] The invention belongs to the field of materials, and in particular relates to a method for preparing a methylated polythiophene electromagnetic material. Background technique [0002] Conductive polymers are a class of polymers with conjugated structures. Chemical, electrochemical or ion doping can make the conductivity level of the polymer from the insulating level to the metal level. It is used in capacitors, energy, metal anti-corrosion and biosensors. It has a good application prospect; [0003] Polythiophene has been paid attention to by researchers because of its good optical, electrical and environmental stability. It is compounded with inorganic nanomaterials to form organic-inorganic nanocomposites, not only because of the introduction of inorganic substances to improve its original performance, but also because of the nano effect and the synergy between polythiophene and inorganic substances, the performance of composite materials is better ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G61/12C08K9/04C08K9/02C08K3/04C08K3/22
CPCC08G61/126C08G2261/11C08G2261/143C08G2261/144C08G2261/3223C08K3/04C08K3/22C08K9/02C08K9/04C08K2003/2275C08K2201/01
Inventor 赵阳
Owner 赵阳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com