Computer mouse cell material and preparation method thereof

A shell material and computer technology, applied in the field of mouse materials, can solve problems such as poor fire resistance, poor wear resistance, and insufficient environmental protection, and achieve improved wear resistance, acid and alkali resistance, heat resistance, and insulation Good results

Inactive Publication Date: 2017-09-22
HEFEI SIBOT SOFTWARE DEV CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Among the above-mentioned mouse materials, the environmental protection is not enough, and the wear resistance is poor, and the fire resistance is poor, so a computer mouse shell material is needed to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of computer mouse housing material of the present embodiment comprises the raw material of following weight portion:

[0031] 25 parts of polycarbonate, 15 parts of fluorosilicone rubber, 40 parts of acrylonitrile-butadiene-styrene copolymer, 12 parts of glass fiber, 4 parts of diatomaceous earth, 18 parts of cast stone powder, 6 parts of silicon nitride, 3 parts of silicone oil 5 parts of paraffin, 10 parts of phosphite, 8 parts of zinc oxide, 2 parts of essence, 16 parts of plasticizer, 1 part of stabilizer, and 1 part of antistatic agent.

[0032] In this embodiment, the glass fiber has a length of 0.5 mm and a diameter of 0.1 mm; the meshes of the cast stone powder and zinc oxide are 500 mesh.

[0033] In this embodiment, the essence is a mixture of peppermint essence, jasmine essence, geranium essence, mimosa essence, and ylang-ylang essence.

[0034] In this embodiment, the plasticizer is triethyl citrate, tributyl citrate, acetyl tributyl citrate, triocty...

Embodiment 2

[0046] A kind of computer mouse housing material of the present embodiment comprises the raw material of following weight portion:

[0047] 28 parts of polycarbonate, 17 parts of fluorosilicone rubber, 45 parts of acrylonitrile-butadiene-styrene copolymer, 13 parts of glass fiber, 6 parts of diatomaceous earth, 19 parts of cast stone powder, 7 parts of silicon nitride, 4 parts of silicone oil 6 parts of paraffin, 12 parts of phosphite, 9 parts of zinc oxide, 3 parts of essence, 17 parts of plasticizer, 2 parts of stabilizer, and 2 parts of antistatic agent.

[0048] In this embodiment, the glass fiber has a length of 0.8 mm and a diameter of 0.3 mm; the meshes of the cast stone powder and zinc oxide are 500 mesh.

[0049] In this embodiment, the essence is a mixture of peppermint essence, jasmine essence, geranium essence, mimosa essence, and ylang-ylang essence.

[0050] In this embodiment, the plasticizer is triethyl citrate, tributyl citrate, acetyl tributyl citrate, triocty...

Embodiment 3

[0062] A kind of computer mouse housing material of the present embodiment comprises the raw material of following weight portion:

[0063] 30 parts of polycarbonate, 18 parts of fluorosilicone rubber, 50 parts of acrylonitrile-butadiene-styrene copolymer, 14 parts of glass fiber, 8 parts of diatomaceous earth, 20 parts of cast stone powder, 8 parts of silicon nitride, 5 parts of silicone oil 1, 7 parts of paraffin, 14 parts of phosphite, 10 parts of zinc oxide, 4 parts of essence, 18 parts of plasticizer, 3 parts of stabilizer, and 3 parts of antistatic agent.

[0064] In this embodiment, the glass fiber has a length of 1 mm and a diameter of 0.5 mm; the cast stone powder and zinc oxide have a mesh size of 500 mesh.

[0065] In this embodiment, the essence is a mixture of peppermint essence, jasmine essence, geranium essence, mimosa essence, and ylang-ylang essence.

[0066] In this embodiment, the plasticizer is triethyl citrate, tributyl citrate, acetyl tributyl citrate, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a computer mouse cell material, and belongs to the technical field of a mouse material. The material comprises the following raw materials, by weight part, 25-30 parts of polycarbonate, 15-18 parts of fluorosilicone rubber, 40-50 parts of an acrylonitrile-butadiene-styrene copolymer, 12-14 parts of glass fiber, 4-8 parts of diatomite, 18-20 parts of cast stone powder, 6-8 parts of silicon nitride, 3-5 parts of silicone oil, 5-7 parts of paraffin, 10-14 parts of phosphate, 8-10 parts of zinc oxide, 2-4 parts of essence, 16-18 parts of a plasticizer, 1-3 parts of a stabilizer and 1-3 parts of an antistatic agent. The invention further discloses a preparation method of the material. The material is small in environmental pollution and excellent in wear resistance and high temperature resistance and gives off fragrance.

Description

technical field [0001] The invention relates to the technical field of mouse materials, in particular to a computer mouse shell material and a preparation method thereof. Background technique [0002] The mouse is an input device of a computer, and it is also an indicator of the vertical and horizontal coordinates of the computer display system. It is named "mouse" because it looks like a mouse. [0003] The mouse shell material is generally made of plastics, but the current mouse shell plastics have insufficient wear resistance, poor strength, poor fire resistance, short service time, and the mouse will emit plastic odor, which affects the user's state. [0004] In the patent document whose publication number is CN106046645A, a special anti-slip composite material for computer mouse and its preparation method are disclosed. The main raw materials of the special anti-slip composite material for computer mouse include: modified resin 26-32 parts, 10-15 parts of polyphenylene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L83/08C08L69/00C08K13/04C08K7/14C08K5/524C08K3/22C08K3/36C08K3/34
CPCC08L55/02C08K2003/2296C08K2201/003C08K2201/004C08K2201/007C08K2201/014C08L2201/02C08L2201/08C08L2205/035C08L83/08C08L69/00C08K13/04C08K7/14C08K5/524C08K3/22C08K3/34
Inventor 吴青明
Owner HEFEI SIBOT SOFTWARE DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com