Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Water atomization manufacturing method of silver containing super-performance copper alloy powder

A manufacturing method and alloy powder technology are applied in the field of water atomization manufacturing of silver-containing super-performance copper alloy powder, which can solve the problem of insufficient wear resistance and machinability, ductility can not reach the expected target, and silver materials cannot be completely integrated, etc. problem, to achieve the effect of excellent ductility, good machinability

Inactive Publication Date: 2017-09-05
金华市程凯合金材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Many existing engine bearings are made of lead-containing alloy materials, which have certain deficiencies in wear resistance and machining performance
[0003] However, the existing few silver-containing alloy materials, due to their different manufacturing methods, generally have the problem that the silver material cannot be completely fused, so the ductility cannot reach the expected goal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A method for producing silver-containing super-performance copper alloy powder by water atomization, the main components and weight ratio of the silver-containing super-performance copper alloy powder are: 90.0-93.5% copper, 5.0-7.0% tin, 0.8 ~1.2% silver, 0.5~1.5% copper phosphide;

[0017] The described water atomization manufacturing method is:

[0018] 1) Add the above-mentioned main components into the intermediate frequency electric furnace according to the specified ratio, add a stabilizer when all the raw materials are melted, and carry out slag removal and refining at a temperature of 1250 ° C to 1350 ° C to form a pure alloy liquid;

[0019] 2) Check and analyze the ingredients in front of the furnace, and after confirming that it is qualified, add a covering agent to carry out heat preservation control at 1250 ° C ~ 1350 ° C;

[0020] 3) Then pour the clean copper alloy liquid into it, so that the free-falling copper alloy liquid flow can be efficiently atom...

Embodiment 2

[0023] A water atomization manufacturing method of silver-containing super-performance copper alloy powder, the main components and weight ratio of the silver-containing super-performance copper alloy powder are: 90.0% copper, 5.0% tin, 0.8% silver, 0.5% copper phosphide.

Embodiment 3

[0025] A method for producing silver-containing super-performance copper alloy powder by water atomization, the main components and weight ratio of the silver-containing super-performance copper alloy powder are: 92% copper, 6% tin, 1.0% silver, 1.0% copper phosphide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water atomization manufacturing method of silver containing super-performance copper alloy powder. The silver containing super-performance copper alloy powder comprises the following main components in a ratio by weight parts: 90.0-93.5% of copper, 5.0-7.0% of tin, 0.8-1.2% of silver and 0.5-1.5% of copper phosphate. The water atomization manufacturing method of the silver containing super-performance copper alloy powder has the advantages of great ductility, excellent machining performance and high wear resistance.

Description

technical field [0001] The invention relates to a water atomization manufacturing method of silver-containing super-performance copper alloy powder. Background technique [0002] As a rotating component, the engine bearing is destined to require super wear resistance due to its working method. Many existing engine bearings are made of lead-containing alloy materials, which have certain deficiencies in wear resistance and machining performance. [0003] However, due to the different manufacturing methods of the existing few silver-containing alloy materials, there are generally problems such as the inability of the silver material to be completely fused, resulting in the failure of the ductility to meet the expected goal. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide a water atomization manufacturing method of silver-containing super-performance copper alloy powder with good ductility, good machinability and hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C9/02C22C1/02C22C1/10B22F9/08
CPCB22F9/082B22F2009/0828B22F2009/0848C22C1/02C22C1/1036C22C9/02
Inventor 蒋守高陈连生陆春兰
Owner 金华市程凯合金材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com