A kind of on-line rapid spheroidizing annealing method of gcr15 bearing steel after hot rolling

A spheroidizing annealing and bearing steel technology, applied in the field of bearing steel heat treatment, can solve the problems of long spheroidizing time and shortening spheroidizing annealing time, and achieve the effects of short isothermal time, low rolling resistance and high production efficiency

Active Publication Date: 2018-07-13
NORTHEASTERN UNIV LIAONING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Aiming at the problems that existing GCr15 bearing steel has too long spheroidizing time in the spheroidizing process, the purpose of the present invention is to provide a method for on-line rapid spheroidizing annealing of GCr15 bearing steel after hot rolling, by adjusting the rolling temperature Reasonable selection, using optimized spheroidizing treatment process, controlling the precipitation of proeutectoid carbides in the rolling process through deformation induction, shortening the time required for spheroidizing annealing, and improving energy efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of on-line rapid spheroidizing annealing method of gcr15 bearing steel after hot rolling
  • A kind of on-line rapid spheroidizing annealing method of gcr15 bearing steel after hot rolling
  • A kind of on-line rapid spheroidizing annealing method of gcr15 bearing steel after hot rolling

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The online rapid spheroidizing annealing method of the GCr15 bearing steel in this embodiment is carried out according to the following steps:

[0036] 1. Heat the sample to be rolled to 1000°C in a high-temperature box-type resistance furnace, and treat it isothermally for 30 minutes.

[0037] 2. The initial thickness of the sample is 25mm. After isothermal treatment, a single-pass rolling is carried out at 1000°C to refine the austenite grains. The reduction is 7mm, and the thickness after rolling is about 18mm.

[0038] 3. After the first pass of rolling, air-cool and wait until the temperature reaches 780°C, and carry out three consecutive passes of rolling. About 760°C.

[0039] 4. Put the rolled steel plate into the east and west through-type heat treatment furnaces for isothermal treatment. The isothermal temperature is 720°C, and the isothermal time is 4h. After the isothermal treatment, the furnace is cooled to 600°C, and the furnace-cooled plate is air-cooled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of heat treatment of bearing steel, and particularly relates to an online rapid spheroidizing annealing method after hot rolling of GCr15 bearing steel. In order to solve the problem of too long spheroidization time in the existing GCr15 bearing steel during the spheroidization process, through the reasonable selection of rolling temperature and the use of optimized spheroidization process, the proeutectoid carbides during the rolling process are controlled. Precipitation through deformation induction shortens the time required for spheroidizing annealing and improves energy efficiency. The method of the present invention adopts an online spheroidizing annealing method, and only requires a short subsequent spheroidizing treatment time to form a relatively good spheroidized structure. From the observation and analysis of the metallographic structure, the structure after spheroidizing annealing is fine ferrite and fine dispersed spherical carbide particles. The spheroidization grade can reach level 1, the hardness is 200HV, and the hardness also meets the usage requirements.

Description

technical field [0001] The invention belongs to the field of heat treatment of bearing steel, in particular to an online rapid spheroidizing annealing method after hot rolling of GCr15 bearing steel. Background technique [0002] Bearings are widely used in various fields of the national economy, and are known as "the heart of industry" internationally. Bearing quality In addition to bearing structure design and manufacturing accuracy, bearing steel is the key, which plays a vital role in the processing quality, service life and reliability of bearing products. [0003] The common failure mode of rolling bearings is fatigue spalling, that is, contact fatigue damage. The microstructure of GCr15 bearings in service is composed of martensite, carbide and a small amount of retained austenite. The content, size, shape and distribution of carbide It not only affects the distribution and performance of martensite, but also affects the final service performance of the entire bearin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/32C21D8/02C21D6/00
CPCC21D1/32C21D6/004C21D6/005C21D6/008C21D8/0226C21D2211/004C21D2211/005
Inventor 韩东序杜林秀胡军齐祥羽张彬吴红艳
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com