Damping paint for engine

A damping coating and engine technology, applied in the field of damping coatings, can solve the problems of poor noise reduction effect and unsatisfactory engine performance, and achieve good acid, alkali and salt spray resistance, good flame retardancy, and good salt spray resistance Effect

Active Publication Date: 2017-08-11
郑州安邦达水性材料有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing damping coatings are not very effective in terms of flame retardancy and noise reduction, and cannot meet the needs of engines.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Damping paint for engine
  • Damping paint for engine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An engine damping paint, calculated in parts by weight, including the following raw materials: 300 parts of plasticized acrylic emulsion, 40 parts of antimony trioxide, 40 parts of melamine, 20 parts of active magnesium hydroxide, 25 parts of coarse sepiolite, mica powder 50 parts, 75 parts of silica powder, 15 parts of preservative and 5 parts of black paste.

[0031] Calculated in parts by weight, plasticized acrylic emulsion includes the following raw materials:

[0032] 160 parts of butyl acrylate, 100 parts of styrene, 40 parts of methyl methacrylate, 117 parts of α-ethylhexyl acrylate, 12 parts of methacrylic acid, 9 parts of ammonium acrylate, 15 parts of acrylonitrile, 422 parts of water, 1.7 parts of ammonium sulfate, 1.8 parts of oxidation-reduction initiator system, 2.5 parts of pH adjuster, 0.7 parts of emulsifier and 1.5 parts of chloromethyl isothiazolinone. Among them, the oxidation-reduction initiator system is composed of 0.8 part of inorganic reducing agen...

Embodiment 2

[0040] An engine damping paint, calculated in parts by weight, including the following raw materials: 290 parts of plasticized acrylic emulsion, 35 parts of antimony trioxide, 35 parts of melamine, 18 parts of active magnesium hydroxide, 23 parts of coarse sepiolite, and mica powder 45 parts, 70 parts of silica powder, 17 parts of preservative and 6 parts of black paste.

[0041] Calculated in parts by weight, plasticized acrylic emulsion includes the following raw materials:

[0042] 150 parts of butyl acrylate, 90 parts of styrene, 35 parts of methyl methacrylate, 112 parts of α-ethylhexyl acrylate, 14 parts of methacrylic acid, 11 parts of ammonium acrylate, 17 parts of acrylonitrile, 390 parts of water, 1.2 parts of potassium sulfate, 1.4 parts of oxidation-reduction initiator system, 3 parts of pH adjuster, 0.5 parts of emulsifier and 2 parts of chloromethyl isothiazolinone, among which the oxidation-reduction initiator system consists of 0.6 parts of inorganic reducing agent ...

Embodiment 3

[0049] An engine damping paint, calculated in parts by weight, including the following raw materials: 310 parts of plasticized acrylic emulsion, 45 parts of antimony trioxide, 45 parts of melamine, 22 parts of active magnesium hydroxide, 27 parts of coarse sepiolite, and mica powder 55 parts, 80 parts of silica powder, 13 parts of preservative and 4 parts of black paste.

[0050] Calculated in parts by weight, plasticized acrylic emulsion includes the following raw materials:

[0051] 170 parts of butyl acrylate, 110 parts of styrene, 45 parts of methyl methacrylate, 122 parts of α-ethylhexyl acrylate, 10 parts of methacrylic acid, 8 parts of ammonium acrylate, 13 parts of acrylonitrile, 450 parts of water, 2.2 parts of sodium sulfate, 2.2 parts of oxidation-reduction initiator system, 4 parts of pH adjuster, 1 part of emulsifier and 1 part of chloromethyl isothiazolinone, of which the oxidation-reduction initiator system consists of 1 part of inorganic reducing agent and It is co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides damping paint for an engine. The damping paint comprises raw materials in parts by weight as follows: 290-310 parts of plasticizing acrylic emulsion, 35-45 parts of antimony (III) oxide, 35-45 parts of melamine, 18-22 parts of active magnesium hydroxide and 138-162 parts of functional filler. The damping paint for the engine has good flame retardance, noise isolation property and resistance to acid, alkali and salt spray, and meets application demands of the engine.

Description

Technical field [0001] The invention belongs to the technical field of damping paint, and specifically relates to an engine damping paint. Background technique [0002] Because water-based damping coatings mainly use water as a dispersant, they have low VOC and are green and environmentally friendly, and are now gradually replacing traditional organic solvent-based damping coatings and asphalt-based damping sheets. At the same time, due to the characteristics of the coating, it can be easily coated on more complex interfaces without cutting. Therefore, it has more advantages in construction than the traditional butyl rubber damping film. Due to the disadvantages of water-based damping coatings, their wider applications are also limited. [0003] Damping paint is a new type of functional material that can absorb vibrational mechanical energy. Various mechanical equipment or transportation vehicles' engines or electromechanical equipment will produce varying degrees of vibration a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/08C09D7/12C09D5/18C08F220/18C08F212/08C08F220/14C08F220/06C08F220/44
CPCC08F220/18C08F220/1804C08K3/22C08K3/34C08K3/346C08K5/34922C08K13/02C08K2003/2224C08K2201/014C09D5/18C09D133/08C08F212/08C08F220/14C08F220/06C08F220/44
Inventor 孙天宝谢金彪
Owner 郑州安邦达水性材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com