Preparation method and application of fluorine-containing microspheres without stabilizers on surfaces

A stabilizer and microsphere technology, used in coatings, powder coatings, etc., can solve problems such as harming the health of construction workers, cumbersome processing, and a large amount of organic solvents, achieving good hydrophobicity and corrosion resistance, simple preparation method, Fast response time

Inactive Publication Date: 2017-08-11
FOSHAN UNIVERSITY
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method still requires a series of treatments on the surface of inorganic particles. The treatment process is cumbersome and requires the use of a large amount of organic solvents, which not only pollutes the environment, but also endangers the health of construction workers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of fluorine-containing microspheres without stabilizers on surfaces
  • Preparation method and application of fluorine-containing microspheres without stabilizers on surfaces
  • Preparation method and application of fluorine-containing microspheres without stabilizers on surfaces

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] 1) Add 120 mL of anhydrous tetrahydrofuran (THF) to a single-necked flask, add 2 mmol of polyethylene glycol monomethyl ether (mPEG), 4 mmol of RAFT reagent 4-(2-carboxyethylcarbonyl) oxyethoxyphenyl di Isobutyronitrile thiocarbamate (CEPDB) and 0.2 mmol 4-dimethylaminopyridine (DMAP) were dissolved in anhydrous tetrahydrofuran (THF), and the one-necked flask was placed in an ice-water bath and cooled to 0°C with stirring;

[0053] 2), 2), 4mmol dicyclohexylcarbodiimide (DCC) was dissolved in 30mL anhydrous tetrahydrofuran (THF) to obtain a DCC-THF solution, and the DCC-THF solution was added dropwise in a single-necked flask, and the dropping time was controlled at After 30 minutes of dripping, continue to place the reaction kettle in an ice-water bath for 1 hour after the addition;

[0054] 3), the one-necked flask was taken out from the ice-water bath, then stirred and reacted at room temperature for 48 hours, and the insoluble matter dicyclohexyl urea (DCU) in the r...

Embodiment 2

[0069] 1) Add 120 mL of anhydrous tetrahydrofuran (THF) to a single-necked flask, add 2 mmol of polyethylene glycol monomethyl ether (mPEG), 2.2 mmol of RAFT reagent 4-(2-carboxyethylcarbonyl)oxyethoxyphenyl Isobutyronitrile dithiocarbamate (CEPDB) and 0.02 mmol 4-dimethylaminopyridine (DMAP) were dissolved in anhydrous tetrahydrofuran (THF), and the one-necked flask was placed in an ice-water bath and cooled to 0°C with stirring;

[0070] 2), 2), 2mmol dicyclohexylcarbodiimide (DCC) was dissolved in 30mL anhydrous tetrahydrofuran (THF) to obtain a DCC-THF solution, and the DCC-THF solution was added dropwise in a single-necked flask, and the dropping time was controlled at After 40 minutes of dripping, continue to place the reaction kettle in an ice-water bath for 1 hour after the addition;

[0071] 3), the one-necked flask was taken out from the ice-water bath, then stirred and reacted at room temperature for 48 hours, and the insoluble matter dicyclohexyl urea (DCU) in the ...

Embodiment 3

[0086] 1) Add 120 mL of anhydrous tetrahydrofuran (THF) to a single-necked flask, add 2 mmol of polyethylene glycol monomethyl ether (mPEG), 3 mmol of RAFT reagent 4-(2-carboxyethylcarbonyl) oxyethoxyphenyl di Isobutyronitrile thiocarbamate (CEPDB) and 0.1 mmol 4-dimethylaminopyridine (DMAP) were dissolved in anhydrous tetrahydrofuran (THF), and the one-necked flask was placed in an ice-water bath and cooled to 0°C with stirring;

[0087] 2) Dissolve 5mmol of dicyclohexylcarbodiimide (DCC) in 30mL of anhydrous tetrahydrofuran (THF) to obtain a DCC-THF solution, add the DCC-THF solution dropwise into a single-necked flask, and the dropping time is controlled within 30 minutes to complete the drop After the dropwise addition is completed, continue to place the reaction kettle in an ice-water bath for 1 hour of reaction;

[0088] 3), the one-necked flask was taken out from the ice-water bath, then stirred and reacted at room temperature for 48 hours, and the insoluble matter dicy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and an application of fluorine-containing microspheres without stabilizers on the surfaces. Anhydrous THF (tetrahydrofuran) is added to a single-neck flask, mPEG (methoxy polyethylene glycol), an RAFT reagent CEPDB (4-(2-carboxyethylcarbonyl)oxy-ethoxy phenyl dithiocarbamate isobutyronitrile ester) and DMAP (4-dimethylaminopyridine) are dissolved in anhydrous THF, the single-neck flask is placed in an ice-water bath, and the mixture is stirred and cooled to 0 DEG C; DCC (dicyclohexylcarbodiimide) is dissolved in anhydrous THF, and a DCC-THF solution is obtained; the DCC-THF solution is all dropwise added to the single-neck flask within 30-50 min, and the single-neck flask is continuously placed in the ice-water bath for a reaction for 1 h after the DCC-THF solution is dropwise added. The method is rapid, environment-friendly and energy-saving, and fluorine-containing polymer microspheres without stabilizers on the surfaces are rapidly prepared with an optical RAFT dispersion polymerization method and a thermal aftertreatment method with an ethanol / water mixed solvent as a reaction medium. The preparation method is simple and the reaction speed is high.

Description

technical field [0001] The invention relates to the field of superamphiphobic materials, in particular to a preparation method and application of fluorine-containing microspheres without a stabilizer on the surface. Background technique [0002] Surface wettability is an important characteristic of solid surfaces, and the contact angle (CA) is usually used to characterize the wettability of liquids on solids. Generally speaking, a superhydrophobic surface refers to a surface with a contact angle between a solid surface and water > 150° and a rolling angle < 10°, and if the contact angle of a solid surface to oil > 150°, it becomes a superoleophobic surface. The superhydrophobic / oleophobic superamphiphobic surface has the characteristics of self-cleaning, anti-fouling, anti-fog, hydrophobic, etc., and has a wide range of applications in the fields of coatings, construction, liquid transportation, and biomedicine. [0003] The construction of superamphiphobic surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F293/00C08F220/22C09D153/00C09D5/03
CPCC08F220/22C08F293/005C09D5/03C09D153/00
Inventor 余明光王青陈奕鸿陈尚贤林滨滨卢敏仪欧海浩左思雅
Owner FOSHAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com