A kind of preparation method of calligraphy practice gold brick writing board

A technology of writing boards and gold bricks

Active Publication Date: 2020-09-15
苏州市相城区蠡口袁氏堂澄泥蟋蟀盆工作室
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, cement is added as one of the raw materials of the gold brick writing board, and the adhesion effect of the raw materials is improved through the adhesive effect, but the short setting time of the cement limits the static treatment of the materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of calligraphy practice gold brick writing board
  • A kind of preparation method of calligraphy practice gold brick writing board
  • A kind of preparation method of calligraphy practice gold brick writing board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of preparation method of Chinese calligraphy writing board, comprises the following steps:

[0052] The first step: make the main ingredients:

[0053] Take the lake mud at a depth of 10-12m under the lake, dry the lake mud and crush it into 1.0-1.2mm fine grains to obtain the main ingredient;

[0054] The second step: with materials:

[0055] Materials comprising the following parts by weight: 80 parts of main ingredients, 10 parts of amorphous silicon dioxide, 30 parts of aluminum oxide, 15 parts of graphite, and 20 parts of water;

[0056] Mix the main ingredients with water and stir evenly at low speed, add graphite and then stir quickly for 1 hour, then add Al2O3 and amorphous silica, stir slowly for 0.5 hours, then stand at low temperature for 10 hours to obtain brick-making materials;

[0057] The third step: billet making:

[0058] Put the above-mentioned brick-making materials into the mold, the size of the green body is 60cm*60cm*5cm, and the pressur...

Embodiment 2

[0064] A kind of preparation method of Chinese calligraphy writing board, comprises the following steps:

[0065] The first step: make the main ingredients:

[0066] Take the lake mud at a depth of 10-12m under the lake, dry the lake mud and crush it into 1.0-1.2mm fine grains to obtain the main material;

[0067] The second step: with materials:

[0068] Materials comprising the following parts by weight: 100 parts of main ingredients, 12 parts of amorphous silicon dioxide, 32 parts of aluminum oxide, 25 parts of graphite, and 30 parts of water;

[0069] Mix the main ingredients with water and stir evenly at a low speed, add graphite and stir quickly for 2 hours, then add aluminum oxide and amorphous silica, stir slowly for 1 hour, then stand at low temperature for 12 hours to obtain brick-making materials;

[0070] The third step: billet making:

[0071] Put the above-mentioned brick-making materials into the mold, the size of the green body is 60cm*60cm*5cm, and the pres...

Embodiment 3

[0077] A kind of preparation method of Chinese calligraphy writing board, comprises the following steps:

[0078] The first step: make the main ingredients:

[0079] Take the lake mud at a depth of 10-12m under the lake, dry the lake mud and crush it into 1.0-1.2mm fine grains to obtain the main material;

[0080] The second step: with materials:

[0081] Materials comprising the following parts by weight:

[0082] 92 parts of main ingredients, 12 parts of amorphous silicon dioxide, 30 parts of aluminum oxide, 18 parts of graphite, and 30 parts of water.

[0083] Mix the main ingredients with water and stir evenly at a low speed, add graphite and then stir quickly for 1 hour, then add aluminum oxide and amorphous silica, stir slowly for 0.5 hours, then stand at low temperature for 12 hours to obtain brick-making materials;

[0084] The third step: billet making:

[0085] Put the above-mentioned brick-making materials in the mold, the size of the green body is 40cm*40cm*3cm, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a copybook golden brick writing board. The preparation method comprises the following steps of 1, preparing a main material, wherein lake mud of the deep portion of the bottom of a lake is adopted, the lake mud is smashed after dried to obtain the main material; 2, preparing raw materials, comprising, by weight, 80-100 parts of main materials, 10-12 parts of amorphous silica dioxide, 30-32 parts of aluminium oxide, 15-25 parts of graphite and 20-30 parts of water, the main materials and the water are mixed and uniformly stirred at a low speed, after the graphite is added, quick stirring is conducted, then aluminium oxide and amorphous silica dioxide are added, and slow stirring and low-temperature settling are conducted to obtain a brick preparation material; 3, preparing a raw brick; 4, firing in vacuum; 5, cooling. Cement is not added in the raw materials of the golden brick writing board, the product writing board is smooth and exquisite, water-absorbent, stable in structure, not easy to crack, high in mechanical strength and long in service life.

Description

technical field [0001] The invention relates to a preparation method of a writing board, in particular to a preparation method of a writing board made of gold bricks for calligraphy without adding cement. Background technique [0002] Gold bricks are two-foot-square bricks; since the Forbidden City was first built, this kind of gold bricks made by special techniques has always been a special item in the Forbidden City. Such bricks are laid in the important palaces of the Forbidden City. The gold bricks of the Hall of Supreme Harmony we see now were laid during the Kangxi period of the Qing Dynasty. To this day, they are still as bright as new. This unique gold brick in the world is produced in the outskirts of Suzhou. Because Suzhou's soil is fine and rich in colloids, and has strong plasticity, the gold bricks made are hard and dense. The gold bricks are produced in Yuyao Village, Lumu Town, Xiangcheng District, Suzhou City, Jiangsu Province. Yuyao Village was originall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/132C04B33/32C04B33/14
CPCC04B33/13C04B33/131C04B33/1321C04B33/14C04B33/323C04B2235/3217C04B2235/3418C04B2235/425C04B2235/444C04B2235/448C04B2235/96Y02P40/60
Inventor 袁中平
Owner 苏州市相城区蠡口袁氏堂澄泥蟋蟀盆工作室
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com