C30 concrete and preparation method thereof

A concrete, per cubic technology, applied in the field of C30 concrete and its preparation, to achieve the effect of protecting the ecological environment, the best effect, and reducing serious damage to the environment

Inactive Publication Date: 2017-08-08
CHONGQING JURONG CONSTR GRP
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a concrete production company, how to recycle the construction waste in the renovation of the old city and the waste water from the mixing station in the company's concrete production, reduce construction waste pollution and achieve zero discharge of waste water, and directly use the recycled construction waste and waste water in concrete Production and other construction industries create greater economic benefits for the company while making our ecological environment more environmentally friendly. The inventors of the present invention have found no mention or report after investigation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] C30 concrete, each cubic C30 concrete is composed of the following raw materials: 304kg of P.O42.5R cement, 400kg of river sand, 400kg of machine-made sand, 200kg of recycled aggregate with a particle size of 5-10mm, and recycled aggregate with a particle size of 10-25mm Aggregate 785kg, tap water 82kg, concrete mixing plant recycled water 82kg, S75 mineral powder 51kg, point-400s admixture 6.9kg, sugar retarder 1.9kg, the slump of the C30 concrete is 180mm.

[0017] The preparation method of the C30 concrete is: first, add river sand, machine-made sand, recycled aggregate with a particle size of 5-10mm, recycled aggregate with a particle size of 10-25mm, P.O42.5R cement, and S75 grade mineral powder in order. , tap water, recycled water from the concrete mixing plant, point-400s admixture and sugar retarder, then stir in the mixer for 60 seconds before leaving the machine, and the temperature of the machine is controlled at 25°C.

Embodiment 2

[0019] C30 concrete, each cubic C30 concrete is composed of the following raw materials: 309kg of P.O42.5R cement, 405kg of river sand, 405kg of machine-made sand, 205kg of recycled aggregate with a particle size of 5-10mm, and recycled aggregate with a particle size of 10-25mm Aggregate 795kg, tap water 85kg, concrete mixing plant recycled water 85kg, S75 mineral powder 54kg, point-400s admixture 7.3kg, sugar retarder 2.1kg, the slump of the C30 concrete is 200mm.

[0020] The preparation method of the C30 concrete is: first, add river sand, machine-made sand, recycled aggregate with a particle size of 5-10mm, recycled aggregate with a particle size of 10-25mm, P.O42.5R cement, and S75 grade mineral powder in order. , tap water, recycled water from the concrete mixing plant, point-400s admixture and sugar retarder, then stir in the mixer for 60 seconds before leaving the machine, and the temperature of the machine is controlled at 30°C.

Embodiment 3

[0022] C30 concrete, each cubic C30 concrete is composed of the following raw materials: 315kg of P.O42.5R cement, 410kg of river sand, 410kg of machine-made sand, 210kg of recycled aggregate with a particle size of 5-10mm, and recycled aggregate with a particle size of 10-25mm Aggregate 805kg, tap water 88kg, concrete mixing station recycled water 88kg, S75 mineral powder 57kg, polycarboxylate admixture 7.7kg, glucose retarder 2.3kg, the slump of the C30 concrete is 220mm.

[0023] The preparation method of the C30 concrete is: first, add river sand, machine-made sand, recycled aggregate with a particle size of 5-10mm, recycled aggregate with a particle size of 10-25mm, P.O42.5R cement, and S75 grade mineral powder in order. , tap water, recycled water from the concrete mixing plant, polycarboxylate admixture and glucose retarder, then stir in the mixer for 60 seconds before leaving the machine, and the temperature of the machine is controlled at 35°C.

[0024] Compared with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
slumpaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides C30 concrete. One cubic meter of C30 concrete is prepared from the following raw materials: 304 to 315kg of P.O42.5R cement, 400 to 410kg of river sand, 400 to 410kg of machine-made sand, 200 to 210kg of recycled aggregate with the particle diameter being 5 to 10mm, 785 to 805kg of recycled aggregate with the particle diameter being 10 to 25mm, 82 to 88kg of tap water, 82 to 88kg of concrete stirring station recovery water, 51 to 57kg of S75 stage ore powder, 6.9 to 7.7kg of additives and 1.9 to 2.3kg of retarders; the fall highness of the C30 concrete is 200+ / -20mm. The invention also provides a preparation method of the C30 concrete. In the C30 concrete provided by the invention, the content of the tap water and recovery water is respectively 50 percent; for the mixed recovery water, the ingredients of additives are regulated, so that the fall highness of the C30 concrete is 200+ / -20mm; the quality effect identical to that of the concrete mixed by using pure tap water can be achieved; in addition, 50-percent recovery water is mixed in the C30 concrete; the C30 concrete workability is greatly changed; the use of the tap water is reduced; in addition, the recycled aggregate is obtained through crushing, processing and screening building garbage; the material cost is reduced; meanwhile, the ecological environment is effectively protected.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a C30 concrete and a preparation method thereof. Background technique [0002] With the continuous acceleration of the urbanization process in our country, a large number of people are pouring into the city. While the economy is booming, various problems continue to emerge: road traffic congestion, frequent smog weather, air quality decline, random discharge of waste water, etc., all of which are It is becoming a bottleneck restricting the sustainable development of cities. Among them, waste water refers to the general term of water discharged during residents' activities and runoff rainwater, which includes domestic sewage, industrial waste water, and other useless water such as primary rain tracks flowing into drainage pipes and canals. Wastewater treatment refers to the use of physical, chemical and biological methods to treat wastewater, purify wastewater, reduce ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/16C04B22/00
CPCC04B18/16C04B22/0046C04B28/04C04B14/068C04B14/06C04B22/002C04B14/02C04B2103/302C04B24/10C04B24/24Y02W30/91
Inventor 梁华国梁华勇陈忠伟
Owner CHONGQING JURONG CONSTR GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products