Ceramic blank and manufacturing method thereof

The technology of a ceramic body and a manufacturing method, which is applied in the field of ceramics, can solve the problems of poor appearance of the body, non-wear resistance of the ceramic body, and easy aging and cracking, and achieve good surface smoothness, increased hardness, and improved strength. plasticity effect

Pending Publication Date: 2017-07-11
玉林龙升建筑装饰工程有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The existing ceramic body is relatively rough fired, and its performance is relatively poor. It not only has problems such as low strength and fragility, but also in the case of no internal and external glazing, the ceramic body is not wear-resistant and prone to aging and cracking. And the appearance of the green body without glazing is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic blank and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A kind of ceramic green body provided by the present embodiment comprises 80 parts by weight of basic blanks, 10 parts by weight of reinforcing agents and 1 part by weight of auxiliary agents; wherein, the basic blanks are composed of the following raw materials by weight: 35 parts by weight of diopside , 15 parts of quartz, 10 parts of silicon dioxide, 10 parts of potassium feldspar, 8 parts of zirconium boride, 5 parts of hydroxypropyl methylcellulose, 5 parts of vanadium carbide and 10 parts of absolute ethanol; the reinforcing agent consists of the following parts by weight Composition of raw materials: 30 parts of bentonite, 5 parts of nano silica gel, 5 parts of tungsten disulfide, 5 parts of ABS resin, 1 part of rosin and 1 part of zinc oxide; the auxiliary agent is composed of the following raw materials by weight: 20 parts of aluminum oxide, magnesium oxide 5 parts, talcum powder 10 parts, styrene-butadiene rubber 5 parts and polyethylene glycol 4 parts.

[004...

Embodiment 2

[0056] A kind of ceramic green body provided by the present embodiment comprises 100 parts by weight of a base material, 15 parts by weight of a reinforcing agent and 3 parts by weight of an auxiliary agent; wherein, the base material consists of the following raw materials by weight: 45 parts by weight of diopside , 18 parts of quartz, 12 parts of silicon dioxide, 12 parts of potassium feldspar, 10 parts of zirconium boride, 7 parts of hydroxypropyl methylcellulose, 6 parts of vanadium carbide and 18 parts of absolute ethanol; the reinforcing agent consists of the following parts by weight Composition of raw materials: 38 parts of bentonite, 7 parts of nano-silica gel, 7 parts of tungsten disulfide, 7 parts of ABS resin, 3 parts of rosin and 3 parts of zinc oxide; the auxiliary agent is composed of the following raw materials by weight: 28 parts of aluminum oxide, magnesium oxide 8 parts, talcum powder 15 parts, styrene-butadiene rubber 10 parts and polyethylene glycol 6 parts...

Embodiment 3

[0073] A kind of ceramic green body provided by the present embodiment comprises 120 parts by weight of base material, 20 parts by weight of reinforcing agent and 5 parts by weight of auxiliary agent; wherein, the base material is made up of the following raw materials by weight: 65 parts by weight of diopside , 20 parts of quartz, 15 parts of silicon dioxide, 15 parts of potassium feldspar, 12 parts of zirconium boride, 10 parts of hydroxypropyl methylcellulose, 8 parts of vanadium carbide and 25 parts of absolute ethanol; the reinforcing agent consists of the following parts by weight Composition of raw materials: 45 parts of bentonite, 10 parts of nano silica gel, 10 parts of tungsten disulfide, 10 parts of ABS resin, 5 parts of rosin and 5 parts of zinc oxide; the auxiliary agent is composed of the following raw materials by weight: 35 parts of aluminum oxide, magnesium oxide 12 parts, 20 parts of talcum powder, 15 parts of styrene-butadiene rubber and 7 parts of polyethyle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a ceramic blank and a manufacturing method thereof, and relates to the technical field of ceramics, the ceramic blank includes 80-120 parts by weight of a based blank, 10-20 parts by weight of an enhancer and 1-5 parts by weight of an additive; the production process of the ceramic blank comprises the following steps: 1) making mud, 2) making a wet blank, and 3) drying the blank. Through the improvement of raw materials and production methods, the prepared ceramic blank has good chemical stability and good mechanical strength, and the prepared ceramic blank also has good toughness and shaping property, is anti-falling and not easy to break, has low production cost, long service life and wide application range, and is worthy of promotion.

Description

[0001] 【Technical field】 [0002] The invention relates to the technical field of ceramics, in particular to a ceramic green body and a manufacturing method thereof. [0003] 【Background technique】 [0004] China is one of the first countries in the world to apply ceramics. The so-called ceramics include pottery and porcelain. The products made of ceramics mainly include daily-use, art, and architectural pottery. Ceramics are widely used in the fields of tableware, decoration, and science because of their hard texture, fineness, and high temperature resistance. [0005] The existing ceramic body is relatively rough fired, and its performance is relatively poor. It not only has problems such as low strength and fragility, but also in the case of no internal and external glazing, the ceramic body is not wear-resistant and prone to aging and cracking. And the appearance of the green body without glazing is poor. [0006] 【Content of invention】 [0007] In view of this, the purp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/22C04B35/626
CPCC04B35/22C04B35/62605C04B35/62615C04B35/62635C04B35/6266C04B2235/3206C04B2235/3217C04B2235/3284C04B2235/3418C04B2235/3445C04B2235/3472C04B2235/349C04B2235/3813C04B2235/3839C04B2235/446C04B2235/77C04B2235/96C04B2235/9607
Inventor 高琦
Owner 玉林龙升建筑装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com