Fabric made of high polymer material

A technology of polymer materials and fabrics, applied in the field of fabrics made of polymer materials, can solve problems affecting the appearance of fabrics, and achieve the effects of good sales, good dyeability, and good air permeability

Inactive Publication Date: 2017-06-13
QINGDAO CHENYUN E COMMERCE CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, whether it is sunshade cloth or curtains, it is not often cleaned by consumers, especially outdoor fabrics used outdoors need to withstand the test of external weather environments such as wind, rain, and sun. It will contain a variety of organic and inorganic pollutants, which not only affect the appearance of the fabric, but also the accumulated dirt will cause the growth and reproduction of microorganisms on the surface of the fabric

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0029] The fabric of this embodiment is prepared by the following preparation process:

[0030] A, after blending 2 parts of polyester fiber, 3 parts of bamboo fiber, 4 parts of cupro ammonia fiber, 3 parts of polylactic acid fiber, and 1 part of seaweed fiber, carry out melt granulation, and then spin space change yarn and weave gray cloth;

[0031] Further, each raw material in the step A is subjected to opening pretreatment before blending: each raw material is opened into a single fiber shape, impurities are removed, carding is carried out on a carding machine, and each raw material is pre-opened , which is conducive to the uniform mixing of raw materials.

[0032] B, putting the gray cloth into the finishing solution for padding, then drying and cooling to obtain the finished fabric; the finishing solution includes the following ingredients: 20g / L titanium dioxide, 18g / L acrylate adhesive, 2g / L glycerin , Gemini cationic softener 35g / L, flame retardant 3g / L, micronano ox...

Embodiment 3

[0040] The fabric of this embodiment is prepared by the following preparation process:

[0041] After blending 4 parts of polyester fiber, 4 parts of bamboo fiber, 3 parts of cupro ammonia fiber, 2 parts of polylactic acid fiber and 1 part of seaweed fiber, melt granulation, and then weave gray cloth by spinning space change yarn;

[0042] B, putting the gray cloth into the finishing solution for padding, then drying and cooling to obtain the finished fabric; the finishing solution includes the following ingredients: 18g / L titanium dioxide, 30g / L acrylate adhesive, and 3g / L glycerin , Gemini cationic softener 30g / L, flame retardant 3g / L, micronano oxide 7g / L, alkyl polyoxyethylene ether succinate sulfonate 1g / L, tribenzylphenol polyoxyethylene ether 1g / L, sodium cetyl sulfate 15g / L, sodium alkyl diphenyl ether disulfonate 5g / L, sodium dodecyl carboxylate 10g / L, ammonium salt 5-g / L, sodium hypophosphite 5g / L L, polyglycerol fatty acid ester 5g / L, succinic acid 4g / L, natural a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention provides high polymer fabric made of a high polymer material. The fabric is prepared through following preparation processes: A, polyester fibers, bamboo fibers and cuprammonium fibers are subjected to melting granulation, then air-jet texturing filaments are spun and woven, and grey fabric is obtained; B, the grey fabric is put in a finishing liquid for dipping, dried and cooled, and finished fabric product is obtained, wherein the finishing liquidis prepared fromcomponents as follows: 12-20 g / L of titanium dioxide, 18-32 g / L of an acrylate binder, 1-3 g / L of glycerin, 3-4 g / L of a flame retardant, 1-2 g / L of alkyl polyoxyethylene ether succinatesulfonate, 1-2.5 g / L of tribenzylpolyoxyethylenephenol ether, 8-15 g / L of cetyl sodium sulfate and 1.5-3 g / L of an antibacterial agent,the natural antibacterial agent is a plant extract prepared from cudweed,floschrysanthemi, folium artemisiaeargyi, fructusforsythiae andherbahouttuyniae in a mass ratio being (1-2):(1-3):(1-3):(1-2):(1-1.5) through mixed extraction, and density of the plant extract is 1-1.5 g / ml. The pure-natural and non-toxic antibacterial extract is utilized to perform antibacterialtreatment on the fabric, so that the antibacterial effect is realized, the ecological problem in the prior art is solved very well, and energy-saving and environment-friendly effects are realized.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a fabric made of polymer materials. Background technique [0002] At present, whether it is a sunshade cloth or a curtain, it is not often cleaned by consumers, especially outdoor fabrics used outdoors need to withstand the test of external weather environments such as wind, rain, and sun. It will contain a variety of organic and inorganic pollutants, which not only affect the appearance of the fabric, but also the accumulated dirt will cause the growth and reproduction of microorganisms on the surface of the fabric. Contents of the invention [0003] In order to solve the problems in the prior art, the present invention proposes a fabric made of polymer materials, which not only has the effect of shading and heat resistance, but also has a strong antibacterial effect. [0004] It is achieved through the following technical solutions: a fabric made of polymer mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/46D06M11/70D06M13/00D06M13/148D06M13/188D06M13/192D06M13/256D06M13/262D06M13/46D06M15/00D06M15/263D06M15/53D06M101/04D06M101/32
CPCD06M11/46D06M11/70D06M13/00D06M13/148D06M13/188D06M13/192D06M13/256D06M13/262D06M13/46D06M15/00D06M15/263D06M15/53D06M16/00D06M2101/04D06M2101/32D06M2200/25D06M2200/35D06M2200/50
Inventor 陈晓娟
Owner QINGDAO CHENYUN E COMMERCE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com