Composite emulsified asphalt and preparation technology thereof

A technology of composite emulsification and preparation technology, which is applied in the field of composite emulsified asphalt and its preparation technology, can solve problems such as poor high temperature resistance, high temperature deformation of asphalt roads, and insufficient interlayer cohesion, so as to meet application requirements and high temperature resistance Good performance and excellent overall performance

Inactive Publication Date: 2017-05-17
SUZHOU AIBOMAIER NEW MATERIAL CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the initial strength of the existing emulsified asphalt is low, which cannot meet the application requirements of important projects such as heavy-duty traffic roads and expressways.
In addition, the softening point of emulsified asphalt is usually 46-55°C, the high temperature resistance is not good, and the bonding strength is low. Especially in areas with high temperature weather and large vehicle load, it is easy to cause high temperature deformation of asphalt roads and interlayer adhesion. Insufficient and other defects greatly reduce the performance and service life of emulsified asphalt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite emulsified asphalt and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of composite emulsified asphalt, by weight, is made up of following components: 45 parts of base pitch, 10 parts of petroleum coke, 2 parts of polybutene, 3 parts of EVA, 2 parts of pentaerythritol, 4 parts of 8-hydroxyquinoline 3 parts of monolauryl phosphate, 1 part of vinyl tertiary carbonate, 3 parts of propylene glycol block polyether, 6 parts of Swire oil, 2 parts of oleamide, 0.8 part of ethylene oxide diamine, 0.5 part of aminated lignin , 1 part of bentonite, 0.6 parts of phosphate betaine, 14 parts of water, 3 parts of sodium dodecylbenzenesulfonate, 2 parts of ammonium humate, 1.6 parts of hydrochloric acid, 2.2 parts of ammonium chloride, 1.5 parts of β-butyrolactone , 1.8 parts of vinyl bis stearamide.

[0023] The base asphalt is petroleum asphalt, and its penetration is 50-80 1 / 10mm.

[0024] The preparation technology of above-mentioned composite emulsified asphalt comprises the steps:

[0025] 1) Weigh according to the above parts by weight;

...

Embodiment 2

[0032] A composite emulsified asphalt, by weight, is composed of the following components: 58 parts of base asphalt, 18 parts of petroleum coke, 9 parts of polybutene, 7 parts of EVA, 6 parts of pentaerythritol, 4 parts of 8-hydroxyquinoline -8 parts, 9 parts of monolauryl phosphate, 5 parts of vinyl tertiary carbonate, 8 parts of propylene glycol block polyether, 10 parts of Swire oil, 9 parts of oleamide, 1.5 parts of ethylene oxide diamine, aminated lignin 2.4 parts, 3 parts of bentonite, 1.8 parts of phospholipid betaine, 20 parts of water, 6 parts of sodium dodecylbenzenesulfonate, 8 parts of ammonium humate, 3 parts of hydrochloric acid, 5 parts of ammonium chloride, β-butyrolactone 4 parts, 3 parts of vinyl bis stearamide.

[0033] The base asphalt is oxidized asphalt, and its penetration is 50-80 1 / 10mm.

[0034] The preparation technology of above-mentioned composite emulsified asphalt comprises the steps:

[0035] 1) Weigh according to the above parts by weight;

...

Embodiment 3

[0042]A kind of composite emulsified asphalt, by weight, is made up of following components: 48 parts of base pitch, 12 parts of petroleum coke, 2.5 parts of polybutene, 3.5 parts of EVA, 2.7 parts of pentaerythritol, 8-hydroxyquinone 4.6 parts of morphine, 3.5 parts of monolauryl phosphate, 1.2 parts of vinyl tertiary carbonate, 3.3 parts of propylene glycol block polyether, 6.4 parts of Swire oil, 2.6 parts of oleamide, 0.9 parts of ethylene oxide diamine, aminated lignin 0.7 parts, 1.6 parts of bentonite, 0.8 parts of phospholipid betaine, 16 parts of water, 3.5 parts of sodium dodecylbenzenesulfonate, 2.6 parts of ammonium humate, 1.8 parts of hydrochloric acid, 2.6 parts of ammonium chloride, β-butyrolactone 1.6 parts, 2 parts of vinyl bis stearamide.

[0043] The base asphalt is petroleum asphalt and deoiled asphalt with a weight ratio of 4:1, and its penetration is 50-80 1 / 10mm.

[0044] The preparation technology of above-mentioned composite emulsified asphalt compris...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
softening pointaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides composite emulsified asphalt and a preparation technology thereof. The composite emulsified asphalt is prepared from the following components: matrix asphalt, petroleum tar, polybutylene, EVA (ethylene-vinyl acetate), pentaerythritol, 8-hydroxyquinoline, lauryl alcohol phosphate acid ester, vinyl versatate, propylene glycol block polyether, Turkey red oil, oleamide, epoxy ethanediamine ethylene diamine, aminated lignin, bentonite, phosphonolipid betaine, water, sodium dodecyl benzene sulfonate, ammonuim humate, hydrochloric acid, ammonium chloride, beta-butyrolactone and ethylene bis stearamide. The prepared composite emulsified asphalt has the advantages that the shear strength is 1.12 to 1.23MPa at the temperature of 25 DEG C, and is 0.59 to 0.74MPa at the temperature of 60 DEG C, the adhering strength is good, and the high temperature-resistant property is better; the softening point is higher than 63 DEG C, the needle penetration is 68 / 0.1mm at the temperature of 25 DEG C, the comprehensive property is excellent, and the application requirement of road construction projects can be met.

Description

technical field [0001] The invention belongs to the technical field of asphalt, and in particular relates to a composite emulsified asphalt and a preparation process thereof. Background technique [0002] Emulsified asphalt is widely used in road construction projects, such as micro-surfacing for road maintenance and repair, slurry seal layer, adhesive layer between pavement layers, and waterproof layer for road and bridge surfaces. Emulsified asphalt is formed by mechanically processing and dispersing asphalt, water and emulsifier into asphalt particles suspended in water. With the rapid development of social infrastructure, the requirements for emulsified asphalt are getting higher and higher. However, the existing emulsified asphalt has low initial strength and cannot meet the application requirements of important projects such as heavy-duty traffic roads and expressways. In addition, the softening point of emulsified asphalt is usually 46-55°C, the high temperature res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L23/08C08L97/00C08L23/20C08K13/02C08K3/34C08K5/3437C08K5/42C08K5/20
CPCC08L95/00C08L2201/08C08L2205/035C08L23/0853C08L97/005C08L23/20C08K13/02C08K3/346C08K5/3437C08K5/42C08K5/20
Inventor 李子寅
Owner SUZHOU AIBOMAIER NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com