Metallic luster glaze and preparation method thereof

A technology of metallic luster and formulation, applied in the field of metallic luster glaze and its preparation, can solve the problems of unstable firing effect of firing process, and achieve the effect of strong layering, uniform distribution and moderate size

Inactive Publication Date: 2017-04-26
钦州市高新技术产业服务中心
View PDF1 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because this kind of glaze has relatively high requirements on formula composition and firing process, and the firing effect is unstable, so this kind of glaze is only suitable for ceramic tiles and artworks at present, and has not been applied in sanitary ceramics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A metallic luster glaze is composed of the following formula components in parts by mass: 10-20 parts of albite, 8-10 parts of boron frit, 10-12 parts of perlite, 15-17 parts of burnt kaolin, 40-50 parts of pottery clay, 16-18 parts of vermiculite, 15-25 parts of sandy loam, 5-7 parts of zinc oxide, 6-8 parts of cristobalite, 10-20 parts of burnt talc, 6-7 parts of alumina, 14-18 parts of gypsum powder, catalyst 1-2 servings.

Embodiment 2

[0020] A metallic luster glaze is composed of the following formula components in parts by mass: 10 parts of albite, 8 parts of boron frit, 10 parts of perlite, 15 parts of burnt kaolin, 40 parts of pottery clay, 16 parts of vermiculite, 15 parts of sandy loam, 5 parts of zinc oxide, 6 parts of cristobalite, 10 parts of calcined talc, 6 parts of alumina, 14 parts of gypsum powder, and 1 part of catalyst.

Embodiment 3

[0022] A metallic luster glaze is composed of the following formula components in parts by mass: 15 parts of albite, 9 parts of boron frit, 11 parts of perlite, 16 parts of burnt kaolin, 45 parts of pottery clay, 17 parts of vermiculite, 120 parts of sandy loam, 6 parts of zinc oxide, 7 parts of cristobalite, 15 parts of calcined talc, 6.5 parts of alumina, 16 parts of gypsum powder, and 1.5 parts of catalyst.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses metallic luster glaze and a preparation method thereof. The metallic luster glaze consists of the following components in parts by mass: 10 to 20 parts of albite, 8 to 10 parts of boron frit, 10 to 12 parts of perlite, 15 to 17 parts of calcined kaolin, 40 to 50 parts of argil, 16 to 18 parts of vermiculite, 15 to 25 parts of sandy loam soil, 5 to 7 parts of zinc oxide, 6 to 8 parts of cristobalite, 10 to 20 parts of calcined talc, 6 to 7 parts of aluminium oxide, 14 to 18 parts of gypsum powder and 1 to 2 parts of a catalyst. According to the metallic luster glaze and the preparation method thereof, the chemical composition of the formula is optimized, a plurality of superfine ferric oxide crystallization grains are separated out of the glaze when the glaze is condensed at the high-temperature sintering later period, and a plurality of isolated single lamelliform crystal flowers which glitter like small gold foils are formed, so that the Venus-like metallic glaze effect is played.

Description

technical field [0001] The invention relates to the technical field of ceramic production, in particular to a metallic luster glaze and a preparation method thereof. Background technique [0002] At present, with the improvement of people's living taste, higher decorative requirements have been placed on the glazed surface of sanitary ceramics, which not only have use value but also have ornamental value. Due to the elegant and resplendent artistic effect of metal decorative materials, glazed surfaces with metallic luster are becoming more and more popular. Venus glaze is a special type of microcrystalline glaze. Its mechanism is that when the crystallization agent condenses in the late stage of high-temperature firing, many fine iron oxide crystal grains are precipitated to form gold sand. These extremely fine gold grain crystals are not floating on the glaze. above the surface, but buried beneath the surface of the glaze, suspended in a transparent glass matrix. Through ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B41/86
CPCC03C8/14C04B41/5022C04B41/86
Inventor 戚炎月丘泰西
Owner 钦州市高新技术产业服务中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com