Antirust anti-oxidation water-borne impervious sealant for container and preparation method of sealant

A container and anti-oxidation technology, applied in the field of sealants, can solve the problems of impermeability, low elasticity of water resistance, restricting the scope of use and service life, etc., to improve water resistance and impermeability, high waterproof and impermeability, and long service life. Effect

Inactive Publication Date: 2017-03-29
天长市永泰密封材料有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned sealant products still have the problems of impermeability, water resistance and low elasticity, which restrict their application range and service life in practical applications, and need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] An anti-rust, anti-oxidation, water-based and impermeable container sealant is prepared from the following components and raw materials in weight (kg):

[0015] 40% solids polyacrylate emulsion 40, 40% solids neoprene latex 5, 40% solids EP-44 waterborne epoxy resin emulsion 3, rosin 3, liquid paraffin 2, titanate Joint agent 3, barite powder 40, tributyl citrate 3, potassium sorbate 0.5, phytate 0.5, glycerol citrate 0.5, water 10.

[0016] A preparation method of a rust-proof, oxidation-proof, water-based and impermeable container sealant, comprising the following steps:

[0017] (1) Mix the polyacrylate emulsion, chloroprene latex and water-based epoxy emulsion evenly and stir at 1000 / min for 0.5h to obtain component A;

[0018] (2) First mix rosin, liquid paraffin and tributyl citrate, stir at 80°C for 0.5h, then add titanate coupling agent and stir at 100°C for 10min, after cooling, add glycerol citrate and water at 50°C , 1200r / min stirring for 0.5h, then adding...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antirust anti-oxidation water-borne impervious sealant for a container. The sealant is made from the following raw materials, by weight part, 40-60 of a polyacrylate emulsion with the solid content being 40-50%, 5-10 of polychloroprene latex with the solid content being 40-50%, 3-5 of EP-44 water-borne epoxy resin emulsion with the solid content being 40-50%, 3-5 of rosin, 2-4 of liquid paraffin, 3-5 of a titanate coupling agent, 40-60 of barite powder, 3-5 of tributyl citrate, 0.5-1 of potassium sorbate, 0.5-1 of inositol hexaphosphate, 0.5-1 of glyceride citrate, and 10-15 of water. The sealant for a container is high in elasticity, good in water resistance and impermeability and excellent in sealing performance. The sealant has antirust and anti-oxidation effect, is good in durability and long in service life, and is green and eco-friendly.

Description

technical field [0001] The invention relates to the technical field of sealants, in particular to an anti-rust, anti-oxidation, water-based and impermeable container sealant and a preparation method thereof. Background technique [0002] Sealant is a sealing material that guides the deformation with the shape of the sealing surface, is not easy to flow, and has a certain adhesiveness. It is an adhesive used to fill the configuration gap to play a sealing role. play an important role. In recent years, with the rapid development of the container transportation industry, sealant, as the main auxiliary material in the container manufacturing process, has also received more attention on its performance. Traditionally, solvent-based butyl rubber or neoprene sealants are used for container sealing. These types of sealants have heavy odor and large VOC emissions, which may cause environmental pollution and even harm to the human body, failing to meet environmental protection requir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/04C09J111/02C09J163/00C09J193/04C09J191/06C09J11/04C09J11/06
CPCC08L2201/08C08L2205/035C09J11/04C09J11/06C09J133/04C08L11/02C08L63/00C08L93/04C08L91/06C08K13/06C08K9/08C08K9/04C08K2003/3045C08K5/11C08K5/098C08K5/521C08K5/103
Inventor 刘晓朋
Owner 天长市永泰密封材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products