Preparation method and applications of graphene/Fe3O4 magnetic nanometer composite material

A technology of ferroferric oxide and magnetic nanometers, which is applied in chemical instruments and methods, oxidized water/sewage treatment, physical/chemical process catalysts, etc., can solve the problems of high carcinogenicity and disturbing ecosystems, and achieve short reaction time and distribution The effect of uniformity and easy large-scale industrial production

Inactive Publication Date: 2017-03-08
江苏金茂源生物化工有限责任公司
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Printing and dyeing wastewater enters the water, seriously disturbing the ecosystem, and some of its compounds are highly carcinogenic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and applications of graphene/Fe3O4 magnetic nanometer composite material
  • Preparation method and applications of graphene/Fe3O4 magnetic nanometer composite material
  • Preparation method and applications of graphene/Fe3O4 magnetic nanometer composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The preparation method of described graphene / ferroferromagnetic nanocomposite material, comprises the following steps:

[0031] (1) Graphene oxide is prepared by ultrasonic method:

[0032] a. According to the mass ratio of 1:300, the graphene oxide dispersion with a solid content of 2% is added to distilled water and stirred, then ultrasonicated with an ultrasonic cell pulverizer for 1 min and then centrifuged, and the upper graphene oxide solution is taken for subsequent use;

[0033] (2) Preparation of graphene / ferromagnetic nanocomposite material:

[0034] b. FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 O was mixed according to the molar ratio of 1:1, then added deionized water, and stirred until fully dissolved, in which FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 The mass ratio of O total mass to deionized water is 1:8;

[0035] c. Under the protection of nitrogen, the FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 The aqueous solution of O was added to the graphene oxide solution stirred a...

Embodiment 2

[0040] The preparation method of described graphene / ferroferromagnetic nanocomposite material, comprises the following steps:

[0041] (1) Graphene oxide is prepared by ultrasonic method:

[0042] a. According to the mass ratio of 10:145, the graphene oxide dispersion liquid with a solid content of 3% is added to distilled water and stirred, then centrifuged after ultrasonic 5min with an ultrasonic cell pulverizer, and the upper graphene oxide solution is taken for subsequent use;

[0043] (2) Preparation of graphene / ferromagnetic nanocomposite material:

[0044] b. FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 O was mixed according to the molar ratio of 2:1, then added deionized water, stirred until fully dissolved, in which FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 The mass ratio of O total mass to deionized water is 6:20;

[0045] c. Under the protection of nitrogen, the FeCl 3 ·6H 2 O and FeSO 4 ·7H 2The aqueous solution of O was added to the graphene oxide solution stirred at a cons...

Embodiment 3

[0050] The preparation method of described graphene / ferroferromagnetic nanocomposite material, comprises the following steps:

[0051] (1) Graphene oxide is prepared by ultrasonic method:

[0052] a. According to the mass ratio of 5:200, the graphene oxide dispersion liquid with a solid content of 2.3% is added to distilled water and stirred, then centrifuged after ultrasonic 3min with an ultrasonic cell pulverizer, and the upper graphene oxide solution is taken for subsequent use;

[0053] (2) Preparation of graphene / ferromagnetic nanocomposite material:

[0054] b. FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 O was mixed according to the molar ratio of 1.5:1, then added deionized water, and stirred until fully dissolved, wherein FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 The mass ratio of O total mass to deionized water is 3:10;

[0055] c. Under the protection of nitrogen, the FeCl 3 ·6H 2 O and FeSO 4 ·7H 2 The aqueous solution of O was added to the graphene oxide solution stirred at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method and applications of a graphene / Fe3O4 magnetic nanometer composite material, and belongs to the technical field of magnetic nanometer composite materials. A purpose of the present invention is to solve the problems of low efficiency and difficult recovery of the existing catalyst. The preparation method comprises: a, adding a graphene oxide dispersion liquid to distilled water, stirring, carrying out ultrasonic treatment, centrifugating, and taking the upper layer graphene oxide solution so as to be spare; b, mixing FeCl3.6H2O and FeSO4.7H2O, adding deionized water, and dissolving; c, adding the obtained solution to the graphene oxide solution, and uniformly stirring to obtain a mixing solution; d, adding ammonia water to the mixing solution in a dropwise manner, and crystallizing to obtain a composite material dispersion liquid; and e, carrying out ultrasonic treatment on the dispersion liquid, carrying out suction filtration to separate a graphene / Fe3O4 magnetic nanometer composite material, washing, and drying to obtain the graphene / Fe3O4 magnetic nanometer composite material. The method of the present invention can be used for preparing the graphene / Fe3O4 magnetic nanometer composite material.

Description

technical field [0001] The invention relates to a magnetic graphene composite material, in particular to a preparation method and application of a graphene / ferroferric oxide magnetic nanocomposite material, and belongs to the technical field of magnetic nanocomposite materials. Background technique [0002] Graphene (Graphene, GP) is a carbon atom with sp 2 The planar film of the hexagonal honeycomb lattice composed of hybrid orbitals, a new two-dimensional carbon nanomaterial with a thickness of only one carbon atom, has always been considered a hypothetical structure that cannot exist alone. In 2004, a physicist at the University of Manchester in the United Kingdom Andre Geim successfully separated graphene from graphite in experiments, confirming that it can exist alone, creating a new era of research and application of graphene materials. Due to its excellent characteristics such as extremely low resistivity and extremely fast electron migration speed, graphene has a ve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/745C02F1/72
CPCC02F1/722B01J23/745C02F2103/325C02F2101/308B01J35/33Y02W10/37
Inventor 张超瞿玮陈浩李腾李芳
Owner 江苏金茂源生物化工有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products