A photocatalyst air cleaning agent and a preparing method thereof

An air purifier, photocatalyst technology, applied in chemical instruments and methods, botanical equipment and methods, physical/chemical process catalysts, etc., to achieve the effect of enhancing film formation

Inactive Publication Date: 2017-02-08
广州光纳环保科技有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because chitosan can only be dissolved in some dilute inorganic acids or organic acids, it cannot be directly dissolved in water, which limits its application to a large extent. Therefore, chitosan can be modified to be water-soluble by modification. Chitosan, but still retains its superior properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A photocatalyst air cleaning agent and a preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A photocatalyst air purifier, the purifier is composed of the following components in percentage by weight: nano titanium dioxide 1%, triethylhexyl phosphoric acid 0.6%, emulsified silicone oil 0.4%, carboxymethyl chitosan 2%, deionized water 96%; the particle size of the nano titanium dioxide is 10 nm.

[0024] The specific steps of the preparation process are as follows:

[0025] (1) Add water-soluble chitosan into deionized water according to the formula, and stir at room temperature until it dissolves;

[0026] (2) Add nano-titanium dioxide to the solution generated in step (1) according to the formula, and stir evenly at room temperature to form an emulsion. The stirring speed is 1500 rpm and the stirring time is 30 minutes;

[0027] (3) Add the dispersant according to the formula to the emulsion produced in step (2), stir evenly at room temperature, the stirring speed is 1500 rpm, and the stirring time is 20 minutes;

[0028] (4) Add defoamer according to the formula in th...

Embodiment 2

[0030] A photocatalyst air purifier, which is composed of the following components by weight percentage: nano titanium dioxide 5%, sodium lauryl sulfate 1%, higher alcohol fatty acid ester compound 0.7%, quaternary ammonium salt shell polymer Sugar is 5%, deionized water is 88.3%; the particle size of the nano-titanium dioxide is 10 nm.

[0031] The specific steps of the preparation process are as follows:

[0032] (1) Add water-soluble chitosan into deionized water according to the formula, and stir at room temperature until it dissolves;

[0033] (2) Add nano-titanium dioxide to the solution generated in step (1) according to the formula amount, and stir evenly at room temperature to form an emulsion. The stirring speed is 1300 rpm and the stirring time is 45 minutes;

[0034] (3) Add the dispersant according to the formula to the emulsion generated in step (2), stir evenly at room temperature, the stirring speed is 1300 rpm, and the stirring time is 30 minutes;

[0035] (4) Add defo...

Embodiment 3

[0037] A photocatalyst air purifier, the purifier is composed of the following components in percentage by weight: nano titanium dioxide 3%, methyl pentanol 1%, polyoxyethylene polyoxypropylene pentaerythritol ether 0.5%, carboxymethyl chitosan 2 %, 93.5% of deionized water; the particle size of the nano titanium dioxide is 30 nm.

[0038] The specific steps of the preparation process are as follows:

[0039] (1) Add water-soluble chitosan into deionized water according to the formula, and stir at room temperature until it dissolves;

[0040] (2) Add nano-titanium dioxide to the solution generated in step (1) according to the formula, and stir evenly at room temperature to form an emulsion. The stirring speed is 1000 rpm and the stirring time is 60 minutes;

[0041] (3) Add the dispersant according to the formula to the emulsion generated in step (2), stir evenly at room temperature, the stirring speed is 1000 rpm, and the stirring time is 40 minutes;

[0042] (4) Add defoamer accordin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of environment friendly material air cleaning, and particularly discloses a photocatalyst air cleaning agent and a preparing method thereof. The photocatalyst air cleaning agent comprises, by weight, 1-5% of nanometer titanium dioxide, 0.6-1% of a dispersant, 0.3-0.7% of a defoamer, 2-5% of water-soluble chitosan and 88-96% of deionized water. The product can decompose and react under visible light, can effectively prevent harms caused by formaldehyde release after decoration to human body health, and has double sterilizing and antibacterial functions.

Description

Technical field [0001] The invention relates to the technical field of environmental protection material air purification, in particular to a photocatalyst air purification agent and a preparation method thereof. Background technique [0002] With the continuous improvement of people's health awareness, people have higher and higher requirements for the living environment, especially the living environment and the car interior environment. After the decoration of the living environment or the purchase of new furniture, it is easy to emit harmful gases such as formaldehyde, benzene, amines, TVOC, etc., which directly endanger people's health. Therefore, the management of the internal environment after the house decoration is very important. [0003] Photocatalyst is a nano-scale metal oxide material (titanium dioxide is more commonly used). It is coated on the surface of the substrate and dried to form a thin film. Under the action of visible light, it produces a strong catalytic d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J31/38A01N59/16A01N43/16A01P1/00A01P3/00
CPCA01N43/16A01N59/16B01J31/06B01J31/38B01J35/39A01N2300/00
Inventor 刘博刘哲
Owner 广州光纳环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap