Preparation method of elastic polyester fiber and flax fiber blended yarns by adopting bio-enzyme method

A flax fiber and elastic polyester technology, applied in the field of elastic polyester fiber and flax fiber blended yarn, can solve the problems of restricting development, rough feel of flax fiber, easy deformation, etc., and achieve the effect of improving style, improving hand feeling and good elasticity

Inactive Publication Date: 2017-01-11
JIANGSU HUAXIN LINEN TEXTILE
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, some defects of hemp also restrict its development. The flax fiber feels rough and hard, and it is easy to deform in a wet state.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: a preparation method of elastic polyester fiber and flax fiber blended yarn, the weight content of the flax fiber is 45-75%, and the rest is elastic polyester fiber, and the preparation includes the following steps:

[0033] Step 1. Pretreatment: Loosely stack flax fibers and elastic polyester fibers, mix them with water, and spray them evenly on the flax fibers, and use pretreatment agents to evenly spray them on the elastic polyester fibers, respectively. sealed stack;

[0034] Step 2, cleaning: disperse the pretreated flax fibers and elastic polyester fibers respectively and mix them together evenly, and remove the impurities attached to the flax fibers and elastic polyester fibers themselves;

[0035] Step 3, Carding: Combing the mixed flax fiber and elastic polyester fiber into a cotton web to remove impurities and short fibers;

[0036] Step 4, drawing frame: using three processes to evenly mix multiple cotton webs to form lines with uniform diamete...

Embodiment 2

[0044] Embodiment 2: a preparation method of elastic polyester fiber and flax fiber blended yarn, the weight content of the flax fiber is 55%, and the rest is elastic polyester fiber, and the preparation includes the following steps:

[0045] Step 1. Pretreatment: Loosely stack flax fibers and elastic polyester fibers, mix them with water, and spray them evenly on the flax fibers, and use pretreatment agents to evenly spray them on the elastic polyester fibers, respectively. sealed stack;

[0046] Step 2, cleaning: disperse the pretreated flax fibers and elastic polyester fibers respectively and mix them together evenly, and remove the impurities attached to the flax fibers and elastic polyester fibers themselves;

[0047] Step 3, Carding: Combing the mixed flax fiber and elastic polyester fiber into a cotton web to remove impurities and short fibers;

[0048] Step 4, drawing frame: using three processes to evenly mix a plurality of cotton webs to form lines with uniform diam...

Embodiment 3

[0056] Embodiment 3: a preparation method of elastic polyester fiber and flax fiber blended yarn, the weight content of the flax fiber is 45-75%, and the rest is elastic polyester fiber, and the preparation includes the following steps:

[0057] Step 1. Pretreatment: Loosely stack flax fibers and elastic polyester fibers, mix them with water, and spray them evenly on the flax fibers, and use pretreatment agents to evenly spray them on the elastic polyester fibers, respectively. sealed stack;

[0058] Step 2, cleaning: disperse the pretreated flax fibers and elastic polyester fibers respectively and mix them together evenly, and remove the impurities attached to the flax fibers and elastic polyester fibers themselves;

[0059] Step 3, Carding: Combing the mixed flax fiber and elastic polyester fiber into a cotton web to remove impurities and short fibers;

[0060] Step 4, drawing frame: using three processes to evenly mix a plurality of cotton webs to form lines with uniform d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of elastic polyester fiber and flax fiber blended yarns by adopting a bio-enzyme method. The weight content of flax fibers is 45 percent to 75 percent and the balance is elastic polyester fibers; the preparation method comprises: pre-treating, blowing, cotton carding, drawing, roving, degumming, bleaching, acid washing, washing and spinning. By adopting the preparation method provided by the invention, the elastic polyester fiber and flax fiber blended yarns with moisture absorption, lightness and thinness, glossiness, air permeability, antibacterial property and mite inhibition property can be prepared. The elastic polyester fiber and flax fiber blended yarns provided by the invention have high spinnability and good elasticity; cloth woven by the elastic polyester fiber and flax fiber blended yarns is light and soft, comfortable and breathable, has sweat-absorbing and antibacterial properties and has elasticity; the cloth has novel and fashionable appearance. The elastic polyester fibers and the flax fibers are blended and the disadvantage of low elasticity of the flax fibers can be made up; a prepared fabric has a comfortable hand feeling and has good elasticity; the style of the blended yarns can be improved and the hand feeling of the blended yarns can be improved.

Description

technical field [0001] The invention relates to the field of textiles, in particular to an elastic polyester fiber and flax fiber blended yarn. Background technique [0002] The main components of hemp are cellulose, lignin, hemicellulose, pectin, etc. The biggest difference between hemp products and other natural cellulose textiles is that they need to be degummed. The degumming process has a great impact on the quality of hemp, and it is also one of the topics that the hemp industry has been working on in recent years. The traditional degumming process is mainly chemical degumming, that is, using chemical reagents that can dissolve pectin to scour the hemp fiber for a long time to remove the gum. The disposal of large volumes of degumming wastewater places great pressure on the environment and costs. Taking Hubei as an example, Hubei Province has an annual output of more than 4,000 tons of refined and dried flax. There are 5 degumming production enterprises, and only 2 h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/32D01C1/04D06M11/71D06M11/13D06M11/76D06L4/15D06L4/12D06M101/06D06M101/32
CPCD02G3/04D01C1/04D02G3/328D06M11/13D06M11/71D06M11/76D06M2101/06D06M2101/32D10B2201/04D10B2331/04
Inventor 王雅琴薛茂深
Owner JIANGSU HUAXIN LINEN TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com