Production method of vase

A production method and vase technology, applied in clay products, household utensils, applications, etc., can solve the problems of focusing on quality, deterioration, difficulty, etc., and achieve the effect of saving materials, simple process, and high coloring rate

Inactive Publication Date: 2017-01-04
TONGCHENG FURUN PACKAGING MATERIAL
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now it is also used to refer to women who are beautiful but have no connotation and ability. It is made on a biscuit-fired blank, by taking pictures (making a draft with holes infiltrated with color), manually constructing lines, mixing water, and passing through 1350 degrees. Firing at high temperature is very difficult. The key is that the blue and white material cannot see any change in shade before firing. It is comp...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) The production of the bottom of the bottle: take 5kg of clay, 2kg of quartz sand, 10kg of methyl methacrylate, 10kg of methacrylic acid, 2kg of sodium nitrilotriacetic acid, 6kg of shell powder, 1kg of pigment and 10kg of Portland cement; The materials were uniformly mixed and pulverized, and water was added, and the mass ratio of water and the mixture was 1:1.5; the water-added mixture obtained in the upper part was put into the mold at the bottom of the bottle, and stood still for 5 hours.

[0021] (2) Production of the bottle body:

[0022] a, preparation of mixed slurry: get the mixed solution of dispersant, deionized water and dehydrated ethanol and nanopowder and put it into the homogeneous 30 minutes on the high-speed homogenizer, adopt ultrasonic wave to disperse 20 times then; Described dispersant, deionized The mass ratio of ionized water, absolute ethanol and nano powder is 5:30:20:55;

[0023] b. Made of green body: The porcelain clay is composed of the...

Embodiment 2

[0028] A kind of manufacture method of vase, its concrete steps are:

[0029] (1) The production of the bottom of the bottle: take 70kg of clay, 40kg of quartz sand, 12kg of methyl methacrylate, 12kg of methacrylic acid, 5kg of sodium nitrilotriacetic acid, 13kg of shell powder, 3kg of pigment and 15kg of Portland cement; The materials were uniformly mixed and pulverized, and water was added, and the mass ratio of water and the mixture was 1:1.5; the water-added mixture obtained in the upper part was put into the mold at the bottom of the bottle, and stood still for 6.5 hours.

[0030] (2) Production of the bottle body:

[0031] a, preparation of mixed slurry: get the mixed solution of dispersant, deionized water and dehydrated ethanol and nanopowder and put it into homogeneous 45 minutes on the high-speed homogenizer, adopt ultrasonic wave to disperse 25 times then; Described dispersant, deionized The mass ratio of ionized water, absolute ethanol and nano powder is 5:30:20:5...

Embodiment 3

[0037] A kind of manufacture method of vase, its concrete steps are:

[0038] (1) The production of the bottom of the bottle: take 100kg of clay, 60kg of quartz sand, 15kg of methyl methacrylate, 15kg of methacrylic acid, 8kg of sodium nitrilotriacetic acid, 20kg of shell powder, 5kg of pigment and 20kg of Portland cement; The materials were uniformly mixed and pulverized, and water was added, and the mass ratio of water and the mixture was 1:1.5; the water-added mixture obtained in the upper part was put into the mold at the bottom of the bottle, and stood still for 8 hours.

[0039] (2) Production of the bottle body:

[0040] a, preparation of mixed slurry: get the mixed solution of dispersant, deionized water and dehydrated ethanol and nanopowder and put it into a high-speed homogenizer and homogenize for 60 minutes, then adopt ultrasonic dispersion for 30 times; The mass ratio of ionized water, absolute ethanol and nano powder is 5:30:20:55;

[0041] b. Made of green bod...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a production method of a vase. The production method comprises the following steps of producing a vase bottom; producing a vase body; preparing mixed slurry; producing a green body; biscuiting at high temperature; performing colored drawing and color burning; airing; taking a mixed solution of a dispersing agent, deionized water and absolute ethyl alcohol and nano powder, putting the mixed solution and the nano powder into a high-speed homogenizer for homogenizing, and then performing ultrasonic dispersion, wherein the mass part ratio of the dispersing agent to the deionized water to the absolute ethyl alcohol to the nano powder is 5 to 30 to 20 to 55; forming the green body: petuntse is prepared from the following raw materials in percentage by weight: 5.3 percent of nano mixed slurry, silicon dioxide, aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, phosphorus pentoxide, zirconia, boric oxide and yttria, putting the petuntse on the formed vase bottom, and molding by using the petuntse. The vase bottom of the vase produced by using the mode is firm and cannot be easily broken up.

Description

technical field [0001] The invention relates to the field of household products, in particular to a method for making a vase. Background technique [0002] A vase is a kind of vessel, mostly made of ceramics or glass, with a beautiful and smooth appearance; the precious ones are made of expensive materials such as crystals to hold beautiful plants with flower branches. The bottom of the vase usually holds water to keep the plants alive and beautiful. Now it is also used to refer to women who are beautiful but have no connotation and ability. It is made on a biscuit-fired blank, by taking pictures (making a draft with holes infiltrated with color), manually constructing lines, mixing water, and passing through 1350 degrees. Firing at high temperature is very difficult. The key is that the blue and white material cannot see any change in shade before firing. It is completely controlled by the artist's feeling and experience. How to use the vase produced by the traditional vase...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/13C04B35/14C04B35/632C04B35/622C04B41/86
CPCC04B33/13C04B33/1305C04B33/131C04B35/14C04B35/622C04B35/632C04B35/6325C04B41/5022C04B41/86C04B2235/3201C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3225C04B2235/3232C04B2235/3244C04B2235/3272C04B2235/3286C04B2235/3293C04B2235/3294C04B2235/34C04B2235/3409C04B2235/3418C04B2235/422C04B2235/449
Inventor 杨峰
Owner TONGCHENG FURUN PACKAGING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap