Preparation process of aging-resistant elevator compensation cable

A technology for elevator compensation and preparation process, applied in textile cables, coatings, textiles and papermaking, etc., can solve problems such as iron chain corrosion, hidden dangers, rust and breakage, etc., and achieve the effect of good corrosion resistance.

Active Publication Date: 2019-08-06
XUANCHENG VALIN PRECISION TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The compensation chain (cable) is an elevator component that balances the weight of the traction wire rope. The load-bearing structure of the existing compensation chain (cable) is made of ordinary steel. In coastal areas, the iron chain is easily corroded by the air, and even rusted and broken. Rubber is easy to age, which brings safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The aging-resistant elevator compensation cable preparation process includes the following steps:

[0021] The first step: galvanizing aviation steel wire ropes or compensation chains, coating the surface of several aviation steel wire ropes or compensation chains with an ultra-thick zinc layer of 265-290g / m², and the preferred thickness of the zinc layer is 270, 276, 280, 285 g / m2 ;

[0022] The second step: winding, the aviation steel wire rope obtained in step 1 is wound into a steel wire rope core by a winding machine, and the wound steel wire rope core is placed in an anti-rust oil tank for 15-35 minutes to ensure that the cuts of several aviation steel wire ropes are covered with anti-rust Rust oil, the immersion time is 16, 18, 22, 25 and 30 minutes, and the anti-rust oil coated inside the cut of some aviation wire ropes is basically saturated;

[0023] The third step: put on the corrosion-resistant rubber sheath, and put the corrosion-resistant rubber sheath on...

Embodiment 2

[0028] The aging-resistant elevator compensation cable preparation process includes the following steps:

[0029] Step 1: Galvanize aviation steel wire ropes or compensation chains, and coat several aviation steel wire ropes or compensation chains with an ultra-thick zinc layer of 285g / m²;

[0030] The second step: winding, the aviation steel wire rope obtained in step 1 is wound into a steel wire rope core by a winding machine, and the steel wire rope core obtained by winding is soaked in an anti-rust oil tank for 30 minutes to ensure that the cuts of several aviation steel wire ropes are covered with anti-rust oil;

[0031] The third step: put on the corrosion-resistant rubber sheath, and put the corrosion-resistant rubber sheath on the steel wire rope core or the compensation chain jacket;

[0032] The fourth step is to coat the PP sheath, and use the plastic coating process to apply the PP material to the outside of the corrosion-resistant rubber sheath to form a 01.5mm PP...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing technology for an anti-ageing elevator compensation cable. The preparing technology comprises the following steps that firstly, a plurality of aviation steel wire ropes or compensation chains are plated with zinc, wherein the surfaces of the aviation steel wire ropes or compensation chains are plated with the super-thick zinc layers at 265-290 g / m<2>; secondly, winding is carried out, wherein the aviation steel wire ropes obtained in the first step are wound into a steel wire rope core through a winding machine, and the steel wire rope core is put into an anti-rusting oil trough to be soaked for 15-35 min; thirdly, a corrosion-resistant rubber sheath is arranged in a sleeving mode; fourthly, a PP protection layer is smeared, wherein a PP material is smeared to the outer part of the corrosion-resistant rubber sheath with the plastic coating technology, the PP protection layer with the thickness of 0.3-1.5 mm is formed, and supra polymer polyvinyl chloride with the weight percentage of 18-23% is added into the PP material in the plastic coating technology. The corrosion resistance and the anti-ageing property of the compensation cable prepared through the technology are improved, the stable performance of the product is maintained in the harsh environment with strong ultraviolet while various physical indexes in the conventional environment are ensured, the service life is prolonged, and the safety is improved.

Description

technical field [0001] The invention relates to the technical field of elevator compensation cables, in particular to the technical field of manufacturing technology of elevator compensation cables and the preparation process of aging-resistant elevator compensation cables. Background technique [0002] The compensation chain (cable) is an elevator component that balances the weight of the traction wire rope. The load-bearing structure of the existing compensation chain (cable) is made of ordinary steel. In coastal areas, the iron chain is easily corroded by the air, and even rusted and broken. Rubber is easy to age, which brings safety hazards. Therefore, our company has developed an anti-aging and anti-corrosion elevator compensation cable product. Contents of the invention [0003] In order to overcome the deficiencies in the prior art above, the present invention provides a preparation process for aging-resistant elevator compensation cables, the purpose of which is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D07B1/06D07B1/14
CPCD07B1/0606D07B1/144D07B2201/2011D07B2201/2087D07B2201/2088D07B2201/2089D07B2205/201D07B2205/2021D07B2205/2032D07B2205/3071D07B2205/502D07B2401/2025D07B2401/207D07B2801/18
Inventor 黄业华
Owner XUANCHENG VALIN PRECISION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com