Multifunctional filter core used for water producer
A water generator, multi-functional technology, applied in the direction of filtration separation, filtration treatment, water/sewage treatment, etc., to achieve good wear resistance and low density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0034] Comprising the following parts by weight:
[0035] UHMWPE: 50 copies
[0036] Cross-linking agent: 1.5 parts
[0037] Modified activated carbon: 300 parts
[0038] Antioxidant: 1.5 parts
[0039] Lubricant: 0.5 parts
[0040] Described modified activated carbon is made through the following steps:
[0041] Immerse coconut shell activated carbon in 1mol / L concentrated sulfuric acid solution and oxidize to obtain oxidized activated carbon, immerse oxidized activated carbon into 400mg / L silver ammonia solution and 0.5g / L diamino-bis(tert-butoxy)-silane Modification is carried out to obtain modified activated carbon.
[0042] After the above raw materials were fully mixed, they were added to the mold, and under the protection of nitrogen, the temperature was raised to 150°C at a heating rate of 5°C / min, kept for 10 minutes, and then cooled to room temperature at a cooling rate of 15°C / min to obtain a filter element.
[0043] The crosslinking agent is a mixture of tria...
Embodiment 2
[0050] Comprising the following parts by weight:
[0051] UHMWPE: 70 copies
[0052] Cross-linking agent: 3 parts
[0053] Modified activated carbon: 270 parts
[0054] Antioxidant: 1 part
[0055] Lubricant: 1 part
[0056] Described modified activated carbon is made through the following steps:
[0057]Immerse coconut shell activated carbon in 1mol / L concentrated sulfuric acid solution and oxidize to obtain oxidized activated carbon, immerse oxidized activated carbon into 400mg / L silver ammonia solution and 0.5g / L diamino-bis(tert-butoxy)-silane Modification is carried out to obtain modified activated carbon.
[0058] After the above raw materials were fully mixed, they were added to the mold, and under the protection of nitrogen, the temperature was raised to 150°C at a heating rate of 5°C / min, kept for 10 minutes, and then cooled to room temperature at a cooling rate of 15°C / min to obtain a filter element.
[0059] The crosslinking agent is a mixture of triallyl isoc...
Embodiment 3
[0066] Comprising the following parts by weight:
[0067] UHMWPE: 100 copies
[0068] Cross-linking agent: 0.5 parts
[0069] Modified activated carbon: 250 parts
[0070] Antioxidant: 2 parts
[0071] Lubricant: 2 parts
[0072] Described modified activated carbon is made through the following steps:
[0073] Immerse coconut shell activated carbon in 1mol / L concentrated sulfuric acid solution and oxidize to obtain oxidized activated carbon, immerse oxidized activated carbon into 400mg / L silver ammonia solution and 0.5g / L diamino-bis(tert-butoxy)-silane Modification is carried out to obtain modified activated carbon.
[0074] After the above raw materials were fully mixed, they were added to the mold, and under the protection of nitrogen, the temperature was raised to 150°C at a heating rate of 5°C / min, kept for 10 minutes, and then cooled to room temperature at a cooling rate of 15°C / min to obtain a filter element.
[0075] The crosslinking agent is a mixture of trially...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com