Inorganic hybrid polyester polyol etherified melamine resin and preparation method thereof

A technology of alcohol-etherified melamine resin and alcohol-etherified melamine, which can be used in polyester coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc. High temperature resistance and flame retardant performance, the effect of high flame retardant performance

Active Publication Date: 2016-12-21
CHANGZHOU JUMBO ENERGY SAVING TECH CO LTD
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when applied to highly flame-retardant polyurethane materials, there is still a certain gap in its high-temperature resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic hybrid polyester polyol etherified melamine resin and preparation method thereof
  • Inorganic hybrid polyester polyol etherified melamine resin and preparation method thereof
  • Inorganic hybrid polyester polyol etherified melamine resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Preparation of Borated Phthalic Anhydride Diethylene Glycol Etherified Melamine Resin

[0039] Molecular formula:

[0040]

[0041] (1) etherification reaction

[0042] Add hexamethylolmelamine and phthalic anhydride diethylene glycol into the reaction kettle, add acid to adjust the pH to 2.5, and carry out the etherification reaction at 35°C with a stirring speed of 60 rpm and keep warm for 120 minutes to obtain phthalic anhydride diethylene glycol Alcohol etherified melamine resin;

[0043] (2) Alkaline neutralization

[0044] Stir at a speed of 40 rpm, add alkali to adjust the pH to 8.0, and keep the temperature below 50°C during the alkali neutralization process;

[0045] (3) Hybridization reaction

[0046] Add sodium octaborate tetrahydrate and water into the reaction kettle, raise the temperature to 100°C and react for 2 hours, and the hybridization reaction is completed;

[0047] (4) cooling filter

[0048] Cool to 60°C, add 2% diatomaceous earth filter ...

Embodiment 2

[0050] Preparation of Melamine Resin Etherified with Antimony Hybrid Phthalic Anhydride and Glycerin

[0051] Molecular formula:

[0052]

[0053] (1) etherification reaction

[0054] Add hexamethylol melamine and phthalic anhydride glycerin into the reaction kettle, add acid to adjust the pH to 5.5, under the condition of 65°C, the stirring speed is 80 rpm, and keep warm for 30 minutes to carry out etherification reaction to obtain phthalic anhydride glycerin Etherified melamine resin;

[0055] (2) Alkaline neutralization

[0056] Stir at a speed of 80 rpm, add alkali to adjust the pH to 9.0, and keep the temperature below 50°C during the alkali neutralization process;

[0057] (3) Hybridization reaction

[0058] Add antimony trioxide and water into the reaction kettle, raise the temperature to 110°C and react for 0.5 hours, and the hybridization reaction is completed;

[0059] (4) cooling filter

[0060] Cool to 80°C, add 2.5% diatomite filter aid, filter out the sa...

Embodiment 3

[0062] Preparation of Borated Phthalic Anhydride Diethylene Glycol Etherified Melamine Resin

[0063] Molecular formula:

[0064]

[0065] (1) etherification reaction

[0066] Add hexamethylol melamine and phthalic anhydride diethylene glycol into the reaction kettle according to the above ratio, add acid to adjust the pH to 3.0, and under the condition of 45°C, the stirring speed is 650 rpm, and the etherification reaction is carried out for 70 minutes after heat preservation, to obtain Phthalic anhydride diethylene glycol etherified melamine resin;

[0067] (2) Alkaline neutralization

[0068] Stir at a speed of 50 rpm, add alkali to adjust the pH to 8.5, and keep the temperature below 50°C during the alkali neutralization process;

[0069] (3) Hybridization reaction

[0070] Add sodium octaborate tetrahydrate and water into the reaction kettle, raise the temperature to 100°C and react for 1 hour, and the hybridization reaction is completed;

[0071] (4) cooling filt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of inorganic hybrid polymers and especially relates to inorganic hybrid polyester polyol etherified melamine resin and a preparation method thereof. The preparation method mainly comprises the following steps: (1) etherification reaction: adding hexamethylolmelamine and polyester polyol into a reaction vessel to carry out a thermal reaction so as to obtain tetraetherified or pentaetherified melamine resin; (2) alkali neutralization; (3) hybridization reaction; (4) cooling and filtering to obain the finished product. Through the above method, the inorganic hybrid polyester polyol etherified melamine resin is prepared. By hybridization cross-linking reaction with an inorganic hybrid compound, high-temperature-resistant fire retardant elements such as boron, molybdenum, antimony, etc. are introduced into the finally produced amino resin polyol such that high temperature resistance and flame retardant property of amino resin polyol are enhanced. The product of the invention is mainly used in preparation of premixed polyols and paint coating.

Description

technical field [0001] The invention belongs to the technical field of inorganic hybrid polymer materials, and in particular relates to an inorganic hybrid polyester polyol etherified melamine resin and a preparation method thereof. Background technique [0002] Because amino resin has a certain temperature resistance, it is used in many fields, including coating industry, furniture industry, polyurethane industry and so on. However, when applied to highly flame-retardant polyurethane materials, there is still a certain gap in its high-temperature resistance. [0003] Due to the special molecular structure of polyurethane foam plastics, it is easy to burn and not resistant to high temperature. With the continuous popularization and application of polyurethane energy-saving thermal insulation rigid foam application technology, the requirements for its flame retardant performance are getting higher and higher, especially GB8624-2012 "Classification method for the combustion p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/91C08G18/46C09D175/06C09D175/08C09D167/08C09D163/00C09D133/00C09D161/20C09D5/18C08J3/24C08G101/00
CPCC08G18/46C08G18/4661C08G63/914C08G63/916C08G2101/00C08J3/24C08J2367/00C08J2367/02C09D5/18C09D133/00C09D161/20C09D163/00C09D167/08C09D175/06C09D175/08
Inventor 王洪波
Owner CHANGZHOU JUMBO ENERGY SAVING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com