Preparation method of pandermite ethyl oleate compound modified bentonite

A composite modification and ethyl oleate technology, which is applied in the field of modification of bentonite, can solve the problem that the adsorption capacity of pollutants needs to be improved, and achieve the effects of improving adsorption effect, great application prospect, good adsorption performance and regeneration.

Inactive Publication Date: 2016-12-14
GUANGXI PROVINCE NANNING CITY XUXI TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although bentonite has good pollutant adsorption performance, its adsorption capacity for pollutants needs to be improved under some special environmental conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A preparation method of white boron calcium petroleum ethyl ester composite modified bentonite, comprising the steps of:

[0015] (1) Ingredients: Take by weighing 160g of leucumite, 600g of ethyl oleate, and 900g of bentonite respectively;

[0016] (2) Mixing materials: mix bentonite and leucumite evenly, then add ethyl oleate and stir evenly;

[0017] (3) Reaction: Pour the mixed material into a high-temperature and high-pressure reactor, fill the reactor with inert gas and exhaust the air, adjust the pressure in the reactor to 3.2Mpa, and the temperature to 230°C, and place the reactor in an ultrasonic field. The frequency of the ultrasonic field is 32KHz, and the power density is 0.48w / cm 2 ;

[0018] (4) Drying: After reacting for 20mim, cool naturally to 75°C, pour the material out of the reaction kettle and spread it into an oven at 75°C, so that the unreacted ethyl oleate is volatilized, and then grind to a particle size smaller than 100 microns, that is.

...

Embodiment 2

[0024] A preparation method of white boron calcium petroleum ethyl ester composite modified bentonite, comprising the steps of:

[0025] (1) Batching: the ratio by weight is boronite: ethyl oleate: bentonite=5:25:40 and take each component for subsequent use;

[0026] (2) Mixing materials: mix bentonite and leucumite evenly, then add ethyl oleate and stir evenly;

[0027] (3) Reaction: Pour the mixed material into a high-temperature and high-pressure reactor, fill the reactor with inert gas to exhaust the air, adjust the pressure in the reactor to 3Mpa, and the temperature to 220°C, and place the reactor in an ultrasonic field. The frequency of the field is 30KHz and the power density is 0.45w / cm 2 ;

[0028] (4) Drying: After reacting for 15 min, cool naturally to 70°C, pour the material out of the reaction kettle and spread it into an oven at 70°C, so that the unreacted ethyl oleate is volatilized, and the product is obtained.

Embodiment 3

[0030] A preparation method of white boron calcium petroleum ethyl ester composite modified bentonite, comprising the steps of:

[0031] (1) Batching: the ratio by weight is boronite: ethyl oleate: bentonite=10:35:50 and take each component for subsequent use;

[0032] (2) Mixing materials: mix bentonite and leucumite evenly, then add ethyl oleate and stir evenly;

[0033] (3) Reaction: Pour the mixture into a high-temperature and high-pressure reactor, fill the reactor with inert gas and exhaust the air, adjust the pressure in the reactor to 3.5Mpa, and the temperature to 240°C, and place the reactor in an ultrasonic field. The frequency of the ultrasonic field is 35KHz, and the power density is 0.5w / cm 2 ;

[0034] (4) Drying: After reacting for 30mim, cool naturally to 80°C, pour the material out of the reaction kettle and spread it into an oven at 80°C, so that the unreacted ethyl oleate is volatilized, and the product is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Disclosed is a preparation method of pandermite ethyl oleate compound modified bentonite. The method comprises the following steps that pandermite, ethyl oleate and bentonite are weighed according to the ratio of parts by weight being (5-10):(25-35):(40-50) for use; the bentonite and the pandermite are mixed to be uniform, and the ethyl oleate is added and stirred to be uniform; the mixed material is poured into a high temperature and high pressure reaction kettle, inert gas is introduced into the reaction kettle, air is exhausted, and the reaction kettle is placed into an ultrasonic field; after the reaction is performed for 15-30 min, natural cooling is performed, the unreacted ethyl oleate is volatilized thoroughly, and then grinding is performed to obtain the pandermite ethyl oleate compound modified bentonite. The pandermite ethyl oleate compound modified bentonite obtained through the method has the specific adsorptivity, dispersibility and rheological property of clay mineral, has polyfuncitonal groups and reaction activity of organic compounds and improves the adsorption effect.

Description

technical field [0001] The invention relates to a modification method of bentonite, in particular to a preparation method of white boron calcium petroleum ethyl ester composite modified bentonite. Background technique [0002] With the rapid development of industry and agriculture, a large number of industrial chemicals are discharged into rivers, lakes, seas and other water bodies, causing serious pollution to the water body environment and increasingly endangering the health of the people. At present, the problem of water pollution control has become one of the important problems that our government urgently needs to solve. The existing common methods of sewage treatment include physical chemical method, chemical method and biochemical method, but these methods are complicated in process, high in cost and low in efficiency. Studies have shown that using adsorbent materials to adsorb pollutants in sewage is an efficient and convenient treatment method to solve water enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/12B01J20/30C02F1/28C02F101/20C02F101/30
CPCB01J20/12C02F1/281C02F2101/20C02F2101/30
Inventor 不公告发明人
Owner GUANGXI PROVINCE NANNING CITY XUXI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com