Environment-friendly inorganic coating agent composition and preparation method thereof

A coating agent and composition technology, which is applied in the field of environment-friendly inorganic coating agent composition and its preparation, can solve the problems of unsatisfactory solution stability, application limitations, and low curability, and achieve compatibility and dispersion Good, improved compatibility, low adhesion effect

Active Publication Date: 2018-01-09
梁哲豪
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] In addition, as a coating using inorganic components, alkali silicate is a soluble silicate, a coating agent that has excellent adhesion and dispersibility due to alkali metals with strong hydrophilicity, but for fields that require water resistance , there are limitations in its application
[0017] Therefore, in order to improve the water resistance of the coating utilizing the inorganic components, the molar ratio of the silicate can be increased to prepare the coating composition, but the stability of the solution cannot be satisfied, and gelation will occur.
[0018] In addition, if alkoxysilane is added as a viscosity enhancer, the water resistance will be greatly improved, and it can be used in various forms, but there is a problem of low curability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly inorganic coating agent composition and preparation method thereof
  • Environment-friendly inorganic coating agent composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] According to another aspect of the present invention, there is provided a method for preparing an inorganic coating agent composition, comprising the following steps: a step of forming a modified silane silicate composition, based on 100 parts by weight of silicate, to the Add 0.1 to 2 parts by weight of silane to the silicate, dilute at a temperature range of 95 to 110 ° C, and stir at a speed of 200 to 400 rpm for 1 to 2 hours; in the step of forming a silane compound, based on 100 parts by weight of silane, mix silane and After 0.01 to 3 parts by weight of a catalyst formed of hydrochloric acid, sulfuric acid or a mixture thereof, and 70 to 120 parts by weight of water, the hydrolyzed silane compound is formed by stirring at 200 to 400 rpm for 1 to 4 hours at a temperature of 80 to 90° C. ; Under the temperature range of 65 to 110° C., based on 100 parts by weight of the modified silane silicate composition prepared according to the modified silane silicate compositio...

Embodiment 1

[0095] First, after mixing 100 g of alkali silicate and 1 g of plastic trimethoxysilane, at a temperature of 97° C. or higher, the mixture was stirred at a speed of 300 rpm for 1.5 hours to form a modified silane silicate composition.

[0096] Next, 100 g of epoxy silane, 1 g of hydrochloric acid, and 100 g of water were mixed, added to the epoxy silane, and stirred at about 300 rpm for 3 hours at a temperature of 85° C. to form a hydrolyzed silane compound.

[0097] Next, maintaining a temperature of 70° C., mixing 100 g of the modified silane silicate composition, 20 g of a hydrolyzed silane compound, 150 g of a water-dispersed polyurethane dispersant, 15 g of an acrylic emulsion resin, and 100 g of water to prepare an inorganic coating agent composition .

Embodiment 2

[0099] First, after mixing 100 g of alkali silicate and 1 g of plastic trimethoxysilane, the modified silane silicate composition was formed by stirring at a temperature of 97° C. or higher at a speed of 300 rpm for 1.5 hours.

[0100] Next, 1 g of hydrochloric acid and 100 g of water were mixed with 100 g of epoxysilane, and then added to and mixed with epoxysilane, and stirred at 300 rpm for 3 hours at a temperature of 85° C. to form a hydrolyzed silane compound.

[0101] Next, while maintaining the temperature of 70°C, 100 g of the modified silane silicate composition, 20 g of the hydrolyzed silane compound, 150 g of a water-dispersed polyurethane dispersant, 15 g of an acrylic emulsion resin, 20 g of a surfactant composed of an amine salt, and 100 g of water were mixed. An inorganic coating agent composition was prepared.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The present invention provides: an inorganic coating agent composition comprising 5-30 parts by weight of a hydrolytic silane compound, 50-150 parts by weight of a water dispersible polyurethane dispersant, 10-30 parts by weight of an acrylic emulsion resin, and 5-120 parts by weight a solvent on the basis of 100 parts by weight of a modified silane silicate synthesized product; and a preparation method therefor. The inorganic coating agent composition according to the present invention has effects of forming a physically and chemically stable film on a target surface on which a film is to be formed and improving corrosion resistance, while not discharging harmful materials and being environmentally friendly.

Description

technical field [0001] The present invention relates to an inorganic coating agent composition and a preparation method thereof. An environmentally friendly inorganic coating agent composition with cold resistance, corrosion resistance, chemical resistance and / or durability, etc., specifically, relates to an environmentally friendly functional inorganic coating agent composition with an inorganic hybrid type and a preparation method thereof. Background technique [0002] Coating liquid compositions have been developed for a long time in various applications and in various compositions. [0003] Here, the coating liquid composition is also referred to as a paint (paint), and is used for coating and adhering to various object surfaces, such as the object surfaces of products made of metal, tile, wood, or concrete, etc., thereby Protects the attachment surface from physical / chemical shocks from the external environment such as polluted water. [0004] In particular, water-bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D183/02C09D133/06
CPCC09D1/00C09D133/06C09D183/02
Inventor 梁哲豪曹载洙
Owner 梁哲豪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap