Electrolytic etching agent for chromium-zirconium-copper alloy and electrolytic etching method

An etchant, chromium-zirconium-copper technology, applied in the field of electrolytic etchant for chromium-zirconium-copper alloys, can solve problems such as less chromium-zirconium-copper alloys, achieve better bonding force, overcome instability, and improve service life

Active Publication Date: 2016-10-26
GUANGZHOU SANFU NEW MATERIALS TECH
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many researches at home and abroad on the material of the crystallizer, its surface coating structure and the type of plating solution used, and there are few research reports on the electrolytic etching of chromium-zirconium-copper alloy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrolytic etching agent for chromium-zirconium-copper alloy and electrolytic etching method
  • Electrolytic etching agent for chromium-zirconium-copper alloy and electrolytic etching method
  • Electrolytic etching agent for chromium-zirconium-copper alloy and electrolytic etching method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The chromium-zirconium-copper alloy electrolytic etchant of the present embodiment is made up of the following components by weight percentage:

[0039]

Embodiment 2

[0041] The chromium-zirconium-copper alloy electrolytic etchant of the present embodiment is made up of the following components by weight percentage:

[0042]

[0043]

Embodiment 3

[0045] The chromium-zirconium-copper alloy electrolytic etchant of the present embodiment is made up of the following components by weight percentage:

[0046]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an electrolytic etching agent for a chromium-zirconium-copper alloy and an electrolytic etching method. The electrolytic etching agent comprises, by weight, 18-38% of an electrolytic salt, 3-15% of a complexing agent, 1-5% of a regulator, 1-3 % of an activator, 0-1% of a surfactant and the balance water. The electrolytic etching agent for a chromium-zirconium-copper alloy realizes uniform electrolysis of a chromium-zirconium-copper alloy plate under energization so that the chromium-zirconium-copper alloy crystallizer surface with crystal lines and without an oxide film is obtained and thus a bonding capacity of the etched galvanoplastic nickel-cobalt coating and a chromium-zirconium-copper alloy matrix is better, the coating and the matrix are firmly bonded and a crystallizer service life is prolonged.

Description

technical field [0001] The invention relates to the field of metal etching, in particular to an electrolytic etchant and an electrolytic etching method for chromium-zirconium-copper alloys. Background technique [0002] The mold made of chrome-zirconium-copper alloy is the most critical part in continuous casting equipment. In order to improve the service life of the mold, it is necessary to electroform Ni-Co and other alloy coatings on its inner surface. However, the mechanical polishing of the chrome-zirconium-copper alloy plate before electroforming will cause great damage to the substrate, making it difficult to remove impurities on the surface of the substrate. If electroforming is performed directly on the polished surface of the chrome-zirconium-copper alloy, the coating will not be firmly bonded to the substrate. In order to improve the bonding force between the coating and the substrate, it is necessary to etch the chromium-zirconium-copper alloy of the crystallizer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C25F3/02
CPCC25F3/02
Inventor 田志斌郭艳红詹益腾何桂明
Owner GUANGZHOU SANFU NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com