A kind of antibacterial stainless steel and preparation method thereof

An antibacterial stainless steel and stainless steel technology, applied in the direction of metal material coating process, etc., can solve the problems of antibacterial film preparation process defects, difficult to achieve nano-size effect, uncontrollable film surface structure, etc., to achieve uniform and firm adhesion, short preparation period, The effect of less investment in equipment

Inactive Publication Date: 2018-09-21
WUHAN UNIV OF SCI & TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Second, the antibacterial conditions are limited
Some surface antibacterial stainless steel needs ultraviolet light irradiation to achieve photocatalytic antibacterial effect, which is not only difficult to meet the requirements in public places, but also will cause certain harm to the human body in industrial and household fields, and it is difficult to maintain the antibacterial effect in the absence of light
[0005] Third, there are defects in the antibacterial film preparation process
The prepared coating is too thick, it is not firmly bonded to the substrate, and it is easy to peel off. At the same time, the surface structure of the film is uncontrollable, and it is difficult to maintain a uniform nanometer size effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An antibacterial stainless steel and a preparation method thereof. Under the condition of -5~10℃, deposit the pretreated stainless steel in the dopamine buffer solution for 0.1~3h, then deposit in the solution containing titanium ions for 0.1~1h, and then deposit in the solution containing silver ions 0.1 ~ 1h, that is, get antibacterial stainless steel.

[0030] The concentration of the titanium ion-containing solution is 0.001-0.005 mol / L, and the pH value is 6-8.

[0031] The concentration of the silver ion-containing solution is 0.001-0.005 mol / L, and the pH value is 6-8.

[0032] The titanium ion-containing solution is ammonium fluotitanate solution; the silver ion-containing solution is silver nitrate solution.

Embodiment 2

[0034] An antibacterial stainless steel and a preparation method thereof. Under the condition of 10-25°C, deposit the pretreated stainless steel in a dopamine buffer solution for 3-12 hours, then deposit it in a solution containing titanium ions for 1-3 hours, and then deposit it in a solution containing silver ions for 1 ~ 3h, that is antibacterial stainless steel.

[0035] The concentration of the titanium ion-containing solution is 0.005-0.05 mol / L, and the pH value is 4-6.

[0036] The concentration of the silver ion-containing solution is 0.005-0.05 mol / L, and the pH value is 4-6.

[0037] The titanium ion-containing solution is a titanium sulfate solution; the silver ion-containing solution is a silver sulfate solution.

Embodiment 3

[0039] An antibacterial stainless steel and a preparation method thereof. Under the condition of 15-30℃, the surface pretreated stainless steel is deposited in dopamine buffer solution for 12-36 hours, then deposited in solution containing titanium ions for 3-5 hours, and then deposited in solution containing silver ions for 3 hours ~5h, the antibacterial stainless steel can be obtained.

[0040] The concentration of the titanium ion-containing solution is 0.05-0.5 mol / L, and the pH value is 3-5.

[0041] The concentration of the silver ion-containing solution is 0.05-0.5 mol / L, and the pH value is 3-5.

[0042] The titanium ion-containing solution is titanium tetrachloride solution; the silver ion-containing solution is silver chloride solution.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention particularly relates to antibacterial stainless steel and a preparing method thereof. According to the technical scheme of the antibacterial stainless steel and the preparing method thereof, stainless steel obtained after surface pretreatment is put into a dopamine buffer solution to be deposited for 0.1 h to 72 h under the condition with the temperature ranging from -5 DEG C to 40 DEG C; then the obtained stainless steel is put into a solution containing titanium ions to be deposited for 0.1 h to 6 h; and finally the obtained stainless steel is put into a solution containing silver ions to be deposited for 0.1 h to 6 h, and therefore the antibacterial stainless steel is obtained. The concentration of the dopamine buffer solution ranges from 0.01 mol / L to 1 mol / L, the concentration of the solution containing the titanium ions ranges from 0.001 mol / L to 1 mol / L, and the concentration of the solution containing the silver ions ranges from 0.001 mol / L to 1 mol / L. By means of the antibacterial stainless steel and the preparing method thereof, the technology is simple, environment friendliness is achieved, and the cost is low; the surface antibacterial nanometer film layer structure of the antibacterial stainless steel prepared through the method is well-defined and orderly, is firmly combined with a base material, is high in corrosion resistance and hardness and has good antibacterial performance both under the illumination condition and the non-illumination condition.

Description

technical field [0001] The invention belongs to the field of stainless steel materials. Specifically relates to an antibacterial stainless steel and a preparation method thereof. Background technique [0002] Stainless steel is widely used in daily life. It is not only clean and beautiful, but also resistant to corrosion and rust. With the increasing awareness of people's health and sanitation and antibacterial, antibacterial stainless steel with antibacterial, antibacterial and sterilizing functions has emerged as the times require. From the perspective of practical application, antibacterial stainless steel uses more antibacterial properties on the surface of stainless steel, while alloy antibacterial stainless steel contains antibacterial metal ions on the surface and inside of stainless steel, which not only causes a certain amount of waste, but also increases Therefore, surface antibacterial stainless steel has great application prospects and research value. However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/50C23C22/68C23C22/73C23C22/78C23C22/80
CPCC23C22/50C23C22/68C23C22/73C23C22/78C23C22/80
Inventor 詹玮婷倪红卫陈荣生胡万培刘伟
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products