Tungsten cathode laser multilayer cladding repairing method

A multi-layer cladding and repair method technology, applied in electrodes, coatings, metal material coating processes, etc., can solve the problems of not seeing, difficult to tolerate metals, etc., and achieve the effect of convenient and flexible operation

Active Publication Date: 2016-10-05
包头市三隆稀有金属材料有限责任公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] After the applicant's search and verification: the repair of the "neck neck" part of the tungsten cathode has been completed by using the laser multi-layer cladding process. There is no relevant report in the domestic industry. At present, there are still some difficulties in processing refractory metals by laser cladding. Scientific research Workers need further innovative research

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] (a) At room temperature, clean and polish the "neck" part of the tungsten cathode. The "neck" is the surface part to be melted, and the oxide layer and corrosion layer are cleaned;

[0047] (b) Coating material: silicon carbide SiC, palladium Pd, and pure tungsten W three kinds of mixed powders, among which SiC particle size is -300~350 mesh high-purity granular powder, palladium particle size is -140~300 mesh pure palladium Powder, tungsten particle size is -200~300 mesh pure tungsten powder;

[0048] (c) The mixed powder with a volume fraction of SiC 20%, Pd 0.5%, and the rest is W is evenly mixed in an agate jar for 10 hours with a planetary high-energy ball mill at a speed of 150r / min.

[0049] (d) Using 4kW CO 2 Laser and CNC workbench, use HUST-IV high-precision powder feeder and coaxial powder feeding nozzle to clad the mixed powder on the surface of the workpiece line by line under the protection of argon atmosphere;

[0050] (e) Inspection: Use a micrometer t...

Embodiment 2

[0061] (a) At room temperature, clean and polish the "neck" part of the tungsten cathode. The "neck" is the surface part to be melted, and the oxide layer and corrosion layer are cleaned;

[0062] (b) Coating material: silicon carbide SiC, palladium Pd, and pure tungsten W three kinds of mixed powders, among which SiC particle size is -300~350 mesh high-purity granular powder, palladium particle size is -140~300 mesh pure palladium Powder, tungsten particle size is -200~300 mesh pure tungsten powder;

[0063] (c) The mixed powder with a volume fraction of SiC 25%, Pd 1.5%, and the rest is W is evenly mixed in an agate jar for 10 hours with a planetary high-energy ball mill at a speed of 200r / min.

[0064] (d) Using 4kW CO 2Laser and CNC workbench, use HUST-IV high-precision powder feeder and coaxial powder feeding nozzle to clad the mixed powder on the surface of the workpiece line by line under the protection of argon atmosphere;

[0065] (e) Inspection: Use a micrometer to...

Embodiment 3

[0076] (a) At room temperature, clean and polish the "neck" part of the tungsten cathode. The "neck" is the surface part to be melted, and the oxide layer and corrosion layer are cleaned;

[0077] (b) Coating material: silicon carbide SiC, palladium Pd, and pure tungsten W three kinds of mixed powders, among which SiC particle size is -300~350 mesh high-purity granular powder, palladium particle size is -140~300 mesh pure palladium Powder, tungsten particle size is -200~300 mesh pure tungsten powder;

[0078] (c) The mixed powder with a volume fraction of SiC 30%, Pd 1.0%, and the rest is W is uniformly mixed in an agate jar for 10 hours with a planetary high-energy ball mill at a speed of 170r / min.

[0079] (d) Using 4kW CO 2 Laser and CNC workbench, use HUST-IV high-precision powder feeder and coaxial powder feeding nozzle to clad the mixed powder on the surface of the workpiece line by line under the protection of argon atmosphere;

[0080] (e) Inspection: By using a micr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of laser cladding, particularly relates to a tungsten electrode laser multilayer repairing process used for rare earth fused salt electrolysis, belongs to the technical field of laser cladding and particularly relates to a tungsten cathode laser multi-layer repairing method. The tungsten cathode laser multi-layer repairing method is characterized in that a necking-down part of a tungsten electrode is cleaned and polished at the room temperature, and an oxide layer and a corrosion layer are removed thoroughly; then a 4 kW CO2 laser and a numerically-controlled worktable are used, a HUST-IV type high-precision powder feeding device and a coaxial powder feeding nozzle are used for cladding three kinds of mixed powder including SiC powder, Pd powder and pure W powder to the surface of a workpiece row by row and line by line under the protection of the argon atmosphere; a single-way multi-layer deposition manner is adopted for laser cladding, and a multi-layer coating with the thickness ranging from 6.0 mm to 10 mm is obtained; and finally, flaw detection is conducted, and it is ensured that the defects of cracks, air holes and inclusions are avoided in a cladding layer. The repairing method has the beneficial effects that the combining performance is high, operation is simple, and high temperature oxidability resistance and fused salt corrosivity resistance are good.

Description

technical field [0001] The invention belongs to the technical field of laser cladding, and in particular relates to a tungsten cathode laser multilayer repair method. Background technique [0002] The production of rare earth metals by molten salt electrolysis often uses refractory and corrosion-resistant metal tungsten as the cathode. Tungsten cathodes generally work under the conditions of electrolyte electrolysis temperature of 1000~1100℃, electrolysis current of 5500~6000A, and electrolysis voltage of 10V. The service life of a ø80mm×780mm tungsten cathode is 6-7 months, and the most serious loss of tungsten cathode is the middle part above the molten salt liquid level, which is mainly related to the oxidation of the electrode at high temperature. [0003] In order to prolong the service life of the tungsten cathode, the tungsten cathode is usually turned around and installed, and the thinned part is placed below the molten salt liquid level to continue to use. However,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C24/10C25C7/02C22C27/04C22C32/00
CPCC22C27/04C22C32/0063C23C24/103C25C7/025
Inventor 雷忠雷强杨胜岭李佩璋李建林高平兰兰吕建军杨春霞邸建辉张鸣一田迎春吕鑫李刚陈二喜王凡
Owner 包头市三隆稀有金属材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com