Middle-temperature high-grade daily tableware porcelain and preparation method thereof

A high-grade, daily-use technology, used in the field of ceramic manufacturing, can solve the problems of high firing temperature, complex production process, and many raw materials, and achieve the effects of low firing temperature, strong light transmission, and reasonable formula

Active Publication Date: 2016-09-28
德化县如瓷生活文化有限公司
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this kind of high-grade tableware porcelain has a certain reduction in raw material cost and firing temperature compared with bone china, the raw materials used in this kind of high-grade tableware porcelain are many, the production process is complicated, and the firing temperature is still high temperature, which needs to be further improved. Improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0034] The blank components of medium-temperature high-grade daily tableware porcelain are as follows: 35 parts of kaolin, 26 parts of potassium feldspar, 14 parts of wollastonite, 13 parts of quartz, 8 parts of lepidolite, 2 parts of dolomite, and 2 parts of burnt talc;

[0035] The glaze composition of medium-temperature high-grade daily tableware porcelain is as follows: 32 parts of low-temperature transparent frit, 18 parts of feldspar, 10 parts of kaolin, 10 parts of waste glass, 12 parts of fluorite, 8 parts of quartz, 4 parts of zinc oxide, and 5 parts of barium carbonate , 1 part of lepidolite; the chemical percentage content of the low-temperature transparent frit is: SiO 2 48%, Al 2 o 3 8%, B 2 o 3 22%, Li 2 0 13%, ZnO 2%, K 2 O 2%, Na 2 O 5%.

[0036] The firing temperature of the medium-temperature high-grade daily tableware porcelain of this embodiment is 1100° C. and the firing time is 7 hours.

specific Embodiment 2

[0037] The blank components of medium-temperature high-grade daily tableware porcelain are as follows: 37 parts of kaolin, 20 parts of potassium feldspar, 16 parts of wollastonite, 12 parts of quartz, 6 parts of lepidolite, 6 parts of dolomite, and 3 parts of burnt talc;

[0038]The glaze composition of medium-temperature high-grade daily tableware porcelain is as follows: 31 parts of low-temperature transparent frit, 12 parts of feldspar, 13 parts of kaolin, 14 parts of waste glass, 18 parts of fluorite, 6 parts of quartz, 1 part of zinc oxide, and 3 parts of barium carbonate , 2 parts of lepidolite; the chemical percentage content of the low-temperature transparent frit is: SiO 2 51%, Al 2 o 3 6%, B 2 o 3 14%, Li 2 0 14%, ZnO 3%, K 2 O 5%, Na 2 O 7%.

[0039] The firing temperature of the medium-temperature high-grade daily tableware porcelain of this embodiment is 1080° C., and the firing time is 8 hours.

specific Embodiment 3

[0040] The blank components of medium-temperature high-grade daily tableware porcelain are as follows: 38 parts of kaolin, 20 parts of potassium feldspar, 12 parts of wollastonite, 11 parts of quartz, 9 parts of lepidolite, 4 parts of dolomite, and 6 parts of burnt talc;

[0041] The glaze composition of medium-temperature high-grade daily tableware porcelain is as follows: 37 parts of low-temperature transparent frit, 14 parts of feldspar, 15 parts of kaolin, 13 parts of waste glass, 11 parts of fluorite, 4 parts of quartz, 2 parts of zinc oxide, and 1 part of barium carbonate , 3 parts of lepidolite; the chemical percentage content of the low-temperature transparent frit is: SiO 2 53%, Al 2 o 3 6%, B 2 o 3 16%, Li 2 0 12%, ZnO 4%, K 2 O 3%, Na 2 O 6%.

[0042] The firing temperature of the middle-temperature high-grade daily tableware porcelain of this embodiment is 1120° C., and the firing time is 6.8 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of porcelain manufacture and concretely relates to a middle-temperature high-grade daily tableware porcelain and a preparation method thereof. Blank materials of the middle-temperature high-grade daily tableware porcelain comprise kaolin, potassium feldspar, wollastonite, quartz, lithionite, dolomite and calcinedtalc. Glaze materials of the middle-temperature high-grade daily tableware porcelain comprise low temperature transparent frit, feldspar, kaolin, waste glass, fluorite, quartz, zinc oxide, barium carbonate and lithionite. Through adjustment of the blank materials and glaze materials and use of a reasonable formula and specially-produced frit, a sintering temperature is reduced to 1050-1150 DEG C so that a sintering temperature is low, fuel is saved, product stability is high and a production cost is reduced. The glaze materials improve blank whiteness. The middle-temperature high-grade daily tableware porcelain has fine and transparent texture, good light transmittance and a gentle color, has qualitative sense close to that of bone-china, does not release lead and cadmium in a test, is safe for use and has good social and economic benefits.

Description

technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to a medium-temperature high-grade daily tableware porcelain and a preparation method thereof. Background technique [0002] The firing and application of ceramic tableware has a long history in our country. Its various shapes, colorful colors, cool and smooth feel, easy to wash, are deeply loved by Chinese people. Existing high-grade tableware usually adopts bone china, which is made of bone meal, kaolin, quartz, feldspar and other raw materials. The firing temperature is between 1300-1350 °C, and the cost of raw materials is high and the firing temperature is high. [0003] With the rising prices of ceramic raw materials and concerns about environmental pollution and other issues, ceramic manufacturers are also transforming towards reducing costs and low-temperature environmental protection during ceramic production. Disclosed is a high-grade porcelain tableware and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/13C03C8/04C03C8/14C04B41/86
CPCC03C8/04C03C8/14C04B33/13C04B41/009C04B41/5022C04B41/86C04B2235/3208C04B2235/321C04B2235/3236C04B2235/3418C04B2235/3445C04B2235/3472
Inventor 徐海燕
Owner 德化县如瓷生活文化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com