Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ceramic product prepared from waste ceramic and preparation method thereof

A technology of ceramic products and porcelain, applied in the field of ceramic products and their preparation, to achieve the effects of reducing firing costs, improving market competitiveness, and reducing energy consumption

Inactive Publication Date: 2012-07-18
FUJIAN DEHUA NINGCHANG CERAMIC
View PDF2 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For this reason, the applicant considers using a large amount of waste porcelain as the raw material of the blank. However, to use the waste porcelain as the raw material of the blank to produce ceramic products that meet the quality requirements, many problems need to be solved: such as the proportion of waste porcelain in the blank, How to choose other components of the blank to match the waste porcelain, the particle gradation of the blank after adding waste porcelain, molding process, glaze selection, firing process, etc. If these problems are not solved properly, it will become a problem to use a large number of waste porcelain to produce ceramic products. empty talk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] In parts by weight, the blank formula is as follows: 34 parts of waste porcelain powder; 28 parts of kaolin; 18 parts of plastic clay; 20 parts of feldspar;

[0031] In parts by weight, the formula of the basic glaze is as follows: 32 parts of red lead; 10 parts of limestone; 25 parts of feldspar; 11 parts of clay; 22 parts of quartz.

[0032] Add appropriate amount of artificial synthetic pigments to the basic glaze formula, and carry out the steps of blank batching, ball milling, drying, granulation, blank molding, biscuit firing, decoration and glaze firing to obtain finished products. The main technical indicators of the obtained products are as follows:

[0033] Glaze linear expansion coefficient: 5.8×10 -6 / °C;

[0034] Blank glaze bonding: good bonding;

[0035] Glaze gloss: good;

[0036] Thermal stability: 200-20 ℃ water heat exchange once without cracking;

[0037] Glazed effect: It has high artistic quality, and the transition between colors is natural. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a ceramic product prepared from waste ceramic and a preparation method thereof. The blank formula of the ceramic product comprises the following components in part by weight: 32-36 parts of waste ceramic powder, 25-28 parts of kaolin, 15-22 parts of plastic clay and 17-25 parts of feldspar. The basic glaze formula of the ceramic product comprises the following components in part by weight: 30-35 parts of miniumite, 8-12 parts of limestone, 20-30 parts of feldspar, 8-14 parts of clay and 20-25 parts of quartz. A right amount of coloring metal compounds and / or coloring materials are added into the basic glaze. Compared with the prior art, a large amount of waste ceramic powder is used for replacing the traditional ceramic raw material for the basic glaze formula, and the technological difficulties of waste ceramic powder compounding, grain composition, sintering, decoration and the like are overcome. Not only is the waste changed into the valuable and a large amount of waste ceramic products are fully utilized, but also the sintering temperature of the ceramic product can be lowered, the energy consumption is reduced, the production cost of ceramic manufacturers is lowered, and the market competitiveness of the product is increased.

Description

technical field [0001] The invention relates to the field of ceramic manufacturing, in particular to a ceramic product made from waste porcelain and a preparation method thereof. Background technique [0002] At present, domestic recycling of ceramic waste is limited to a small amount of decorative additives used in buildings, and some ceramic manufacturers have introduced a small amount of glaze into the glaze to improve the bonding performance of the body and glaze. There is no research and development of related technologies for mass recycling of waste porcelain. [0003] For this reason, the applicant considers using a large amount of waste porcelain as the raw material of the blank. However, to use the waste porcelain as the raw material of the blank to produce ceramic products that meet the quality requirements, many problems need to be solved: such as the proportion of waste porcelain in the blank, How to choose the other components of the blank to match the waste por...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/00C04B41/86C04B35/622
Inventor 苏自艺苏友谊苏友吉曾宪春
Owner FUJIAN DEHUA NINGCHANG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com