Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Waterborne thin-coating diatom mud

A thin-coating, diatom mud technology, applied in anti-fouling/underwater coatings, coatings, anti-corrosion coatings, etc., can solve problems such as unfavorable human health, environmental protection, and excessive formaldehyde content

Inactive Publication Date: 2016-08-10
赵广全
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Whether it is traditional latex paint or various decorative wall materials currently on the market, the indoor formaldehyde content will exceed the standard during and after decoration, which is not environmentally friendly, not conducive to human health, and its function is single , the general function is only to prevent the wall from being oxidized and prevent the wall from falling off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1. A water-based thin-coating type diatom mud, including deionized water: 220 grams, cellulose using Ashland viscosity 30,000: 2.7 grams, antifreeze using Dow ft100: 18 grams, defoaming agent using Tao Dow 681f: 1g, Dow bd-109 as wetting agent: 2.2g, Dow oe-300 as multifunctional additive: 1.8g, Dispersant 5040: 5.5g, Negative ion paste: 22g, Titanium dioxide: 160 gram, kaolin 4000 mesh: 130 grams, talcum powder 1250 mesh: 55 grams, heavy calcium 1250 mesh: 170 grams, multifunctional polymer powder: 45 grams, diatomite 800 mesh: 165 grams, sepiolite: 6 grams, inorganic Composite gel: 23 grams, emulsion f208: 260 grams, Dow oe-300 as film-forming aid: 9 grams, preservative: 2.2 grams, antifungal agent 1100: 4 grams, thickener ase-60: 1.5 grams ,Thickener 180: 1.6g.

[0025] In one embodiment, the thickener ase-60 needs to be blended with 1.5 grams of water before being put into use, and the thickener ase-60 is put into use when its initial viscosity after water...

Embodiment 2

[0034] Embodiment 2, a water-based thin coating type diatom mud, including deionized water: 240 grams, cellulose with a viscosity of 30,000: 2.9 grams, antifreeze agent: 16 grams, defoamer: 1.2 grams, wetting agent: 2.2 grams, multifunctional additives using Dow oe-300: 1.6 grams, dispersant 5040: 5.8 grams, negative ion slurry: 24 grams, titanium dioxide: 180 grams, kaolin 4000 mesh: 160 grams, talcum powder 1250 mesh: 65 grams , heavy calcium 1250 mesh: 190 grams, multifunctional polymer powder: 42 grams, diatomite 800 mesh: 180 grams, sepiolite: 7 grams, inorganic composite gel: 26 grams, emulsion f208: 280 grams, film-forming aid Agent: 8.5 grams, preservative: 2.4 grams, antifungal agent: 4.5 grams, thickener ase-60: 2 grams, thickener 180: 1.6 grams.

[0035] In one embodiment, the thickener ase-60 needs to be blended with 2 grams of water before being put into use, and the thickener ase-60 is put into use when the initial viscosity of the thickener ase-60 after watering...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based thin coating type diatom mud, including deionized water, cellulose, antifreeze agent, defoamer, wetting agent, multifunctional auxiliary agent, dispersant, negative ion slurry, titanium dioxide, kaolin 4000 mesh , Talc powder 1250 mesh, heavy calcium 1250 mesh, multifunctional polymer powder, diatomite 800 mesh, sepiolite, inorganic composite gel, emulsion f208, film-forming aid, defoamer, preservative, antifungal agent, Thickener ase‑60 and thickener 180. The invention is a wall material integrating environmental protection and functionality. It has the functions of heat preservation and heat insulation, and can save electricity and heating costs for houses decorated with it. The energy saving standard reaches more than 80%. The coating surface not only No blistering, shedding, obvious discoloration, etc. It also has the advantages of tensile resistance, fracture resistance, noise resistance, acid and alkali resistance, water resistance, aging resistance, chalking resistance, discoloration resistance and formaldehyde purification.

Description

technical field [0001] The invention relates to a water-based thin coating type diatom mud. Background technique [0002] Whether it is traditional latex paint or various decorative wall materials currently on the market, the indoor formaldehyde content will exceed the standard during and after decoration, which is not environmentally friendly, not conducive to human health, and its function is single , the general function is only to prevent the wall from being oxidized and prevent the wall from falling off. Therefore, to develop a kind of deficiencies in the above-mentioned problems in the traditional and current decoration wall materials on the market, the applicant developed a kind of wall material integrating environmental protection and functionality, which can independently breathe and adjust humidity, and absorb excess air in the air. Moisture, reduce the humidity of the air to reduce the phenomenon of indoor humidity, especially suitable for house decoration in sou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D5/14C09D5/08
CPCC09D1/00C09D5/08C09D5/14
Inventor 赵广全
Owner 赵广全
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products