Antibacterial blended recuperated cotton yarn and preparation method thereof

A technology for regenerated cotton yarn and cotton fabric, which is applied in yarn, biochemical fiber treatment, textile and papermaking, etc. It can solve the problems of single performance and poor antibacterial effect, and achieve good modification effect

Inactive Publication Date: 2016-07-20
SOUTHERN CHINA REGENERATED COTTON YARN WUZHOU CO LTD
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide an antibacterial blended regenerated cotton yarn and its preparation method, which can solve the problems of poor antibacterial effect and single performance in the existing regenerated cotton yarn

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment １

[0016] The antibacterial blended regenerated cotton yarn and its preparation method are made of raw materials with the following weights:

[0017] 35 kg of waste cotton, 20 kg of tea fiber, 2 kg of yam extract, 3 kg of aloe vera, 6 kg of potassium hydrogen tartrate, 12 kg of methyl methacrylate, 0.3 kg of peracetic acid, 8 kg of water-based epoxy resin, polyethylene 5 kg of wax;

[0018] Including the following steps:

[0019] A. Put potassium hydrogen tartrate, methyl methacrylate, water-based epoxy resin and polyethylene wax in a stirring tank, add 16 times the amount of water, stir and heat until it is completely gelatinized, and then keep the reaction temperature at 45°C , Then add peracetic acid, yam extract, and aloe vera liquid and stir for 1.2 hours to obtain a mixed slurry for use;

[0020] B. After vibrating and screening the waste cotton fabrics, cut them into sections with a length and width of less than 15 cm;

[0021] C. Wash and bleach the segment material obtained in s...

Embodiment 2

[0025] The antibacterial blended regenerated cotton yarn and its preparation method are made of raw materials with the following weights:

[0026] 38 kg of waste cotton fabric, 25 kg of tea fiber, 5 kg of yam extract, 6 kg of aloe vera, 10 kg of potassium hydrogen tartrate, 15 kg of methyl methacrylate, 0.6 kg of peracetic acid, 10 kg of water-based epoxy resin, polyethylene 7 kg of wax;

[0027] Including the following steps:

[0028] A. Put potassium hydrogen tartrate, methyl methacrylate, water-based epoxy resin and polyethylene wax in a stirring tank, add 16 times the amount of water, stir and heat until it is completely gelatinized, and then keep the reaction temperature at 45°C , Then add peracetic acid, yam extract, and aloe vera liquid and stir for 1.2 hours to obtain a mixed slurry for use;

[0029] B. After vibrating and screening the waste cotton fabrics, cut them into sections with a length and width of less than 15 cm;

[0030] C. Wash and bleach the segment material obta...

Embodiment 3

[0034] The antibacterial blended regenerated cotton yarn and its preparation method are made of raw materials with the following weights:

[0035] 36 kg of waste cotton fabric, 23 kg of tea fiber, 4 kg of yam extract, 5 kg of aloe vera, 7 kg of potassium hydrogen tartrate, 13 kg of methyl methacrylate, 0.5 kg of peracetic acid, 9 kg of water-based epoxy resin, polyethylene 6 kg of wax;

[0036] Including the following steps:

[0037] A. Put potassium hydrogen tartrate, methyl methacrylate, water-based epoxy resin and polyethylene wax in a stirring tank, add 16 times the amount of water, stir and heat until it is completely gelatinized, and then keep the reaction temperature at 45°C , Then add peracetic acid, yam extract, and aloe vera liquid and stir for 1.2 hours to obtain a mixed slurry for use;

[0038] B. After vibrating and screening the waste cotton fabrics, cut them into sections with a length and width of less than 15 cm;

[0039] C. Wash and bleach the segment material obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an antibacterial blended recuperated cotton yarn and a preparation method thereof, and belongs to the technical field of textile. The cotton yarn is made from the following raw materials in parts by weight: 35 parts to 38 parts of waste and old cotton fabrics, 20 parts to 25 parts of tea fiber, 2 parts to 5 parts of yam extracts, 3 parts to 6 parts of aloe liquid, 6 parts to 10 parts of potassium acid tartrate, 12 parts to 15 parts of methyl methacrylate, 0 .3 part to 0.6 part of peroxyacetic acid, 8 parts to 10 parts of waterborne epoxy resin and 5 parts to 7 parts of Tissuemat E. The method comprises the following steps of A, preparing mixed slurry; B, cutting the waste and old cotton fabrics into material sections; C, cutting the material sections into fibers with the length being 5mm to 7mm; D, immersing the fiber into slurry, raising the temperature to 60 DEG C and maintaining the state for 3 hours to 5 hours, and then taking out and drying the materials; E, after the fiber and the tea fiber are mixed, performing cotton combing and fine combing to obtain the cotton yarn. The antibacterial blended recuperated cotton yarn can solve the problems of poor antibacterial effect and single performance of the existing recuperated cotton yarn.

Description

Technical field [0001] The invention relates to the technical field of textile products, in particular to an antibacterial blended regenerated cotton yarn and a preparation method thereof. Background technique [0002] With the shortage of raw material resources and the need to protect the environment, the recycling and reuse of waste textiles has attracted more and more attention. It can not only alleviate the shortage of resources in the textile industry, but also reduce the pollution caused by textiles to the environment. Economic and social benefits benefit the country and the people. Therefore, how to produce regenerated cotton yarn that is strong and durable, has good antibacterial effect, and is natural and environmentally friendly is a new problem that people continue to solve. Summary of the invention [0003] The technical problem to be solved by the present invention is to provide an antibacterial blended regenerated cotton yarn and a preparation method thereof. This m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D06M13/224D06M15/55D06M15/227D06M13/196D06M13/00D06M15/00D06M13/207D06M101/06
CPCD02G3/042D06M13/00D06M13/196D06M13/207D06M13/2246D06M15/00D06M15/227D06M15/55D06M16/00D06M2101/06D10B2201/01D10B2201/02D10B2401/13
Inventor 潘盈
Owner SOUTHERN CHINA REGENERATED COTTON YARN WUZHOU CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com