Method for manufacturing photocatalyst diatom ooze light high-strength plate

The technology of diatom mud and high-strength board is applied in the field of building materials, which can solve the problems of non-inhibition of bacterial reproduction, complicated process, inorganic fire-proof thermal insulation rock mud and calcium silicate board do not have the removal function, etc. Scientific formula, good thermal insulation performance

Inactive Publication Date: 2016-07-20
白山市东北亚新型建筑材料有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, their preparation method design formula is simple, the process is complicated, and the prepared inorganic fireproof insulation rock mud and calcium silicate board do not have the function of removing harmful gases such as formaldehyde, and do not have inhibitory effect on bacterial reproduction, which is far from satisfying market needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing photocatalyst diatom ooze light high-strength plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1 A kind of method for making of light-weight high-strength board of photocatalyst diatom mud, its steps and conditions are as follows:

[0037] The light-weight high-strength board of a kind of photocatalyst diatom mud is made of substrate and photocatalyst layer coated on the surface of substrate;

[0038] The composition and mass percentage of the substrate are as follows:

[0039] (ⅰ) Tertiary algal earth: 40%;

[0040] (ii) quicklime: 15%;

[0041] (ⅲ) Cement: 30%;

[0042] (ⅳ) Reinforcing fiber: 15%;

[0043] The composition and mass percentage of described photocatalyst layer are as follows:

[0044] (a) Graphite phase carbon nitride: 0.3%;

[0045] (b) Surfactant: 10%;

[0046] (c) Adhesive: 0.1%; the balance is water.

[0047] The reinforcing fiber is wood pulp;

[0048] The particle size of the graphite phase carbon nitride is 50μ;

[0049] Described surfactant is polyethylene glycol;

[0050] The binder is polyvinyl alcohol.

[0051] Des...

Embodiment 2

[0065] Embodiment 2 A kind of preparation method of photocatalyst diatom ooze light weight high-strength board, its steps and conditions are as follows:

[0066] The light-weight high-strength board of a kind of photocatalyst diatom mud is made of substrate and photocatalyst layer coated on the surface of substrate;

[0067] The composition and mass percentage of the substrate are as follows:

[0068] (ⅰ) Tertiary algal earth: 50%;

[0069] (ii) Quicklime: 10%;

[0070] (ⅲ) Cement: 20%;

[0071] (ⅳ) Reinforcing fiber: 20%;

[0072] The composition and mass percentage of described photocatalyst layer are as follows:

[0073] (a) Graphite phase carbon nitride: 5%;

[0074] (b) Surfactant: 5%;

[0075] (c) Adhesive: 3%; the balance is water.

[0076] The reinforcing fiber is straw paddle;

[0077] The particle size of the graphite phase carbon nitride is 5μ;

[0078] Described surfactant is polyethylene glycol;

[0079] The adhesive is 108 glue.

[0080] The preparatio...

Embodiment 3

[0085] Embodiment 3 A kind of method for making of photocatalyst diatom ooze light weight high-strength board, its steps and conditions are as follows:

[0086] The light-weight high-strength board of a kind of photocatalyst diatom mud is made of substrate and photocatalyst layer coated on the surface of substrate;

[0087] The composition and mass percentage of the substrate are as follows:

[0088] (ⅰ) Tertiary algal earth: 45%;

[0089] (ii) quicklime: 13%;

[0090] (ⅲ) Cement: 25%;

[0091] (ⅳ) Reinforcing fiber: 17%;

[0092] The composition and mass percentage of described photocatalyst layer are as follows:

[0093] (a) Graphite phase carbon nitride: 3%;

[0094] (b) Surfactant: 10%;

[0095] (c) Adhesive: 5%; the balance is water. The preparation method is the same as in Example 1.

[0096] The composition and mass percentage of described photocatalyst layer are as follows:

[0097] (a) Graphite phase carbon nitride: 0.3-5%;

[0098] (b) Surfactant: 0.2-10%; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Flexural strengthaaaaaaaaaa
Thermal conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for manufacturing a photocatalyst diatom ooze light high-strength plate.The photocatalyst diatom ooze light high-strength plate is composed of a base plate and a photocatalyst layer applied to the base plate.The formula is scientific, and compatibility of various production materials is realized.The photocatalyst diatom ooze light high-strength plate can not cause pollution.By the adoption of the photocatalyst diatom ooze light high-strength plate, air purification can be achieved, formaldehyde purification performance can reach 92.5%, and formaldehyde purification effect durability can reach 90%; indoor moisture can be adjusted, moisture in air can be absorbed and stored under the moist condition, and moisture can be released under the dry condition; in this way, a breathable wall is obtained.The service life of the photocatalyst diatom ooze light high-strength plate is over 30 years, edge warping, falling off and fading are avoided, oxidation resistance is high, and the photocatalyst diatom ooze light high-strength plate can stay new for a long time.Self-cleaning of a wall is realized, and static electricity is not generated so that dust adsorption can be avoided.Sound insulation and noise reduction are realized.Heat insulation and energy conservation are realized, and heat insulation property is over 6 times that of cement and mortar.The photocatalyst diatom ooze light high-strength plate is resistant to fire and inflaming and can resist temperature as high as 1300 DEG C.The photocatalyst diatom ooze light high-strength plate has a soft color and can avoid eyestrain.The photocatalyst diatom ooze light high-strength plate is widely applied to architectural decoration and industrial equipment.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to a method for preparing a light-weight high-strength board made of photocatalyst diatom mud. Background technique [0002] At present, in the field of building materials, there are many kinds of building materials with fireproof and thermal insulation functions. Inorganic fireproof and thermal insulation rock mud is one of them. The inorganic fireproof and thermal insulation rock mud is cement, bentonite, flocculent iron fiber short filaments, glass fiber short filaments, foam stone particles, kerogen shale particles, hydrophobic perlite particles mixed with water to form a plastic slurry, which can cement sand and gravel and other materials. The powdery hydraulic cementitious material hardened in air and water can be used for the inner and outer walls of buildings. [0003] Calcium silicate board is another one of them. Calcium silicate board is a building board inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/02C04B14/08C04B18/26C04B22/06C04B18/24C04B14/42
CPCC04B28/02C04B14/08C04B22/064C04B18/26C04B18/24C04B14/42Y02W30/91
Inventor 潘长发
Owner 白山市东北亚新型建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com