Method for preparing microbial fuel cell anode electrodes from agricultural wastes

A technology of agricultural waste and fuel cells, which is applied in the direction of battery electrodes, circuits, electrical components, etc., can solve the problems that the specific surface area is difficult to further increase and the steps are complicated, and achieve strong functionality, high raw material utilization, and high specific surface area. Effect

Inactive Publication Date: 2016-07-13
CHANGZHOU UNIV
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(Patent name: A method for constructing nanoporous membrane electrodes for direct methanol fuel cells based on the sacrificial template method, patent application number: 2013105249177) However, this method involves the use and removal of template agents, and the steps are complicated, and the specific surface area is difficult to improve. promote

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing microbial fuel cell anode electrodes from agricultural wastes
  • Method for preparing microbial fuel cell anode electrodes from agricultural wastes
  • Method for preparing microbial fuel cell anode electrodes from agricultural wastes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Dry the sample, and react for 30 minutes in a nitrogen atmosphere with a heating rate of 10°C / min and 400°C, and control the nitrogen flow rate at 600Ml / min to carbonize the sample, then take it out and grind it to 60 mesh, and soak it in 5wt% HCl for 6h , wash to neutral. Soak in 3wt% HF for 6h, wash until neutral, and dry; mix and grind the sample with KOH to 100 mesh, move it to a nickel crucible, and set the activation conditions as follows: temperature setting 700°C, temperature 1h, ratio 1:4, the obtained activated porous carbon material is marked as D-700-4-1.

Embodiment 2

[0042] Dry the sample, and react for 30 minutes in a nitrogen atmosphere with a heating rate of 10°C / min and 400°C, and control the nitrogen flow rate at 600Ml / min to carbonize the sample, then take it out and grind it to 60 mesh, and soak it in 5wt% HCl for 6h , wash to neutral. Soak in 3wt% HF for 6h, wash until neutral, and dry; mix and grind the sample with KOH to 100 mesh, move to a nickel crucible, and set the activation conditions as follows: temperature setting 800°C, temperature 1h, ratio 1:2, the activated porous carbon material was obtained, marked as D-800-2-1.

Embodiment 3

[0044] Dry the sample, and react for 30 minutes in a nitrogen atmosphere with a heating rate of 10°C / min and 400°C, and control the nitrogen flow rate at 600Ml / min to carbonize the sample, then take it out and grind it to 60 mesh, and soak it in 5wt% HCl for 6h , wash to neutral. Soak in 3wt% HF for 6h, wash until neutral, and dry. Mix and grind the sample with KOH to 100 mesh, move it to a nickel crucible, and set the activation conditions as follows: temperature setting 800°C, temperature 1h, ratio 1:3, and the activated porous carbon material is obtained, marked as D -800-3-1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of microbial fuel cells, in particular to a method for preparing microbial fuel cell anode electrodes from agricultural wastes.The method includes drying a sample, increasing the temperature to 400 DEG C at a temperature increase rate of 10 DEG C / min in an atmosphere of nitrogen, reacting at 400 DEG C for 30 minutes, carbonizing the sample by controlling nitrogen flow speed at 600 Ml / min, taking the carbonized sample out, grinding the carbonized sample to be in 60-mesh size, soaking the ground carbonized sample for 6 hours by 5wt% HCl, and washing the soaked ground carbonized sample to be neutral; soaking the neutral sample for 6 hours by 3wt% HF, washing the soaked sample to be neutral and drying; mixing the dried sample with KOH, grinding a mixture to be in a 100-mesh size, and transferring the ground mixture to a nickel crucible to activate at 700-900 DEG C in an atmosphere of nitrogen for 1-2 hours, wherein the ratio of the sample to the KOH is 1:2-1:6.The method for preparing the microbial fuel cell anode electrodes from the agricultural wastes has the advantages that the high-quality biomass porous carbon electrodes, prepared from agricultural wastes-bean dregs, are high in specific surface area and capacitance and have good microbial biomass enrichment effect; the method, which is capable of achieving waste resource utilization, is high in raw material use efficiency, powerful in functionality, capable of achieving environment friendliness of the electrodes and the like.

Description

technical field [0001] The invention relates to the technical field of microbial fuel cells, in particular to a method for preparing anode electrodes of microbial fuel cells from agricultural waste. Background technique [0002] In recent years, with the depletion of fossil energy and the harm caused to the environment by the combustion of coal, oil and other fossil fuels, it has become an urgent task to find a resource-saving and environment-friendly new energy. [0003] According to reports, in 2014, China's soybean production was about 12.35 million tons, the import volume was 71.404 million tons, the export volume was 2.07 million tons, and the domestic soybean apparent consumption was 83.547 million tons. China is one of the main countries that process soybeans in the world. As the largest by-product in the soybean processing industry (accounting for about 15% to 20% of the dry weight of whole beans), okara produces about 16 million tons of wet okara per year. In the cu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/88H01M4/86H01M4/96
CPCH01M4/8605H01M4/88H01M4/8828H01M4/96Y02E60/50
Inventor 杨彦袁宁一冯昊瑜查建华程时
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com