High-toughness atmosphere corrosion resistance flux-cored solder wire and preparation method thereof

An atmospheric corrosion-resistant, flux-cored wire technology, applied in welding equipment, welding media, manufacturing tools, etc., can solve the problems of vehicle steel structure corrosion, large welding spatter, low welding efficiency, etc., and achieve excellent atmospheric corrosion resistance. Reasonable effect of sub-design

Active Publication Date: 2016-07-06
XIANGTAN UNIV
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the relatively harsh environmental conditions of railway freight, the vehicles responsible for transporting materials operate in atmospheric corrosion environments such as rain, snow, water and dust all year round, and the corrosion problem of the steel structure of vehicles is very prominent
Before the 1980s, railway wagons were mainly made of ordinary carbon steel, which had poor atmospheric corrosion resistance and short service life
The use of gas-shielded solid welding wire has disadvantages such as large welding spatter and poor weld formation.
A large amount of welding spatter generated during the welding process of solid welding wire can easily lead to high work intensity for cleaning the spatter after welding. If the spatter cannot be completely removed, it will lead to poor paint coating effect on the surface of the car body
At the same time, it is difficult to adjust the chemical composition of the solid welding wire, and it is not easy to ensure the atmospheric corrosion resistance and good mechanical properties of the weld.
Although the composition of manual welding rods is convenient, it cannot realize automatic welding. The welding efficiency is low, the labor intensity is high, and the production cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness atmosphere corrosion resistance flux-cored solder wire and preparation method thereof
  • High-toughness atmosphere corrosion resistance flux-cored solder wire and preparation method thereof
  • High-toughness atmosphere corrosion resistance flux-cored solder wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The drug core composition of embodiment 1:

[0040]35.0% rutile, 4.0% quartz sand, 1.5% magnesia, 6.0% aluminosilicate, 3.0% sodium fluoride, 1.5% sodium oxide, 10.0% low carbon ferromanganese, 4.0% ferrosilicon, 5.0% Ni, 4.0% Cr, 2.0% Cu, 3.5% ferro-titanium, a total of 1.5% ferromolybdenum and ferro-vanadium, 19% iron powder.

Embodiment 2

[0041] The drug core composition of embodiment 2:

[0042] 32.0% rutile, 5.0% quartz sand, 2.0% magnesia, 8.0% aluminosilicate, 2.5% sodium fluoride, 2.0% sodium oxide, 9.0% low carbon ferromanganese, 3.5% ferrosilicon, 4.0% Ni, 3.5% Cr, 1.5% Cu, 2.5% ferro-titanium, a total of 1.0% ferromolybdenum and ferro-vanadium, 23.5% iron powder.

Embodiment 3

[0043] The drug core composition of embodiment 3:

[0044] 30.0% rutile, 6.0% quartz sand, 2.5% magnesia, 10.0% aluminosilicate, 2.0% sodium fluoride, 2.5% sodium oxide, 8.0% low carbon ferromanganese, 5.0% ferrosilicon, 4.5% Ni, 4.5% Cr, 2.5% Cu, 3.0% ferro-titanium, a total of 1.5% ferromolybdenum and ferro-vanadium, 18% iron powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-toughness atmosphere corrosion resistance flux-cored solder wire and a preparation method thereof. The flux-cored solder wire is made of carbon steel cold-rolled steel strip and a flux core. The flux core comprises, by mass, 25-40% of rutile, 3-7% of quartz sand, 1-3% of magnesite, 3-12% of aluminosilicate, 1-4% of sodium fluoride, 1-3% of sodium oxide, 5-15% of low-carbon ferromanganese, 3-7% of ferrosilicon, 2.5-5.5% of Ni, 2.5-7% of Cr, 1-3% of Cu, 1.5-5.5% of ferrotitanium, less than or equal to 3% of ferromolybdenum and ferrovanadium, and the balance iron powder. According to the flux-cored solder wire, welding is carried out with 100% of CO2 as protective gas, so that the flux-cored solder wire has good welding usability, and the low-temperature impact absorbing energy of the flux-cored solder wire at minus 40 DEG C is greater than 60J. Moreover, the flux-cored solder wire has good atmosphere corrosion resistance and can meet the requirements for welding of weather resistant steel with the yield strength being 450 MPa.

Description

technical field [0001] The invention relates to the field of gas-shielded flux-cored welding wire materials, in particular to a flux-cored welding wire with high toughness and atmospheric corrosion resistance and a preparation method thereof. Background technique [0002] The railway is the main artery of my country's national economy. 85% of the country's timber, 85% of crude oil, 80% of steel and 60% of coal are transported by rail. However, due to the harsh environmental conditions of railway freight, the vehicles responsible for transporting materials operate in atmospheric corrosion environments such as rain, snow, water and dust all year round, and the corrosion of steel structures of vehicles is very prominent. Before the 1980s, railway wagons were mainly made of ordinary carbon steel, which had poor atmospheric corrosion resistance and short service life. [0003] In order to improve the atmospheric corrosion resistance of vehicles and prolong the maintenance cycle ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/368B23K35/40
CPCB23K35/368B23K35/40
Inventor 尹付成张明华洪波
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products