A kind of preparation method of syngas to olefins catalyst

A catalyst and synthesis gas technology, which is applied in the field of high activity and stability loaded iron-based synthesis gas to low-carbon olefin catalysts and its preparation, and can solve the problems of low-carbon olefin catalyst activity and stability to be further improved, high catalyst cost, and CO conversion. Low efficiency and other problems, to achieve the effect of outstanding comprehensive performance, improved conversion rate, and improved selectivity

Active Publication Date: 2018-03-16
CHINA PETROLEUM & CHEM CORP +1
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] CN1065026A discloses a method for producing ethylene from synthesis gas, which involves the preparation of catalysts by chemical precipitation and mechanical mixing, using precious metals or rare metals, such as niobium, gallium, praseodymium, scandium, indium, cerium, lanthanum, ytterbium, etc. For other chemical elements, the selectivity of ethylene is 65%-94%, but the conversion rate of CO is very low, only about 10%, 12% and 15%. The recycling of CO will inevitably lead to energy consumption, and the catalyst cost is high
However, the activity stability of the long-term operation of the above-mentioned Fe-based silica gel-supported synthesis gas to directly prepare low-carbon olefins catalysts still needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of syngas to olefins catalyst

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] Weigh commercially available alumina (pore volume is 0.96ml / g, specific surface area is 286.81m 2 / g, saturated water absorption is 145ml / g, provided by Fushun Branch of Sinopec Catalyst Co., Ltd., the following examples and comparative examples all use the alumina), the mass concentration is 5% ammonium carbonate aqueous solution saturated spray dipping oxidation Aluminum, immediately after drying at 95°C for 1 hour, the adsorption capacity of the ammonium carbonate aqueous solution is 60% of the saturated absorption solution of the alumina carrier, aging at 60°C for 7 hours, drying at 100°C for 24 hours, and then drying at 300°C Calcined for 5 hours to prepare a modified alumina carrier. The above-mentioned modified alumina carrier was impregnated with an aqueous zinc nitrate solution with a mass fraction of 5% by unsaturated spray impregnation method, the immersion temperature was 50°C, the immersion time was 3h, the impregnation amount was 20% of the saturated absorp...

example 2

[0028] Weigh commercially available alumina, saturate spray and impregnate alumina with a mass concentration of 20% ammonium acetate aqueous solution, and immediately dry at 110°C for 0.5h after drying until the adsorption amount of ammonium acetate aqueous solution is the amount of saturated absorption solution of the alumina carrier 40%, aged at 80°C for 4 hours, dried at 120°C for 8 hours, and then calcined at 400°C for 3 hours to obtain a modified alumina carrier. The above-mentioned modified alumina carrier is impregnated with an aqueous solution of zinc sulfate with a mass fraction of 10% by an unsaturated impregnation method. Dry for 10 hours, then bake at 900°C for 4 hours. The unsaturated carrier after roasting is sprayed and dipped in morphine aqueous solution. The spray volume of morphine aqueous solution is 10% of the total saturated water absorption of the carrier used. The mass content of morphine in the morphine aqueous solution is 2% of the carrier mass. Dry a...

example 3

[0030] Except that 5% ammonium citrate was added to the impregnated ferric nitrate aqueous solution, the rest was the same as in Example 1, and the prepared catalyst was denoted as C-3, and the 300h evaluation results were shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a catalyst for producing low-carbon olefins from syngas, which comprises the following steps: (1) The alumina carrier is equal-volume saturated and impregnated with a buffer solution containing ammonium salt, and dried until the adsorption amount of the buffer solution containing ammonium salt is oxidized The aluminum carrier absorbs 30-60% of the saturated solution, and then the modified alumina carrier is obtained after aging, drying and roasting; (2) The modified alumina carrier prepared in step (1) is impregnated with zinc salt by unsaturated impregnation method solution, dried and then calcined; (3) using unsaturated impregnation method to impregnate the carrier after step (2) roasting with the wetting solution containing the adsorbent; (4) step (3) the carrier containing the adsorbent to be saturated and co-impregnated A mixed solution containing active metal iron, additive manganese and additive potassium is dried and calcined to prepare a catalyst for producing low-carbon olefins from syngas. The catalyst has the characteristics of high activity and stability in long-period operation, and is beneficial to industrial application and popularization.

Description

technical field [0001] The invention relates to a catalyst for producing olefins from synthesis gas and a preparation method thereof, in particular to a high-activity and stability loaded iron-based catalyst for producing low-carbon olefins from synthesis gas and a preparation method thereof. Background technique [0002] Low-carbon olefins such as ethylene and propylene are important basic organic chemical raw materials. With the development of the chemical industry, their demand is increasing. So far, the way to produce low-carbon olefins such as ethylene and propylene is mainly through the cracking process of light oil. With the increasing depletion of oil resources worldwide, the future energy structure will inevitably shift. Compared with oil resources, coal and natural gas resources are relatively abundant, and it is of great significance to develop low-carbon olefin production processes based on coal and natural gas. The development of direct production of ethylene a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/889C07C1/04C07C11/04C07C11/06C07C11/08
CPCY02P20/52
Inventor 李杰张信伟张舒东孙晓丹尹泽群刘全杰
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com