Antirust heat treatment technology for spare parts

A kind of parts and process technology, which is applied in the field of anti-rust heat treatment process of parts, can solve the problems of high energy consumption, poor uniformity of galvanized layer thickness, insufficient surface hardness and wear resistance, etc., achieve low processing cost and improve process efficiency Effect

Inactive Publication Date: 2016-06-08
CHONGQING GUIKUN MACHINERY CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the most effective industrial corrosion method for steel parts, the traditional hot-dip galvanizing process has high energy consumption, poor thickness uniformity of the galvanized layer, corrosion resistance, surface hardness and wear resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Below in conjunction with embodiment the present invention will be further described, and its operating steps are as follows:

[0017] (1) Parts pretreatment: inspect the parts, remove burrs, iron filings, grease and other dirt on the surface of the parts;

[0018] (2) Degreasing: Use water-based metal degreasing cleaning agent to degrease the parts until the parts are completely soaked;

[0019] (3) Pickling: Soak the pipe in the pickling tank to remove the oxide skin on the surface of the steel pipe. The concentration of the pickling solution is 20-22% HCl, and then add a corrosion inhibitor. The temperature is controlled at 21-22°C, and the pickling time is controlled. In 20-30 minutes;

[0020] (4) Rinsing: add 0.1%-0.2% citric acid to clean water for water rinsing;

[0021] (5) Immersion fluxing agent: Put the parts into the fluxing bath to dip the fluxing agent. The fluxing agent is a mixed aqueous solution of ammonium chloride and zinc chloride. The concentrati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antirust heat treatment technology for spare parts. The antirust heat treatment technology comprises the following steps of pretreating the spare parts; performing degreasing; performing pickling; performing rinsing; performing soaking in flux; performing drying and preheating; performing hot galvanizing; performing passivating; performing cooling; and performing inspection and trimming. The antirust heat treatment technology for the spare parts, provided by the invention, has the advantages that the treatment fees are low, the treated spare parts are durable, the technological treatment efficiency is improved, and the quality of workpieces is improved.

Description

technical field [0001] The invention relates to the field of heat treatment, in particular to an antirust heat treatment process for parts. Background technique [0002] Mechanical parts are basically made of iron or steel. When iron or steel comes into contact with carbon dioxide in humid air, the surface will be surrounded by a layer of acid electrolyte solution. Since steel contains a small amount of carbon, when the surface is covered with When the weakly acidic electrolyte solution is used, several primary batteries are formed on the surface. Iron is the negative electrode and carbon is the positive electrode. As the negative electrode, iron will lose electrons and be oxidized into ferric hydroxide precipitation. Carbon dioxide in the air reacts with ferric hydroxide to form red Brown basic iron carbonate, while oxygen, carbon dioxide and water vapor can continue to "attack" in, so the rust becomes thicker and thicker until all the steel is rusted. In order to prevent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C2/06C23C2/02
Inventor 钟传梅
Owner CHONGQING GUIKUN MACHINERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com