Manufacturing method of ceramic cooker with high thermal shock resistance

A technology of thermal shock resistance and cooker, applied in the field of ceramics, can solve the problems of cracking, high water absorption and poor strength of the cooker, and achieve the effects of high product strength, dense glaze layer and regular appearance

Active Publication Date: 2016-06-08
广东雅诚德实业有限公司
View PDF1 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are also some disadvantages. For example, the thermal shock resistance test results of general ceramic cookers are all below "450°C put into 20°C water without cracking once". Rapid cooling and rapid heating with large temperature difference during use may cause the cooker Cracking; some cooking utensils with a poor degree of porcelain have high water absorption and are easy to absorb odors. Their strength is poor and they are easy to be damaged during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0032] (1) Blank preparation

[0033] Get 45 parts by weight of spodumene, 38 parts by weight of kaolin, 8 parts by weight of petalite, 6 parts by weight of waste porcelain, and 2 parts by weight of bentonite as raw materials for blank;

[0034] ——The above-mentioned spodumene was calcined at a temperature of 1240°C for 15 hours; the above-mentioned kaolin came from two different producing areas of Fujian Longyan and Guizhou, of which Fujian Longyan kaolin and Guizhou kaolin each accounted for 50% of the kaolin consumption; the above-mentioned waste Porcelain refers to the scrapped porcelain after firing, which is hammered into pieces;

[0035] After mixing the above raw materials, add water to carry out wet ball milling. The raw materials after ball milling are passed through a 200-mesh sieve after iron removal by the iron remover. The mud machine is used for mud refining, and a billet with a mass moisture content of 22% is prepared for use;

[0036] (2) Glaze preparation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of a ceramic cooker with high thermal shock resistance. The manufacturing method is characterized by including the following production steps of 1, blank preparation; 2, glaze preparation; 3, forming and fettling; 4, biscuiting; 5, glazing; 6, firing. The manufactured ceramic cooker with high thermal shock resistance is high in percent of pass, regular in appearance, dense in glaze layer and high in strength, and the product is not broken after being put in water at the temperature of 20 DEG C for heat exchange once when the thermal shock resistance reaches 600 DEG C.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a ceramic cooker with high thermal shock resistance and a preparation method thereof. Background technique [0002] Ceramic cooking utensils (such as soup pots, woks, etc.) are hygienic, practical, easy to clean, and have good heat storage performance. However, there are also some disadvantages. For example, the thermal shock resistance test results of general ceramic cookers are all below "450°C put into 20°C water without cracking once". Rapid cooling and rapid heating with large temperature difference during use may cause the cooker Cracking; some cooking utensils with a poor degree of porcelain have a high water absorption rate and are easy to absorb odors. Their strength is poor and they are easy to be damaged during use. Through technological innovation, seeking technological breakthroughs in terms of raw material formula and production technology, the ceramic heat-resistant cookin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/04C04B33/24C04B33/34C03C8/02
CPCC03C8/02C04B33/04C04B33/131C04B33/1324C04B33/24C04B33/34C04B2235/3427C04B2235/96Y02P40/60
Inventor 陈彬权周勋楷郑成发曾伟林
Owner 广东雅诚德实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com