Non-curing rubber asphalt waterproof material and preparation method thereof

A technology of asphalt waterproof material and non-curing rubber, which is used in building insulation materials, plastic recycling, bulk chemical production, etc., to avoid insufficient performance, good deformation requirements, and good durability.

Active Publication Date: 2016-05-04
河北交投特种材料科技有限公司 +1
View PDF5 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a method for preparing non-cured rubber asphalt waterproof material, which can avoid the disadvantages of complex process and high cost caused by desulfurization of waste tire rubber powder before use in conventional production, At the same time, it avoids the defect that the performance of the waste tire rubber powder can not be fully exerted due to the direct miscibility of the asphalt.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-curing rubber asphalt waterproof material and preparation method thereof
  • Non-curing rubber asphalt waterproof material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0024] Example 1: Taking the production of 1000 kg of non-cured rubber asphalt waterproof material of the present invention as an example, each part is 10 kg, and the ratio of raw materials used is: 74.5 parts of basic asphalt, 16.5 parts of rubber powder, 0.25 parts of desulfurizing agent, and 1 part of composite modifier. 1 part of softener, 0.25 part of cross-linking agent, 6.5 parts of filler, wherein the base asphalt is heavy traffic 70# petroleum asphalt, the rubber powder specification is 60 mesh waste tire rubber powder for bias tires, and the desulfurizer is pentachlorothiophenol , the composite modifier is SBS, the softener is pine tar, the crosslinking agent is tetramethylthiuram disulfide, and the filler is 1250 mesh light calcium carbonate; the following steps are adopted during specific production:

[0025] (1) Measure the hot-melt asphalt into the mixing tank with heating system, and put the weighed waste tire rubber powder, softener, compound modifier and desulf...

example 2

[0028] Example 2: Take the production of 1000 kg of non-cured rubber asphalt waterproof material of the present invention as an example, each part is 10 kg, and the raw material ratio used is: 63 parts of basic asphalt, 21 parts of waste tire rubber powder, 0.67 parts of desulfurizing agent, compound modification 1.26 parts of softening agent, 4.2 parts of softening agent, 1.3 parts of cross-linking agent, 8.53 parts of filler, wherein base pitch is 110# petroleum pitch, and the selection and preparation method of all the other raw materials are the same as example one.

example 3

[0029] Example 3: Take the production of 1000 kg of non-curing rubber asphalt waterproof material of the present invention as an example, each part is 10 kg, and the raw material ratio used is: 54.4 parts of basic asphalt, 27.2 parts of waste tire rubber powder, 0.816 parts of desulfurizing agent, compound modified 0.816 parts of softening agent, 2.86 parts of softening agent, 1.63 parts of crosslinking agent, and 12.278 parts of filler, wherein base asphalt is crude oil catalytic oil slurry, rubber powder is 30 mesh bias tire rubber powder, and the selection and preparation method of all the other raw materials are the same as example one.

[0030] The non-cured rubber asphalt waterproof material of the present invention has the following characteristics:

[0031] (1) Adaptability to structural deformation: The non-curing rubber asphalt material itself has excellent ductility and cohesiveness, and can adapt to the deformation and cracking of the pavement base layer and the com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a non-curing rubber asphalt waterproof material and a preparation method thereof. The non-curing rubber asphalt waterproof material comprises raw materials in parts by weight as follows: 30-70 parts of base asphalt, 15-40 parts of waste tire rubber powder, 0.25-1.0 part of a desulfurizing agent, 0.8-4 parts of a composite modifier, 0.5-5 parts of a softening agent, 0.25-3 parts of a cross-linking agent and 5-15 parts of filler, wherein the grain size of the waste tire rubber powder is 20-80 meshes. The preparation method comprises steps as follows: raw material preparation, hot melting and mixture homogenization are performed; finally, the cross-linking agent and the filler in parts by weight are sequentially added to a storage tank and are stirred and mixed for 15-20 min, and the non-curing rubber asphalt waterproof material is formed. The waste tire rubber powder is directly subjected to circular shearing desulfurization by a high-shear homogenizer under the action of the desulfurizing agent in a high-temperature asphalt medium, rubber molecules are uniformly dispersed in an asphalt system in a linear structure manner and then form a stable stereoscopic meshed rubber structure with the filler under the action of the cross-linking agent, and the product performance is more stable.

Description

technical field [0001] The invention relates to the technical field of waterproof building materials, in particular to a non-cured rubber asphalt waterproof material and a preparation method thereof. Background technique [0002] According to incomplete statistics, in 2014, the amount of waste tires produced in my country reached tens of millions of tons, and large-scale waste tires caused serious black pollution to the living environment of human beings. Harmless treatment and utilization of waste tires is an urgent need for social development [0003] At present, it has become a development trend in the transportation industry to use waste tire rubber powder as an asphalt modifier for road construction and maintenance, but it is limited to the current technical level, or the simple swelling and mixing of rubber powder and asphalt, and the rubber powder only exists as a filler If it is used in the asphalt system, its performance cannot be fully exerted; or the modification...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L17/00C08L53/02C08L25/10C08L23/06C08L23/12C08K13/02C08K5/40C08J11/28
CPCC08J11/28C08J2317/00C08L95/00C08L2205/035C08L17/00C08L53/02C08L25/10C08L23/06C08L23/12C08K13/02C08K5/40Y02P20/52Y02W30/62
Inventor 翟根旺谭华张红波鲁培行
Owner 河北交投特种材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com